Photoactive Thin Silver Films by Atmospheric Pressure CVD

Yates, Heather M.; Brook, Lucy A.; Sheel, David W.

doi:https://doi.org/10.1155/2008/870392

International Journal of Photoenergy

On this page

Abstract Introduction Experimental Results and Discussion Acknowledgments References Copyright Related Articles

Special Issue

Selected Papers from the Second International Conference on Semiconductor Photochemistry

View this Special Issue

Research Article | Open Access

Volume 2008 | Article ID 870392 | https://doi.org/10.1155/2008/870392

Photoactive Thin Silver Films by Atmospheric Pressure CVD

Heather M. Yates,¹Lucy A. Brook,¹and David W. Sheel¹

Academic Editor: Russell Howe

Received24 Jul 2007

Revised22 Nov 2007

Accepted26 Mar 2008

Published15 May 2008

Abstract

We report the visible and UV activity of thin silver films. The films are grown using a CVD process employing aqueous-based silver precursors, flame-assisted chemical vapour deposition. This approach overcomes many of the previously encountered limitations to silver deposition by employing an atmospheric pressure process, low-cost and low-toxicity precursors. The resultant films are assessed for activity using stearic acid destruction as a model compound. We also report on the addition of titania to these silver films to increase the potential functionality. This activity is also demonstrated, where the films appear largely transparent to the eye, further widening the potential application of this work. It is speculated that the nanoparticulate nature, of the CVD silver, is crucial in determining photoactivity.

1. Introduction

In recent years, photoactive films have attracted increasing attention, particularly based on titania. Significant efforts have been directed at developing the photoactivity of titania into the visible. Methods have included use of other photoactive materials in conjunction with TiO₂ including WO₃ [1] and PdO [2], or by doping with anionic [3, 4], or cationic [5] species. To date, the results have been mixed. In many cases, the doping itself leads to a reduction in photoactivity, often attributed to disruption of the crystal structure [6] and/or the introduction of compensation centres [7]. Some papers do claim visible activity [8], although the form and mechanism of how the photoactivity works is often in dispute [9].

The combination of Ag and TiO₂ produced mainly by sol-gel techniques has been shown to improve TiO₂ UV photoactivity, under the correct conditions. In some cases, this has been shown to relate to the modification of the sample morphology by the Ag with, for example, a change in crystallite size [10] or rutile/anatase [11]. The addition of Ag is considered to promote charge separation of the electron-hole pairs from TiO₂ after photon absorption by acting as an electron sink.

Research literature of the behaviour of just Ag under illuminated light relates mainly to its own transition rather than its effect on other chemical compounds. The reduction of Ag⁺ ions to Ag metal is well documented, and use of UV to form the metal from ions is common practice. Commercial uses of the reduction of Ag⁺ ions include photography [12] and photochromic glass [13]. Films of AgCl were found to be photocatalytic for the oxidation of water, but only in the presence of excess Ag⁺. This activity expanding from the UV to visible due to self-sensitisation [14].

Other research relating to use of Ag in catalysis is usually in conjunction with zeolites, where the presence of Ag⁺ clusters increases the photodecomposition rate of specific organics by acting as active sites, or electron trapping sites [15], or decomposition of inorganics such as NO and H₂O [16]. In these cases, the zeolite is needed to isolate and stabilize the Ag⁺ ions (and their clusters). The zeolite itself is playing a role in the photoactivity of the catalyst, for example, the increased efficiency of the N₂O decomposition reaction with ZSM-5 opposed to zeolite Y [17]. There is only very limited literature available on the photoactivity of thin Ag films with organic materials. Research by Guo et al. [18] states that there is a possible photocatalyic reaction under laser excitation.

A wide range of techniques have been used to deposit thin film silver including electroless deposition [19], electrostatic deposition [20], and PVD processes (e.g., evaporation and sputtering) [21]. Previous studies on silver thin film structure have shown that continuous sheets of silver can be produced easily by PVD [22], and a granular structure can be produced by MOCVD [23, 24]. Although these processes are effective at producing thin films, the degree of silver nanostructure control is typically limited.

