Abstract

The absorption spectra of N719 sensitizer anchored on the films prepared by TiO2 nanocrystals with different morphology and size were investigated for improving the performance of dye-sensitized solar cell (DSC). We find that the morphology and size of TiO2 nanocrystals can affect the UV-vis and FT-IR spectra of the sensitizer anchored on their surfaces. In particular, the low-energy metal-to-ligand charge-transfer transitions (MLCT) band in the visible absorption spectra of N719 is strongly affected, and locations of these MLCT bands revealed larger differences. The results indicate that there is a red shift of MLCT band in the spectra obtained by using TiO2 nanocrystals with long morphology and large size compared to that in solution. And it produced a larger red-shift on the MLCT band after TiO2 nanocrystals with small size mixed with some long nanocrystals. Accordingly, the utilization rate to visible light is increased. This is a reason why the DSC prepared by using such film as a photoelectrode has better performance than before mixing.

1. Introduction

As such a concept for photovoltaic devices, dye-sensitized solar cells (DSCs) have received considerable attention since 1991 due to their relatively high efficiency and low fabrication cost [16]. Ruthenium polypyridyl complexes are commonly used as dyes in DSCs, and the highest power conversion efficiency of 11.3% has been achieved [7]. The typical DSC consists of a dye-coated mesoporous T i O 2 nanoparticle film sandwiched between two transparent electrodes, and a liquid electrolyte, traditionally containing the tri-iodide/iodide redox couple, fills the pores of the film and contacts the nanoparticle. Many factors, in particular, in the part of the photoelectrode such as morphology, particle size, and crystal structure of semiconductor T i O 2 [8], can affect the performance of DSC. They should be investigated in order to raise power conversion efficacy. In the past decade, much work has been done to improve the photovoltaic parameters of DSC including optimizing nanostructured semiconductor electrodes [9, 10], sensitizers [11, 12], redox electrolytes [13, 14], and electric additives [1517]. Only few studies, however, focused on the effect of the T i O 2 nanocrystals on the absorption spectra of the sensitizer anchored on their surfaces. Nazeeruddin et al. [18] reported merely the differences in the absorption spectra of sensitizer N3, N719, and N712 anchored on T i O 2 nanocrystals. In this study, the absorption spectra of sensitizer N719 anchored on T i O 2 nanocrystals with different morphology and particle size were investigated for increasing the utilization rate to visible light. The result is helpful to improve the performances of DSCs.

2. Experimental Details

2.1. Materials

10 wt% tetrabutylammonium hydroxide (TBAOH) aqueous solution and n-propylamine (PA) solution were purchased from Tokyo chemicals. N719 (cis-di(thiocyanate)bis(2,2′-bipyridyl-4,4′-dicarboxylate)-ruthenium(II) bis-tetrabutyl-ammonium) was purchased from Sigma-Aldrich. ST01 (commercial T i O 2 powder) was obtained from Ishihara. ST111 (commercial T i O 2 powder) was obtained from Titan Kogyo. Other chemicals and reagents were of analytical grade, and all the reagents were used as received without further purification.

2.2. Synthesis of TiO2 Nanocrystals

To prepare anatase samples QTBA, QPA, and LPA, an H + -form-layered titanate ( H 1 . 0 7 T i 1 . 7 3 O 4 ) with lepidocrocite-like structure was treated in a TBAOH solution or a PA solution to exfoliate the layered titanate into its nanosheets. The titanate nanosheet solution was then reacted under hydrothermal conditions [19, 20]. The QTBA was obtained by hydrothermal reaction of a titanate nanosheet solution of TBAOH at 120°C and pH 1.8. The samples QPA and LPA were obtained by hydrothermal reaction of a titanate nanosheet solution of PA at 120°C and pH 1.9, and at 135°C and pH 11.3, respectively.

