High-Efficiency 6′′ Multicrystalline Black Solar Cells Based on Metal-Nanoparticle-Assisted Chemical Etching

<table>The optical reflection of 6′′ mc-BSWs with different nanorod lengths. The average length on BSWs distributes from 100 nm to 1 <i>μ</i>m. The reflection is approximately inversely proportional to the average nanorod length. The reflection is about 9.5% for BSW decorated with 100 nm-thick nanorods and suppressed to 2% for BSW with 1 <i>μ</i>m-thick nanorods.</table>

International Journal of Photoenergy

fig3

Figure 3

Figure 3: High-Efficiency 6′′ Multicrystalline Black Solar Cells Based on Metal-Nanoparticle-Assisted Chemical Etching 