In this paper, we report the use of flame-assisted chemical vapour deposition (FACVD) to produce silver nanostructured layers and coatings. The process can use aqueous precursors, which are in many cases very soluble, and of relatively low toxicity. Growth rates are also rapid in comparison to previous APCVD reports, and a high degree of nanostructure control can be achieved with this approach. Indeed, the nanostructured silver deposition control arising from our described approach appears to give an enhancement to photoactivity and also to the bioactivity of the various film structures, as previously shown [25]. We will report on the photoactivity of Ag films in both the visible and the UV, along with examples of Ag/TiO₂ films. The added attraction of the TiO₂/Ag combination is the increased durability of the samples, over that of Ag which is relatively soft and the additional high photoactivity expected of the TiO₂ under UV.

2. Experimental

2.1. Growth

All films were grown on commercially supplied silica-coated barrier glass substrates. The barrier is a thin (60 nm), amorphous film of SiO₂ to prevent diffusion of impurity ions within the float glass. These would all cause a reduction in the quality and photoactivity of the films.

All silver films were produced by flame-assisted chemical vapour deposition (FACVD). The FACVD reactor used is of in-house construction. Basically, it consists of a burner head which allows gas mixing, a translational substrate stage and a precursor delivery system (electronic mass-flow controllers and a nebuliser). A schematic of the system is shown in Figure 1. The substrate stage is made up of a carbon block which can be translated beneath the flame at a rate of 3.6 cm/s. The number of passes under the burner head is related to the sample thickness. The carbon block was held at C for optimum growth. The nebuliser is a commercially available ultrasonic system (ultra-neb2000 Devilbiss 200HS-042), with water used as the transmission medium. The precursor solution sits within a cup that in turn is in contact with the water in the nebuliser, such that ultrasonic waves are passed through to the precursor solution, hence producing droplets of precursor solution. Nitrogen carrier gas then passes through the nebuliser, collecting solution droplets, which are then transported to the flame. Fuelling the burner is a mixture of propane and oxygen gases, flowing at 0.99 L and 3.65 L , respectively, generating a flame output power of 1.50 kW. The precursor is carried in 1.70 L of nitrogen. These gases are also mixed with 13.90 L of make-up nitrogen for flame control. The precursor reagent used was silver nitrate supplied by Aldrich, with a purity of 99.99% dissolved in deionised water to the required concentration.

Electroplated silver was also deposited as a comparison to the FACVD films. These films were deposited using 0.15 M silver nitrate in deionised water (solution A), 0.8 M potassium hydroxide in deionised water (solution B), and a 0.49 M glucose solution (solution C). The glucose solution was made up of 88% deionised water, 11% ethanol, and 1% concentrated nitric acid. The solutions were mixed in the ratio 16 : 8 : 1 of A : B : C, respectively, and deionised water was added to control the speed of the reaction. Concentrated ammonia was used to react with any oxide precipitation.

Titania films were grown using an atmospheric pressure CVD coater. The precursors used were titanium tetrachloride ( mol ) and ethyl acetate ( mol ) (Aldrich), which were transported through the reactor by a carrier gas of nitrogen. The substrate temperature was C. Silver was deposited both under and over these films by FACVD.

2.2. Characterisation

X-ray diffraction (Siemens D5000) was used to confirm the sample crystallinity. The morphology assessed by SEM (Philips XL30). Film thickness (for titania) was estimated by relating the reflected colour to a calibrated chart for thickness versus refractive index. Film thickness for the Ag was determined by cross-sectional SEM and the use of a surface profiler (Dektak 3ST) on an etched edge. X-ray photoelectron spectroscopy, XPS, (Kratos AXIS Ultra) with an Al (monochromated) radiation source was used to check the surface composition and stoichiometry of the films.

