Tear Strength Analysis of MDX4-4210 and A-2186 Silicones with Different Intrinsic Pigments Incorporated by Mechanical and Industrial Methods
Table 1
Mean values ± standard deviation (SD) (N/mm) of tear strength values comparing nonaged and aged silicones.
| Manufacturing method | Pigment/Silicone | Nonaged groups | Aged groups | value | Mean ± SD | Mean ± SD |
| Mechanical | Bronze A-2186 | 68.89 ± 7.74 | 72.12 ± 11.17 | 0.387 | Bronze MDX4-4210 | 27.44 ± 2.45 | 41.16 ± 4.31 | 0.001 | Black A-2186 | 63.79 ± 14.21 | 64.87 ± 13.91 | 0.773 | Black MDX4-4210 | 29.40 ± 2.54 | 41.25 ± 3.82 | 0.002 | Pink A-2186 | 63.11 ± 12.74 | 65.56 ± 12.83 | 0.513 | Pink MDX4-4210 | 28.02 ± 7.64 | 31.65 ± 2.05 | 0.340 |
| Industrial | Bronze A-2186 | 66.24 ± 9.99 | 73.10 ± 11.56 | 0.067 | Bronze MDX4-4210 | 26.46 ± 1.86 | 37.82 ± 3.52 | 0.003 | Black A-2186 | 67.81 ± 7.84 | 65.17 ± 11.85 | 0.484 | Black MDX4-4210 | 29.49 ± 3.23 | 42.53 ± 6.66 | 0.001 | Pink A-2186 | 69.18 ± 11.17 | 70.46 ± 6.07 | 0.722 | Pink MDX4-4210 | 27.04 ± 1.07 | 31.06 ± 4.11 | 0.282 |
|
|
Statistically significant difference ( , Tukey). |