2.3. Fabrication of Dye-Sensitized Solar Cell

A T i O 2 film electrode was prepared by the doctor-blade technique, using T i O 2 nanocrystal paste on an FTO glass plate ( 2 5 × 2 5  mm). The paste sample was prepared by dispersing T i O 2 nanocrystals sample in a 0.2 mol/L H N O 3 solution containing 3 wt% of Triton X-100, 5 wt% of acetylacetone, and 10 wt% of polyethylene glycol (PEG) (molecular weight of 20, 000). The T i O 2 content in the paste was adjusted to about 15–18 wt% to control the thickness of the T i O 2 film. After being coated with the paste on the FTO glass plate, the T i O 2 film electrode was calcined at 450°C for 30 min and then immersed into a 3 × 1 0 4  mol/L N719 dye solution in a mixed solvent of acetonitrile and tert-butyl alcohol (1 : 1 volume ratio) for 24 h to adsorb the dye onto the T i O 2 electrode. The DSC was comprised of the dye-adsorbed T i O 2 electrode and a Pt-coated conducting glass counter-electrode, with an electrolyte solution between the electrodes. The electrolyte solution contained butylmethylimidazolium iodide (0.60 mol/L), I 2 (0.03 mol/L), guanidinium thiocyanate (0.10 mol/L), and 4-tert-butylpyridine (0.50 mol/L) in a mixed solvent of acetonitrile and valeronitrile (85% : 15% volume ratio).

2.4. Photovoltaic Measurements

The photocurrent-voltage characteristic curves for the DSCs were measured using a Hokuto-Denko BAS100B electrochemical analyzer under irradiation with simulated sunlight of AM 1.5 (100 mW/cm2), using a sunlight simulator (YSS-E40, Yamashita Denso) and a 0.25 cm2 mask. The thicknesses of the T i O 2 films were measured using a SURFCOM 480A surface-shape determiner.

2.5. Physical Analysis

Powder X-ray diffraction (XRD) analysis of the samples was carried out on a SHIMADZU XRD-6100 X-ray diffractometer with Cu Kα ( 𝜆 = 0 . 1 5 4 1 8  nm) radiation for the investigation of the crystal structure of the samples. The size and morphology of the particles were observed using fieldemission scanning electron microscopy (FE-SEM) (Hitachi, Model S-900). Transmission electron microscopy (TEM) observation and selected-area electron diffraction (SAED) were performed on a JEOL Model JEM-3010 system at 300 kV, and the powder sample was supported on a microgrid. Nitrogen gas adsorption was carried out on a Quantachrome Autosorb-1-MP apparatus. The specific surface area was calculated from the adsorption data using the Brunauer-Emmett-Teller (BET) method. FT-IR spectra of the samples were measured on a Perkin Elmer Spectrum One spectrophotometer at a resolution of better than 2 cm−1 using the KBr technique. UV-visible spectra were recorded on a SHIMADZU UV-2450 spectrophotometer. A corresponding blank T i O 2 film was used as reference to obtain the UV-visible spectrum of the dye adsorbed on the T i O 2 film. Both have the same thickness.

3. Results and Discussion

3.1. Characterizations of TiO2 Nanocrystals

To investigate the influences of the morphology and size of T i O 2 nanocrystalstals on the UV-vis and FT-IR spectra of the sensitizer anchored on their surfaces, five kinds of T i O 2 nanocrystal samples with different crystal sizes and crystal morphologies were used in this study. Two are typical commercial T i O 2 nanocrystal samples, ST01 and ST111, with different crystal sizes. And the rest are three self-prepared anatase nanocrystal samples with different crystal morphologies and sizes: QTBA, QPA, and LPA. They were prepared from exfoliated layered titanate ( H 1 . 0 7 T i 1 . 7 3 O 4 ) nanosheet solutions by hydrothermal reactions [1921]. An XRD study indicated that they are single phase of anatase as shown in Figure 1. The width and acutance of diffraction peaks indicate the crystallinity increasing order of S T 0 1 < S T 1 1 1 < Q T B A < Q P A < L P A .

The TEM images of these T i O 2 nanocrystals are presented in Figure 2. The QTBA and QPA samples have quadrate crystal morphologies, but the size of the later is as large again as QTBA size of about 20 nm in width. The LPA sample has long nanoleaf-like crystal morphologies and larger size of about 30 nm in width and 300 nm in length. The SAED result indicated that QPA is a single crystal of anatase phase, which agrees with the XRD result in Figure 1.