To test the photocatalytic behaviour under UV (365 nm), the degradation of stearic acid was followed by FTIR (Bruker, Vector 22). The software allows integration of the area under the peaks over a range of 2800–3000 . A typical stearic acid layer would have an integrated absorbance over this range of 1.0 corresponding to ca. molecules [26]. The stearic acid (100 μl of 10 mmoL in methanol) was spun coated onto the sample. After drying in an oven, the sample was exposed to UV light with an intensity of 3 mW/cm². For visible light measurements, a high-intensity tungsten/halogen lamp (300 W) with a 400 nm cut-off filter was used.

3. Results and Discussion

In order to understand the influence of the various layer structures, both silver (by FACVD) and titania (by thermal CVD) were grown. The silver films were analysed, and both the silver and titania films were tested for photoactivity in the visible and the UV regions.

3.1. Visual

The Ag films were produced with a range of thickness (60–250 nm), by increasing the number of passes of the moving substrate under the flame. The comparison TiO₂ films were all transparent (80 nm) with a brown tinge due to interference colouration. Visually, all the Ag films were highly reflective, with a pale pink tinge which darkens to purple for thicker coatings. The films could withstand gentle rubbing or sonification. Those with an upper layer of TiO₂ were slightly more robust.

3.2. X-Ray Diffraction

All Ag films (FACVD and electroplated) were crystalline showing metallic cubic Ag only (JCPDS 04-0783). That of the titania was anatase (JCPDS 21-1272) when grown directly on a glass substrate (or under Ag film), while it contained some rutile (calculated at 33 wt%) when grown on top of the Ag film. Use of Scherrers formula [27] allows calculation of crystallite size (Table 1). The calculation is ideally for a powder not a thin film, so will contain line width broadening from strain as well as crystallite size. Despite these reservations, the values obtained will give an idea of the changes occurring.

3.3. Chemical Composition

Confirmation that the Ag films consisted of metallic Ag, not oxides (or sulphides) came from the XPS. The high-resolution scan only showed the 3d signals at and with a splitting of 6 eV which are characteristic of metallic Ag. From the wide scan, a small amount of Si was detected, which almost certainly comes from the glass substrate. The O 1s signal consisted only of a single peak at 532.7 eV relating to absorbed water on the surface. No O 1s or Ag 3d signal was present for an oxide.

Both TiO₂ deposited over Ag and the inverse (Ag over TiO₂) established that there was both TiO₂ and Ag on the surface. Obviously, in the case of Ag over TiO₂ the intensity of the Ag signal was greater. The high-resolution scan showed Ti 2p signals at and , with a splitting of 5.7 eV, characteristic of TiO₂. This was confirmed by the O 1s signal at 530.2 eV.

3.4. Morphology

From the SEM can be seen (Figure 2) that in the early stages of thin film growth the Ag deposits as particles rather than a continuous film. The exact size and spacing depend on the growth conditions [28]. It is also important to note that the sample thickness is more correctly the height of the individual islands. As the number of passes is increased the particles gradually coalesce and form a continuous sheet. As can be seen in Figure 2(d), the electroplate Ag forms a continuous film with a granular surface.

(a)

(b)

(c)

(d)

3.5. Photoactivity

The photoactivity was assessed by use of stearic acid as a model system, as stearic acid simulates a typical type of solid organic film that deposits on glass and ceramic surfaces. However, it is important to note that if a material is highly photoactive with one model compound, it does not necessarily mean that it is as active with another, or even that the same relative rates of activity can be determined. This has been previously clearly shown with titania [29, 30].

3.5.1. Photoactivity Under UV Radiation

The rate at which the stearic acid was decomposed is shown by the integrated area under the IR signals from the stearic acid (2957.5, 2922.8, and 2853.4 ), which are directly proportional to the concentration. For a period of up to 70 minutes, the FACVD Ag films showed signs of photoactivity, which then levelled out, as seen below in Figure 3. This is particularly obvious for the thinnest sample of 2 passes (60 nm). This behaviour does not occur for the thickest FACVD film of 100 passes (250 nm) or the electroplate film (104 nm).

There is an increased scatter in some of the measurements (enhanced by the normalisation). This is particularly obvious for the thickest film (100 passes) due to increased roughness and haziness. The hazy appearance of the thick samples is due to increased crystalline disorder and increased crystallite size (i.e., above a critical particles size a film is perceived as hazy as more light is scattered).

