Characterizations of Chitosan-Based Polymer Electrolyte Photovoltaic Cells
Table 4
Characteristics of PEC cells using polymer-salt-ionic liquid systems.
| Polymer electrolyte Sample | Dye | Intensity (mW cm−2) | Redox couple | (S cm−1) | (mA cm−2) | OCV (V) | ff | (%) | Ref. |
| 52.5 wt.% PEO + 17.5 wt.% KI + 30 wt.% EMImTFSI | Ru(dcbpy)2(NCS)2 | 100 | | | 4.02 | 0.77 | 0.56 | 1.75 | [43] | 15 wt.% PEO + 5 wt.% KI + 80 wt.% EMISCN | Ru(dcbpy)2(NCS)2 | 27 | | | 1.89 | 0.65 | 0.52 | 0.63 | [44] | 17.5 wt.% PEO + 2.5 wt.% NaI + 80 wt.% EMImTFO | Ru(dcbpy)2(NCS)2 | 60 | | | 5.65 | 0.79 | 0.55 | 2.45 | [38] | 27.5 wt.% Chitosan + 22.5 wt.% wt.% BMII | Anthocyanin from black rice | 100 | | | 0.065 | 0.23 | 0.22 | — | — | 27.5 wt.% Chitosan + 22.5 wt.% wt.% BMII | Betalain from callus of Celosia plumosa | 100 | | | 0.029 | 0.14 | 0.22 | — | — |
|
|