Electroless Deposition of Ni-Cu-P Coatings Containing Nano-Al2O3 Particles and Study of Its Corrosion Protective Behaviour in 0.5 M H2SO4
Table 3
Corrosion parameters of coatings in 0.5 M H2SO4 derived from polarization measurements.
| Concentration of nanoparticles in the bath (ppm) | (mV versus SCE) | (Ω cm2) | (mV/dec) | (mV/dec) | C. R. (mm/year) |
| 0 | −430 | 178.8 | 61 | 117 | 1.14 | 5 | −428 | 194 | 86 | 97 | 1.20 | 10 | −460 | 362.3 | 175 | 123 | 1.02 | 20 | −484 | 790.9 | 112 | 114 | 0.36 | 50 | −473 | 546.1 | 90 | 101 | 0.44 | 100 | −467 | 352.3 | 85 | 127 | 0.74 | 1000 | −464 | 315.3 | 90 | 106 | 0.79 |
|
|