That these decay curves for silver are real and not an artefact of the experimental set up (or instrument fault), a film of TiO₂ was run over the same experimental period, showing the expected zero-order curve as the stearic acid decomposes, (as seen in Figure 3). This is of a similar order to the initial rate of reaction (0–70 minutes) of the thinnest Ag layer (60 nm). A linear fit giving ( molecules ) for the TiO₂ film and ( molecules ) for the initial rate of the Ag layer (2 passes). Most of the curves shown are obviously not linear, so have been fitted by a sigmoidal fit.

The lack of activity for the thick films may relate to differences in the morphology (continuous rather than island formation) and the crystallite size. As previously noted the thinner films have much smaller crystallite sizes (11–20 nm) than that for the thicker films (33–38 nm). This change in crystallite size relates to the extent of deposition. Also, the smaller the nanoparticles, the greater the surface area and hence increased rate of photoactivity.

From Figure 3, in particularly those for 4 and 2 passes, it can be seen that a point is reached at which no more stearic acid is decomposed. These coatings are noncontinuous, but previous research has shown that a pollutant can be removed from incomplete coatings of TiO₂ due to the mobile electron/hole during the photoactive process [31]. This is not occurring here, suggesting that the mechanism for TiO₂ photoactivity is different to that of the Ag.

3.5.2. Photoactivity under Visible Radiation

Before running the experiments, the emission of the “visible” lamp with and without the 400 nm cut-off filter was checked. This confirmed that no obvious emission below 398 nm was detected with the filter in place.

Considering the UV experiments, a sharp reduction of the stearic acid is followed by a point of no change for the thinner samples (Figure 4), while the thicker samples do not show this behaviour, and confirming lack of photoactivity. For reference, a film of TiO₂ (which is not expected to show any visible activity) has been added. This can be seen to show a slight reduction in values with time ( , molecules ), relating to stearic acid changes due to temperature fluctuations and possibly UV undetected by the emission spectra. This trend is in line with that seen for the thicker samples (100 pass FACVD and electroless plate). The thinner samples show a much more pronounced change.

As before, it is proposed that the initial activity seen relates to the formation of nanoparticles in the FACVD which do not occur in the electroplate silver, along with the difference in the morphology. As noted earlier, the thinner FACVD films exist as islands of Ag, rather than continuous film (100 pass and electroplate). Calzaferri et al. [14] suggest that Ag clusters on the surface sensitise the photocatalytic process. These clusters lead to the formation of empty Ag energy levels lower than those in the bulk metal, and so enable a new transition, extending the process from the UV into the visible.

Interestingly, it was possible to repeat this behaviour on addition of more stearic acid, as shown in Figure 5 using the thinnest Ag layer (2 passes). After the standard stearic acid test had been carried out, more stearic acid was spun coated onto the sample and the test repeated. As can be seen the same trend occurs. The initial rate of the reaction (gradient) showed no significant change at (1.25 10¹³ molecules ). In fact, this value is compatible to the UV activity of a TiO₂ film (80 nm).

A possible explanation for this behaviour is that the stearic acid would react with the Ag at the islands, but no reaction would occur between them (being on glass not Ag). When all the stearic acid on the island was used up, no more reaction would occur. On addition of more stearic acid, the process would begin again. This would seem to be in agreement with the SEM (Figure 6) taken after the reaction had finished, showing a patchy coating of stearic acid rather than a film.

As in the case of UV photoactivity, the presence of smaller nanoparticles will increase the surface area available and so increase any reaction between the stearic acid and the film.

As standard practice, the samples were exposed to UV light for 4 hours before the visible experiment as previous work had shown that this gave improved visible photoactivity of sol-gel produced, Ag-doped TiO₂ samples [32, 33]. This is considered due to the UV partially reducing the TiO₂ and favouring the electron transfer to Ag [34]. However, the above experiment with repeated layers of stearic acid showed that this was not necessary for just Ag films (opposed to TiO₂-Ag). Exposing the sample to UV light should reduce any Ag⁺ ions to Ag metal, as is common practice for the formation of Ag/TiO₂ from TiO₂/AgNO₃ for sol-gel films [35].

