Corrosion Behaviour of Heat-Treated Aluminum-Magnesium Alloy in Chloride and EXCO Environments
Table 3
Gravimetric corrosion rate (mm/yr) for the 0.91% Mg specimen.
| Days | NaCl solution | FeCl3 | EXCO solution | As-cast | RRA | As-cast | RRA | As-cast | RRA |
| 0 | 0.000 | 0.000 | 0.000 | 0.000 | 0.000 | 0.000 | 1200 | 0.000 | 0.000 | 0.771 | 0.000 | 0.000 | 0.000 | 2400 | 0.000 | 0.000 | 0.771 | 0.193 | 0.193 | 0.193 | 3600 | 0.000 | 0.000 | 0.642 | 0.257 | 0.128 | 0.257 | 4800 | 0.000 | 0.000 | 0.578 | 0.289 | 0.193 | 0.385 | 6000 | 0.077 | 0.000 | 0.54 | 0.231 | 0.231 | 0.308 | 7200 | 0.064 | 0.000 | 0.515 | 0.257 | 0.322 | 0.322 |
|
|