Determination of Susceptibility to Intergranular Corrosion of UNS 31803 Type Duplex Stainless Steel by Electrochemical Reactivation Method: A Comparative Study
Table 5
DLEPR test results of 2205 type duplex stainless steel.
Temperature (°C)
Time (min)
Activation peak potential, (mV)
Activation peak current density, (mA/cm2)
Reactivation peak potential, (mV)
Reactivation peak current density, (mA/cm2)
Passivation current density, (mA/cm2)
DOS ()
Solution annealed at 1050°C, 1 hr
−212.78
23.1304849
−267.33
0.0063918
0.001448
0.027634
Solution annealed at 1050°C, 1 hr, then aged at 800°C