It has previously been mentioned that under UV light any Ag⁺ would be reduced to Ag metal. However, under visible light in the presence of O₂ this process can be reversed with O₂ acting as an electron acceptor for the photoexcited Ag. This was shown to be a reversible sequence (between UV/visible) by Ohko et al. [36]. Films of AgCl were found to be photocatalytic for the oxidation of water, but only in the presence of excess Ag⁺. This photoactivity expanding from the UV to visible due to self-sensitisation [14]. The presence of the excess Ag⁺ was considered to be responsible for the self-sensitisation with the band gap of AgCl being decreased due to these Ag ion 5s states. For our experiments, there is no initial high concentration of Ag⁺ ions, as no other chemical species than Ag metal were detectable by the limits of XRD or XPS.

Similar experiments were done using multilayers of TiO₂ and Ag. As previously mentioned, if TiO₂ was deposited on top of Ag, anatase with a small amount of rutile was produced. Also, the layer was not continuous, so both Ag and TiO₂ were present on the top surface.

This again (Figure 7) shows the trend seen with the Ag films, along with the ability to repeat the experiment on adding more stearic acid on completion of the first experiment. The TiO₂ film is also plotted, so the contrast between no activity (TiO₂) and activity (TiO₂ on Ag) can be more clearly seen.

Growth Ag (2 passes) on top of TiO₂ again led to a surface containing Ag and TiO₂ (anatase only). In this case, no sign of activity was seen (Figure 8), with the multilayer giving the same lack of activity as seen in the comparison TiO₂ sample. Both samples gave rates of ( molecules ), which are similar to that obtained by uncoated float glass. The complete lack of any activity due to the Ag is surprising given the previous results. Possibly there is an advantage having a mixture of rutile and anatase rather than just anatase as rutile absorbs a higher wavelength of light than anatase, which may in some way help the decomposition of stearic acid which occurs. Also, the presence of rutile may favour the TiO₂ over Ag sample, as it was previously shown by Sclafani et al. [34] that rutile, but not anatase improved the UV photoactivity of sol-gel mixed TiO₂/Ag samples. However, this cannot be the full explanation, as the films of just Ag show photoactivity. Alternatively, deposition of Ag on top of TiO₂, rather than directly on the barrier glass may alter either the amounts or dispersion of Ag being deposited and hence may reduce its effect on the stearic acid. If as earlier postulated the structure of the Ag is of importance and then by growth on a different effective substrate, this structure is changed, hence curtailing the photoactivity. However, the Ag crystallite size itself has not been altered whether grown on either material, so indicating the FACVD deposition process was controlling this property.

The mechanism by which Ag (under certain conditions) removes stearic acid is not clear at this stage. We can speculate on this, as to whether this is a photocatalytic process or a photoactive reduction/oxidation reaction. In this regard, some key points (noted in the above section) are as follows:

(i)under both UV and visible light, stearic acid can be decomposed;(ii)such degradation only occurs for the thin films of Ag and TiO₂ over Ag (which actually consists of TiO₂ interspersed with Ag clusters);(iii)the reaction tails off before completion;(iv)the behaviour can be repeated on the same sample;(v)the (active) thin films consist of noncontinuous island growth of small Ag clusters. Significantly, the two films where no reaction occurred were for the thick, continuous films of 100 passes FACVD, and the electroplate film. Both also have the largest crystallite sizes.The decomposition of the stearic acid might initially suggest a photocatalytic process particularly as the behaviour seems to be repeatable on the same sample. However, the reaction tails off implying that the active species may be being depleted which would suggest a photoactive oxidation/reduction process. It is possible that under more extended testing, full depletion may be observable. However, such a simple silver depletion driven reaction is hard to rationalise with the observation that reaction does not occur (or is substantially slower) in two types of silver films. We could speculate that, in this instance, presence of the nanoparticulate films consisting of isolated clusters, and below a critical crystallite size, is of paramount importance for these UV and visible activated decompositions of stearic acid. Additional studies are planned to try to further elucidate the mechanism involved.