The change in morphology can be explained by the effect of pH value on the dissolution reaction in the synthesis process [19]. The dissolution reactions along the (100), (001), and (101) planes of anatase phase can occur and cut the sheetlike particles into the quadrate anatase nanocrystals because of the acidic conditions (pH < 2) in the synthesis processes of QTBA and QPA samples, and the dissolution reaction only along the (100) plane can occur and cut the sheetlike particles into long nanoleaf-like anatase nanocrystals because the value of pH is 11.3 in the synthesis process of LPA sample. The ST01 and ST111 samples have spherical crystal morphologies with sizes of about 7 nm (ST01) and 10 nm (ST111), respectively. Figure 3 shows FE-SEM images of the single crystal of QTBA and LPA and the films prepared by using the corresponding single crystal. The results agree with TEM analysis and further indicate that the single crystals of QTBA and LPA are flat particles. The BET (Brunauer-Emmett-Teller) specific surface areas (SBET) of the T i O 2 nanoparticles samples are shown in Table 1. The SBET values increase in the order of LPA < QPA < QTBA < ST111 < ST01, which are in agreement with their crystal sizes.

3.2. Absorption Spectra Properties

The UV-vis and FT-IR absorption spectra properties of the N719 sensitizer anchored on the surfaces of T i O 2 nanocrystals ST01, ST111, QTBA, QPA, and LPA samples are shown in Table 1. The data about UV-vis absorption spectra of the N719 sample in ethanol solution and FT-IR absorption spectra of solid N719 sample are given in Table 1 for the comparison. The UV-vis absorption spectra of the N719 sample in ethanol solution reveals four broad bands as shown in Figure 4(a). The two broad visible bands at 531 and 390 nm are assigned to metal-to-ligand charge-transfer (MLCT) origin. The bands in the UV region at 313 and 215 nm with a shoulder at 253 nm are specified to intraligand ( 𝜋 - 𝜋 ) charge-transfer transitions. Figure 4(b) shows a comparison of the absorption spectra of N719 dye adsorbed onto the films (6 to 10  𝜇 m thick) prepared by T i O 2 nanocrystals samples with different morphologies and sizes, and UV-vis absorption spectra of corresponding blank films without absorption band in the visible region are shown in Figure 4(c) for comparison. The low-energy MLCT maximum in N719 dye is considerably shifted upon adsorption onto these films compared to the solution spectra. The blue shifts of the low-energy MLCT band occur onto ST01 (8 nm) and QTBA (14 nm) films. On the other hand, the red shifts of the low-energy MLCT band occur to LPA (67 nm), ST111 (6 nm), and QPA (5 nm) films, and the film prepared by mixing QTBA (80%) and LPA (20%), which induces the largest red shift from 531 to 631 nm. The results reveal that there is a red shift of MLCT band in the spectra obtained by using T i O 2 nanocrystals with long morphology and large size compared to that in solution. And a larger red shift occurs on the MLCT band after T i O 2 nanocrystals with small size mixed with some long nanocrystals. Accordingly, it increases the utilization rate to visible light. The results indicate that the morphology and size of T i O 2 nanocrystals can lead to a shift in the low-energy MLCT of N719 dye. The shift is due to the change in the energy of the lowest unoccupied molecular orbital (LUMO) of the ligand, causing the 𝜋 - 𝜋 and d 𝜋 - 𝜋 transitions to occur at higher or lower energies [18].

