Low-Temperature Reverse Microemulsion Synthesis, Characterization, and Photocatalytic Performance of Nanocrystalline Titanium Dioxide

<table>Degradation ratio of MO under ultraviolet light irradiation over catalysts as: (a) TiO<sub>2</sub> calcined at 500°C, (b) TiO<sub>2</sub> aged at 65°C for 90 h, (c) TiO<sub>2</sub> aged at 65°C for 120 h, (d) commercial P25, (e) TiO<sub>2</sub> aged at 65°C for 72 h, (f) blank.</table>

International Journal of Photoenergy

fig10

Figure 10

Figure 10: Low-Temperature Reverse Microemulsion Synthesis, Characterization, and Photocatalytic Performance of Nanocrystalline Titanium Dioxide 