4. Summary

By use of FACVD, with aqueous precursors, it has been shown possible to controllably deposit polycrystalline cubic Ag films. The thickness of the film and morphology can be controlled by the number of passes of the burner head over the substrate. The comparison TiO₂ is stoichiometric anatase. The silver films deposited in an island formation which gradually closed up becoming a continuous film by a thickness of 250 nm. This nanostructure could be varied by controlling the growth conditions. These films were compared with a continuous film of Ag produced by the electroplate method. All the silver films which consisted of the noncontinuous nanostructure demonstrated an initial visible activity to stearic acid, which was shown to be repeatable on the same sample, although they did not go to completion. No activity was shown by the continuous films of 100 passes or the electroplate samples for UV or visible, suggesting that the nanostructure is a significant factor in the photoactivity seen with stearic acid in the thinner films.

By use of multilayers of thin coatings of Ag under TiO₂, it is possible to combine the visible photoactivity of the Ag and complement its UV activity with the excellent photoactivity of TiO₂. This has potential use in the commercial sector due to the shown repeatable measurement, along with the improved durability of the product over that of just Ag.

Acknowledgments

This work is partially financed by the EC through GRD1-2001-40791, PHOTOCOAT project. LB thanks Corus Plc for financial support.

References

X. Z. Li, F. B. Li, C. L. Yang, and W. K. Ge, “Photocatalytic activity of ${WO}_{x} {-TiO}_{2}$ under visible light irradiation,” Journal of Photochemistry and Photobiology A, vol. 141, no. 2-3, pp. 209–217, 2001.
View at: Publisher Site | Google Scholar
Q. Li, W. Liang, and J. K. Shang, “Enhanced visible-light absorption from PdO nanoparticles in nitrogen-doped titanium oxide thin films,” Applied Physics Letters, vol. 90, no. 6, Article ID 063109, 3 pages, 2007.
View at: Publisher Site | Google Scholar
S. Sakthivel and H. Kisch, “Daylight photocatalysis by carbon-modified titanium dioxide,” Angewandte Chemie International Edition, vol. 42, no. 40, pp. 4908–4911, 2003.
View at: Publisher Site | Google Scholar
R. Asahi, T. Morikawa, T. Ohwaki, K. Aoki, and Y. Taga, “Visible-light photocatalysis in nitrogen-doped titanium oxides,” Science, vol. 293, no. 5528, pp. 269–271, 2001.
View at: Publisher Site | Google Scholar
H. Yamashita, M. Harada, J. Misaka et al., “Application of ion beam techniques for preparation of metal ion-implanted ${TiO}_{2}$ thin film photocatalyst available under visible light irradiation: metal ion-implantation and ionized cluster beam method,” Journal of Synchrotron Radiation, vol. 8, part 2, pp. 569–571, 2001.
View at: Publisher Site | Google Scholar
H. M. Yates, M. G. Nolan, D. W. Sheel, and M. E. Pemble, “The role of nitrogen doping on the development of visible light-induced photocatalytic activity in thin ${TiO}_{2}$ films grown on glass by chemical vapour deposition,” Journal of Photochemistry and Photobiology A, vol. 179, no. 1-2, pp. 213–223, 2006.
View at: Publisher Site | Google Scholar
W. Choi, A. Termin, and M. R. Hoffmann, “The role of metal ion dopants in quantum-sized ${TiO}_{2}$ : correlation between photoreactivity and charge carrier recombination dynamics,” Journal of Physical Chemistry, vol. 98, no. 51, pp. 13669–13679, 1994.
View at: Publisher Site | Google Scholar
