836587.fig.005
Figure 5: Young’s moduli of elasticity of Ti-29Nb-13Ta-4.6Zr subjected to (a) solution treatment (ST) at 1063 K for 3.6 ks, AST, (b) aging at 598 K for 259.2 ks after ST, A598K, (c) aging at 673 K for 259.2 ks after ST, A673K, (d) cold rolling (CR), BCR, (e) aging at 598 K for 259.2 ks after CR, B598K, (f) aging at 673 K for 259.2 ks after CR, B673K, and (g) aging at 723 K for 259.2 ks after CR, B723K.