Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions
Table 4
Temperature-dependent results of samples machined perpendicular to the rolling direction and tested in 50% CO–50% CO2.
| Temperature | | | | Elongation | | Reduction in area (%) | (°C) | (mm) | (mm) | (mm) | (%) | (mm) |
| 25 | 8.18 | 25.24 | 33.42 | 15 | 3.06 | 41 | 30 | 10.90 | 23.26 | 34.16 | 18 | 3.22 | 35 | 35 | 7.84 | 26.00 | 33.84 | 17 | 3.38 | 29 | 40 | 14.82 | 18.52 | 33.34 | 15 | 3.50 | 23 | 45 | 13.80 | 20.92 | 34.72 | 21 | 3.40 | 28 | 48 | 12.42 | 21.90 | 34.32 | 19 | 3.60 | 19 | 50 | 20.92 | 12.18 | 33.10 | 14 | 3.56 | 21 | 60 | 12.16 | 21.00 | 33.16 | 14 | 3.64 | 17 | 70 | 8.94 | 25.00 | 33.94 | 18 | 3.30 | 32 | 75 | 19.50 | 14.20 | 33.70 | 16 | 3.48 | 24 |
|
|