Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions
Table 3
Temperature-dependent results of samples machined perpendicular to the rolling direction.
| Sample | Temperature | Total pressure | | | | Elongation | | Reduction in area | | (°C) | (kPa) | (mm) | (mm) | (mm) | (%) | (mm) | (%) |
| K7 | 20 | 800 | 24.55 | 10.50 | 35.05 | 22.4 | 3.12 | 39.2 | K4 | 20 | 1000 | 15.10 | 20.00 | 35.10 | 22.7 | 3.1 | 39.9 | K9 | 30 | 800 | 23.15 | 10.40 | 33.55 | 15.8 | 3.17 | 37.2 | K2 | 35 | 800 | 17.20 | 17.50 | 34.70 | 20.8 | 3.15 | 38.0 | K6 | 35 | 1000 | 15.50 | 18.25 | 33.75 | 16.7 | 3.42 | 26.9 | K1 | 45 | 1000 | 20.55 | 12.45 | 33.0 | 13.3 | 3.55 | 21.2 | K5 | 45 | 800 | 15.70 | 17.50 | 33.20 | 14.2 | 3.7 | 14.4 | K8 | 50 | 800 | 24.95 | 7.80 | 32.75 | 12.2 | 3.65 | 16.7 | K11 | 60 | 1000 | 24.40 | 9.20 | 33.6 | 16.0 | 3.34 | 30.3 |
|
|