The Effect of Applied Stress on Environment-Induced Cracking of Aluminum Alloy 5052-H3 in 0.5 M NaCl Solution
Figure 6
Fracture appearances for A5052-H3 at T = 353 K and σ = 230 MPa; X550, LT orientation (a), TL orientation (b) in 0.5 M sodium chloride solution.