Electrochemical Impedance and Modelling Studies of the Corrosion of Three Commercial Stainless Steels in Molten Carbonate

<table class="table-group" id="tab1"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr class="thead"><td align="left">Stainless steel</td><td align="center">Composition (wt.%)</td></tr><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td align="left">P92</td><td align="center">Fe-9.0Cr-1.8W-0.5Mn-0.4Mo-0.11Si-0.2V</td></tr><tr><td align="left">SS304</td><td align="center">Fe-19.3Cr-9.4Ni-2.0Mn-0.9Si</td></tr><tr><td align="left">SS310 </td><td align="center">Fe-26.4Cr-18.5Ni-1.4Mn</td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

The compositions of the three commercial stainless steels.

International Journal of Corrosion

tab1

Table 1

Table 1: Electrochemical Impedance and Modelling Studies of the Corrosion of Three Commercial Stainless Steels in Molten Carbonate 