The data about the FT-IR absorption spectra of solid N719 sample in Table 1 show the characteristic band at 2104 cm−1 due to the 𝜈 (NCS) group. The bands at 1714 and 1237 cm−1 are assigned to the 𝜈 (C=O), and 𝜈 (C–O) groups, respectively. The other two strong bands at 1611 ( C O O a s ) and 1370 ( C O O s ) cm−1 are assigned to the asymmetric and the symmetric stretch of the carboxylate group, respectively. The bands at 1611, 1543, and 1406 cm−1 are assigned to the bipyridyl 𝜈 (C=C) absorption. The band at 1467 cm−1 is assigned to the 𝛿 ( C H 2 ) of the B u 4 N + cations. The bands at 2876 and 2964 cm−1 are assigned to 𝜈 (C−H) of tetrabutylammonium symmetric and asymmetric C H 2 and C H 3 groups, respectively [22]. To achieve high quantum yields of the excited state electron transfer process, the dye ideally needs to be in intimate contact with the semiconductor surface. The carboxylate functional groups of the dye serve as grafting agents for the oxide surface of the T i O 2 films. It is an important feature in a dye-sensitized solar cell for electronic communication between the complex and the substrate. The ruthenium complex N719 contains two carboxylic acid and two carboxylate groups. Thus, it can anchor onto the T i O 2 surface by a close overlap of the ligand 𝜋 orbitals and the titanium 3D orbitals. A comparison of FT-IR absorption spectra properties of N719 sensitizer anchored on the surfaces of the T i O 2 nanocrystals ST01, ST111, QTBA, QPA, and LPA samples is shown in Figure 5. The major difference between the solid and the adsorbed N719 spectra occurs in carboxylic acid and carboxylate group bands. The 𝜈 ( C O O s ) bands in all adsorbed N719 samples are shifted to higher energy compared to the carboxylate group band (1370 cm−1) of N719 complex. The shifts increase in the order of ST111 = QTBA (2 cm−1) < ST01 (3 cm−1) < LPA (9 cm−1) < QPA (14 cm−1). The 𝜈 ( C O O a s ) band at 1611 cm−1 also occurs in the shifts, which is to lower energy for ST01 (3 cm−1), ST111 (3 cm−1) and QTBA (4 cm−1), but higher energy for QPA (3 cm−1) and LPA (8 cm−1). The 𝜈 (C–O) bands in all adsorbed N719 samples are shifted to lower energy compared to that (1237 cm−1) in N719 complex. The increasing shift order of ST111 = QTBA (1 cm−1) < ST01 (2 cm−1) < LPA (3 cm−1) < QPA (6 cm−1) agrees with that of the 𝜈 ( C O O s ) bands. The 𝜈 (C=O) band is shifted to lower energy by 57 cm−1, from 1714 to 1657 cm−1 for ST01, ST111, and QTBA, and that in QPA is shifted only 1 cm−1, but the band in LPA is at 1741 cm−1 shifting to higher energy (27 cm−1). The 𝜈 (NCS) group, the bipyridyl 𝜈 (C=C) at 1543 and 1406 cm−1, and the 𝛿 ( C H 2 ) of the B u 4 N + cations bands are shifted hardly with the change of the morphology and the size of T i O 2 nanocrystals. The results indicated that the morphology and size of T i O 2 nanocrystals strongly affect on the 𝜈 ( C O O a s ), 𝜈 ( C O O s ), 𝜈 (C=O) and 𝜈 (C–O) bands. A primary reason is that the morphology and size of T i O 2 nanocrystals can affect the energy level binding mode between the N719 and the T i O 2 . Therefore, the vibration bands of carboxylic acid and carboxylate groups used in grafting the N719 onto T i O 2 nanocrystals with different morphology and size reveal the obvious differences. Besides, 𝜈 (C–H) bands of tetrabutylammonium symmetric and asymmetric C H 2 and C H 3 groups of the N719 anchoring onto the T i O 2 surface also reveal larger differences with the change of the morphology and the size of T i O 2 nanocrystals due to steric reasons.

3.3. Photovoltaic Properties

Typical current-voltage characteristic curves (thin line) for ST01-based, ST111-based, QTBA-based, QPA-based, and LPA-based DSCs are presented in Figure 6. The power conversion efficiency ( 𝜂 ) of the cell can be evaluated from the short circuit photocurrent density ( 𝐽 s c ), the open circuit potential ( 𝑉 o c ), the fill factor (ff) of the cell, and the intensity of the incident light ( 𝐼 s = 1 0 0  mW/cm2) using the equation 𝜂 = 𝐽 s c 𝑉 o c   ff/ 𝐼 s .  Photovoltaic parameters of 𝐽 s c , 𝑉 o c , ff, and 𝜂 for the DSCs prepared by using the above T i O 2 nanocrystals with different morphology and size are summarized in Table 2. These cell parameters are evaluated from the current-voltage curves of the DSCs in Figure 6.We observe that the 𝑉 o c value increases in the order of S T 0 1 < Q P A < Q T B A < L P A , and the 𝐽 s c value increases in the order of L P A < S T 0 1 < Q P A < Q T B A . It is also observed that QPA sample has the lowest ff and 𝜂 values, and LPA sample has the highest ff and 𝜂 values. The QTBA sample with the highest 𝐽 s c value has lower η value due to the lower ff value. One of the important factors is the conductivity of the T i O 2 film. It has been reported that increasing the conductivity of T i O 2 film by adding one-dimensional nanowire-like particles into the spherical nanoparticles can enhance the ff value [23, 24].