J. Wang, S. Yin, M. Komatsu, Q. Zhang, F. Saito, and T. Sato, “Photo-oxidation properties of nitrogen doped ${SrTiO}_{3}$ made by mechanical activation,” Applied Catalysis B, vol. 52, no. 1, pp. 11–21, 2004.
View at: Publisher Site | Google Scholar
Y. Y. Mi, S. J. Wang, J. W. Chai et al., “Effect of nitrogen doping on optical properties and electronic structures of ${SrTiO}_{3}$ films,” Applied Physics Letters, vol. 89, no. 23, Article ID 231922, 3 pages, 2006.
View at: Publisher Site | Google Scholar
A. Dobosz and A. Sobczyński, “The influence of silver additives on titania photoactivity in the photooxidation of phenol,” Water Research, vol. 37, no. 7, pp. 1489–1496, 2003.
View at: Publisher Site | Google Scholar
J.-W. Yoon, T. Sasaki, and N. Koshizaki, “Dispersion of nanosized noble metals in ${TiO}_{2}$ matrix and their photoelectrode properties,” Thin Solid Films, vol. 483, no. 1-2, pp. 276–282, 2005.
View at: Publisher Site | Google Scholar
T. H. James, The Theory of the Photographic Process, MacMillan, New York, NY, USA, 4th edition, 1977.
W. H. Armistead and S. D. Stookey, “Photochromic silicate glasses sensitized by silver halides,” Science, vol. 144, no. 3615, pp. 150–154, 1964.
View at: Publisher Site | Google Scholar
G. Calzaferri, D. Brühwiler, S. Glaus, D. Schürch, A. Currao, and C. Leiggener, “Quantum-sized silver, silver chloride and silver sulfide clusters,” Journal of Imaging Science and Technology, vol. 45, no. 4, pp. 331–339, 2001.
View at: Google Scholar
M. C. Kanan, S. M. Kanan, and H. H. Patterson, “Luminescence properties of silver(I)-exchanged zeolite Y and its use as a catalyst to photodecompose carbaryl in the presence of natural organic matter,” Research on Chemical Intermediates, vol. 29, no. 7-9, pp. 691–704, 2003.
View at: Publisher Site | Google Scholar
M. Matsuoka, K. Iino, H. Chen, and M. Anpo, “Local structures of Ag (I) clusters prepared within zeolites by ion-exchange method and their photochemical properties,” Research on Chemical Intermediates, vol. 31, no. 1–3, pp. 153–165, 2005.
View at: Publisher Site | Google Scholar
M. Matsuoka, W.-S. Ju, H. Yamashita, and M. Anpo, “In situ characterization of the ${Ag}^{+}$ ion-exchanged zeolites and their photocatalytic activity for the decomposition of $N_{2} O$ into $N_{2}$ and $O_{2}$ at 298 K,” Journal of Photochemistry and Photobiology A, vol. 160, no. 1-2, pp. 43–46, 2003.
View at: Publisher Site | Google Scholar
L. J. Guo, Q. Xing, X. L. Liu, Y. B. Huang, and Y. J. Mo, “The structure and properties of self-assembly complex LB films of silver nanoparticles,” Spectroscopy and Spectral Analysis, vol. 25, no. 5, pp. 726–729, 2005.
View at: Google Scholar
S. Chandra, J. N. Sharma, V. K. Mohabey, and R. C. Agrawal, “Superionic solid film. III. Preparation and electrical conductivity of cation substituted silver iodide based superionic solid ${NH}_{4} {Ag}_{4} I_{5}$ ,” Journal of Physics D, vol. 13, no. 3, pp. 495–502, 1980.
View at: Publisher Site | Google Scholar
Z. Liu, X. Wang, H. Wu, and C. Li, “Silver nanocomposite layer-by-layer films based on assembled polyelectrolyte/dendrimer,” Journal of Colloid and Interface Science, vol. 287, no. 2, pp. 604–611, 2005.
View at: Publisher Site | Google Scholar
Y. S. Jung, “Study on texture evolution and properties of silver thin films prepared by sputtering deposition,” Applied Surface Science, vol. 221, no. 1–4, pp. 281–287, 2004.
View at: Publisher Site | Google Scholar
T. L. Alford, L. Chen, and K. S. Gadre, “Stability of silver films on underlying layers at elevated temperatures,” Thin Solid Films, vol. 429, no. 1-2, pp. 248–254, 2003.
