Corrosion Behaviour of Heat-Treated Aluminum-Magnesium Alloy in Chloride and EXCO Environments
Table 10
Electrochemical corrosion rate for the 0.91% Mg specimen.
| T (sec) | NaCl solution | FeCl3 | EXCO solution | As-cast | RRA | As-cast | RRA | As-cast | RRA |
| 0 | 0.0000 | 0.0000 | 0.0000 | 0.0000 | 0.0000 | 0.0000 | 1200 | 0.0242 | 0.0061 | 0.0363 | 0.0176 | 0.0308 | 0.0238 | 2400 | 0.0468 | 0.0117 | 0.0702 | 0.0345 | 0.0605 | 0.04600 | 3600 | 0.0678 | 0.0167 | 0.1035 | 0.0499 | 0.0877 | 0.0653 | 4800 | 0.0871 | 0.0214 | 0.1355 | 0.0653 | 0.1129 | 0.0855 | 6000 | 0.1027 | 0.0252 | 0.1663 | 0.0785 | 0.1360 | 0.01048 | 7200 | 0.1233 | 0.0296 | 0.1959 | 0.0943 | 0.1601 | 0.1232 |
|
|