Abstract
We have studied the optical properties of nanocrystalline silicon (nc-Si) film deposited by plasma enhancement chemical vapor deposition (PECVD) on porous aluminum structure using, respectively, the Photothermal Deflection Spectroscopy (PDS) and Photoluminescence (PL). The aim of this work is to investigate the influence of anodisation current on the optical properties of the porous aluminum silicon layers (PASL). The morphology characterization studied by atomic force microscopy (AFM) technique has shown that the grain size of (nc-Si) increases with the anodisation current. However, a band gap shift of the energy gap was observed.
1. Introduction
Porous anodic alumina films are an interesting material [1] for nanotechnology applications because of their unusual properties compared to the bulk counterparts [2]. Many works have been published relative to the deposition of porous aluminum films [3, 4]. Different methods of film growth on the surface of the porous matrix layer were used, as for example reactive sputtering [5] and low pressure metal-organic chemical vapor deposition [6].
In this work we demonstrate the capability to grow porous aluminum layers (PAL) by a simple electrochemical anodisation method. The anodizing process was done by varying the anodizing voltage between 200 to 400 mV. Crystalline silicon films are deposited on the PAL by a PECVD technique. Photothermal deflection spectroscopy (PDS) is used to determine the optical absorption spectrum and gap energy by comparing the experimental amplitude of the photothermal signal to the corresponding theoretical one. PL and PDS are used in order to study the influence of anodic current on optical properties of our samples. For this purpose, absorption spectrum, gap energies are measured. The optical properties of the deposited films are correlated to the porous aluminum and nc-Si films morphologie.
2. Film Preparation
High-purity aluminum foil (99.997%), 0.25 mm thick, was used as a starting material. The cleaned samples were anodized during 25 min in a solution of diluted sulfuric acid with 66.66% H2SO4 and 33.33% H2O2 at room temperature and with five different anodization currents (200 mA, 250 mA, 300 mA, 350 mA, and 400 mA). On the surface, nc-Si films were deposited by PECVD technique [7] at 50°C using a gas mixture of silane and H2 at a total pressure of 0.5 mTorr.
3. AFM Characterization
The surface morphology of the films was examined by atomic force microscopies. Figure 1 shows AFM images of porous Al filled of nc-Si and obtained with different anodisation currents varying from 200 mA to 400 mA. The surface shows spherical domes with an average size (as estimated from the AFM images), varying approximately from 12 to 15 nm as a function of the anodisation current.
(a)
(b)
(c)
(d)
(e)
4. Optical Characterization
4.1. Photoluminescence
The PL properties were measured using an Ar laser ( nm) and detected by a cooled GaInAs detector with a standard technique using a lock-in.
Figure 2(a) shows the PL spectrum of the nc-Si layer. The PL emission lies in the orange region of the visible spectral range. The PL band peak position varies from 616 nm to 624 nm (2 and 1.98 eV, resp.) as increases from 200 to 400 mA. This observed PL does not seem to have its origin only from silicon nanocrystals embedded in the porous aluminum matrix, as proposed by Ong and Zhu [8] but it is due to the contributions of the two materials (Si incorporated in PAL). To assure that these peaks come from the nc-Si films, we have measured the PL of porous Al (without nc-Si). As shown in Figure 2(b), the PL peak originates from the PAL that is located at 430 nm (2.8 eV) far from the nc-Si ones. The PL peak position represents a blue shift as the nc-Si size decrease. This effect could be explained by the increase of Si–O/Si–H surface bond ratio [9].
(a)
(b)
4.2. Photothermal Measurements
The photothermal deflection spectral measurements have been used for investigating optical properties of semiconductors. The great advantage of the PDS is that it is a direct monitor of the nonradiative recombination processes of photo-excited electrons in a semiconductor.
The experimental setup has been described in detail in [10]. When a sample (Figure 1) is irradiated with modulated and monochromatic beam radiation, the absorbed energy is converted into heat through different relaxation processes. The generated thermal wave diffuses in the material and in the surrounding fluid (CCl4). The temperature variations in the fluid lead to a refractive index gradient causing the deflection of a probe laser beam (He–Ne 4 mW) skimming the sample surface. This deflection is detected by a position photosensor linked to a lock in amplifier. The obtained photothermal signal has two compounds: amplitude and phase. The principle of this technique is shown in Figure 3. The probe beam deflection is given by [11]: where is the fluid refractive index, is the distance between probe beam axis and the sample surface, and is the sample length. is thermal diffusion length in the fluid, the thermal diffusivity, and is the modulation frequency of the heating beam. We notice that the deflection is proportional to the complex temperature expression at the sample surface. This temperature is calculated by solving the one-dimensional heat equation in the different media sample, backing, and the surrounding fluid (Figure 4): These equations are solved while taking into account of the boundary conditions at different interfaces. The obtained surface temperature is given byThermal and optical parameters that appear in the above expression are given in [12].
4.2.1. Near Gap Absorption Spectrum
Figure 5 shows the obtained experimental curves of the normalized amplitude for the studied samples: nanocrystalline Si (nc-Si) thin films deposited on porous aluminum by plasma-enhanced chemical vapor deposition as a function the anodisation current. 200, 250, 300, 350, and 400 mA. The amplitude shows two saturations zones corresponding, respectively, to high and low optical absorption coefficient. For energy higher than the gap energy, the sample is optically opaque (maximum amplitude) and became more and more transparent when the energy decreases (minimum amplitude). We notice that in the subband gap region, the amplitude saturates at different minimum values for each sample.
The comparison of experimental curves of amplitude versus wavelength to theoretical amplitude versus absorption coefficient permits to obtain the optical absorption spectrum for the samples shown on Figure 6. We remark that the less-anodized sample has a relative higher absorption coefficient in the transparency zone.
4.2.2. Determination of the Gap Energies
In order to obtain the gap energy from optical spectra, we have used the Tauc method [13, 14]. For energies higher than , the quantity should have linear variations with , following the Tauc law: where is the absorption coefficient and is the slope of the curve. For indirect bandgap semiconductor such as nanocrystalline Si (nc-Si) thin films deposited on porous aluminum: . The curves of versus are shown in Figures 7(a) and 7(b). The obtained gap energy values are reported in Table 1. We notice a bandgap shift of about 24 mev. The energy bandgap decreases with anodisation current and varies from 2.2 to 1.9 eV as varies from 200 to 400 mA, respectively (Table 1). The obtained value of agrees with gap energies measured by other authors [15].
(a)
(b)
Comparison between the various bandgap shows that the optical absorption properties are significantly affected by particle size of the nc-Si films. The fact that these energies are high than the expected ones (for nanosized Si crystal) could be explained by the contribution of alumina in the absorption spectra. Alumina has in fact a high band gap energy (≈3.2 eV) [16] compared to silicon. The effect could be also attributed to the presence of particles with very small size (quantum confinement). In Table 1, the gap energies measured with photoluminescence spectra and photothermal deflection has been compared for different anodized levels. We notice that the is slightly higher than the real gap energy determined by photothermal deflection, because it corresponds to the radiative transition.
5. Conclusion
In this work, nanocrystal silicon thin films were deposited by PECVD technique on a porous aluminum substrate prepared with different anodizations currents. Optical absorption spectrum, and gap energy are measured and analyzed using the PL and PDS techniques. A bandgap shift induced by the anodisation current is detected. We found a correlation between the particle size and the gap energy.