In order to improve the performance of the DSCs prepared by single T i O 2 nanocrystals samples, QTBA, QPA, and ST01 samples (80%) were mixed with the long leaflike LPA (20%), respectively. The photocurrent-voltage characteristic curves (thick line) of DSCs prepared respectively using the QTBA-LPA, QPA-LPA, and ST01-LPA mixed samples are shown in Figure 6. The cell parameters of 𝑉 o c , 𝐽 s c , ff, and 𝜂 for corresponding DSCs are summarized in Table 2. The cell parameters of 𝑉 o c , 𝐽 s c , ff, and 𝜂 for the DSC enhance 8%, 4%, 28%, and 43%, respectively, comparing with that for original QTBA-based DSC. And the 𝜂 value (7.74%) is also much higher than that of P25-based DSC (6.3%) [25]. The 𝜂 and 𝐽 s c values of the DSCs enhance 26% and 9% for QPA-LPA, and 48% and 32% for ST01-LPA, respectively, comparing with that for corresponding original DSC. The results reveal that the performance of the DSCs is significantly improved. The main reasons enhanced cell parameters are that the addition of the one-dimensional leaflike particles can effectively increase the conductivity for transferring the photoelectrons from the T i O 2 film to FTO glass surface that decreases the recombination loss of injected electrons in T i O 2 film [26], and the relatively larger particle size of LPA also causes the light-trapping effect that enhances the 𝐽 s c [27]. The other reason of the improved cell parameters is that the added LPA with the long leaf-like morphology and larger size brings the larger red shifts of MLCT band of the N719 dye onto the T i O 2 nanocrystals films. The 𝐽 s c value (mA/cm2) increases from 19.9 for QTBA to 20.6 for QTBA-LPA with the red shift of 𝜆 m a x of the MLCT band from 517 to 631 nm. This red shift can expand the absorption region of visible light and thus increases the utilization rate to visible light. Therefore, this would enhance 𝐽 s c and 𝜂 values of the DSCs as well.

4. Conclusions

The morphology and the size of T i O 2 nanocrystals can affect on the UV-vis and FT-IR spectra of the sensitizer anchored on their surfaces. In particular, the low-energy metal-to-ligand charge-transfer transitions band in the visible absorption spectra is shifted after dye N719 adsorbed onto T i O 2 nanocrystals. The maximum wavelength of low-energy MLCT bands increases in the order of q u a d r a t e < s p h e r i c a l < l o n g c r y s t a l . The wavelength increases with the particle size as well. The results indicate that there is a red shift of MLCT band in the spectra obtained by using T i O 2 nanocrystals with long morphology and large size compared to that of N719 in solution. And a larger red shift of the MLCT band arises after T i O 2 nanocrystals with small size mixed with some long nanocrystals, which increases the utilization rate to visible light. This is a reason that the DSC prepared by using such film has better performance than that of before mixing. The morphology and the size of T i O 2 nanocrystals affect strongly on the 𝜈 ( C O O a s ), 𝜈 ( C O O s ), 𝜈 (C=O), and 𝜈 (C−O) bands. The main reason is that the morphology and the size of T i O 2 nanocrystals can affect the energy level binding mode between the N719 and the T i O 2 . Therefore, the vibration bands of carboxylic acid and carboxylate groups used in grafting the N719 onto T i O 2 nanocrystals with different morphology and size reveal the obvious differences.

Acknowledgments

This work was supported by the Natural Science Foundation of China (no. 21173003), the Scientific Research Project from Science and Technology Department of Shaanxi Province (no. 2011JM2009), and the Key Research Project from Baoji University of Arts and Sciences (no. ZK1051).