View at: Publisher Site | Google Scholar
M. Abourida, H. Guillon, C. Jimenez et al., “Silver thin films deposited by injection MOCVD,” in Proceedings of the 203rd Meeting of the Electrochemical Society, pp. 938–945, Paris, France, August 2003.
View at: Google Scholar
L. Gao, P. Härter, C. Linsmeiner, A. Wiltner, R. Emling, and D. S. Landsied, “Silver MOCVD for advanced silver metallization,” Microelectronic Engineering, vol. 82, no. 3-4, pp. 296–300, 2005.
View at: Publisher Site | Google Scholar
L. A. Brook, P. Evans, H. A. Foster et al., “Highly bioactive silver and silver/titania composite films grown by chemical vapour deposition,” Journal of Photochemistry and Photobiology A, vol. 187, no. 1, pp. 53–63, 2007.
View at: Publisher Site | Google Scholar
Y. Paz, Z. Luo, L. Rabenberg, and A. Heller, “Photo-oxidative self-cleaning transparent titanium dioxide films on glass,” Journal of Materials Research, vol. 10, no. 11, pp. 2842–2848, 1995.
View at: Publisher Site | Google Scholar
B. D. Cullity, Elements of XRD, Addison-Wesley, Reading, Mass, USA, 1978.
D. W. Sheel, L. A. Brook, and H. M. Yates, “Controlled nanostructured silver coated surfaces by atmospheric pressure chemical vapour deposition,” Chemical Vapour Deposition, vol. 14, no. 1-2, pp. 14–24, 2008.
View at: Publisher Site | Google Scholar
W. Choi and J. Ryu, “Multi-aspects of photocatalytic activities of ${TiO}_{2}$ : substrate specificity and implication for the activity test standardization,” in Proceedings of the 2nd International Conference on Semiconductor Photochemistry, Aberdeen, UK, July 2007.
View at: Google Scholar
A. Mills and S. Le Hunte, “An overview of semiconductor photocatalysis,” Journal of Photochemistry and Photobiology A, vol. 108, no. 1, pp. 1–35, 1997.
View at: Publisher Site | Google Scholar
S.-K. Lee, S. McIntyre, and A. Mills, “Visible illustration of the direct, lateral and remote photocatalytic destruction of soot by titania,” Journal of Photochemistry and Photobiology A, vol. 162, no. 1, pp. 203–206, 2004.
View at: Publisher Site | Google Scholar
E. Stathatos, T. Petrova, and P. Lianos, “Study of the efficiency of visible-light photocatalytic degradation of basic blue adsorbed on pure and doped mesoporous titania films,” Langmuir, vol. 17, no. 16, pp. 5025–5030, 2001.
View at: Publisher Site | Google Scholar
J.-M. Herrmann, H. Tahiri, Y. Ait-Ichou, G. Lassaletta, A. R. Gonzalez-Elipe, and A. Fernandez, “Characterisation and photocatalytic activity in aq. medium of ${TiO}_{2}$ and Ag- ${TiO}_{2}$ coatings on quartz,” Applied Catalysis B, vol. 13, no. 3-4, pp. 219–228, 1997.
View at: Publisher Site | Google Scholar
A. Sclafani and J.-M. Herrmann, “Influence of metallic silver and of platinum-silver bimetallic deposits on the photocatalytic activity of titania (anatase and rutile) in organic and aqueous media,” Journal of Photochemistry and Photobiology A, vol. 113, no. 2, pp. 181–188, 1998.
View at: Publisher Site | Google Scholar
A. Sclafani, M.-N. Mozzanega, and J.-M. Herrmann, “Influence of silver deposits on the photocatalytic activity of titania,” Journal of Catalysis, vol. 168, no. 1, pp. 117–120, 1997.
View at: Publisher Site | Google Scholar
Y. Ohko, T. Tatsuma, T. Fujii et al., “Multicolour photochromism of ${TiO}_{2}$ films loaded with silver nanoparticles,” Nature Materials, vol. 2, no. 1, pp. 29–31, 2003.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2008 Heather M. Yates et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1553

Downloads

885

Citations