Corrosion Behaviour of Heat-Treated Aluminum-Magnesium Alloy in Chloride and EXCO Environments
Table 14
Electrochemical corrosion rate for the 2.02% Mg specimen.
| T (sec) | NaCl solution | FeCl3 | EXCO solution | As-cast | RRA | As-cast | RRA | As-cast | RRA |
| 0 | 0 | 0 | 0 | 0 | 0 | 0 | 1200 | 0.0117 | 0.0242 | 0.0119 | 0.0058 | 0.0117 | 0.0058 | 2400 | 0.0222 | 0.046 | 0.0226 | 0.0107 | 0.0222 | 0.0107 | 3600 | 0.034 | 0.0653 | 0.0314 | 0.0151 | 0.032 | 0.0148 | 4800 | 0.0386 | 0.0838 | 0.0402 | 0.0189 | 0.0419 | 0.0189 | 6000 | 0.0452 | 0.1027 | 0.0472 | 0.0216 | 0.0493 | 0.0226 | 7200 | 0.0505 | 0.1183 | 0.053 | 0.0246 | 0.0554 | 0.0259 |
|
|