Bulky Macroporous TiO<sub>2</sub> Photocatalyst with Cellular Structure via Facile Wood-Template Method

Sun, Qingfeng; Lu, Yun; Tu, Jinchun; Yang, Dongjiang; Cao, Jun; Li, Jian

doi:https://doi.org/10.1155/2013/649540

International Journal of Photoenergy

On this page

Abstract Introduction Materials Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Special Issue

Progress and Perspectives in Visible-Light-Driven Photocatalysis

View this Special Issue

Research Article | Open Access

Volume 2013 | Article ID 649540 | https://doi.org/10.1155/2013/649540

Bulky Macroporous TiO₂ Photocatalyst with Cellular Structure via Facile Wood-Template Method

Qingfeng Sun,^1,2Yun Lu,¹Jinchun Tu,³Dongjiang Yang,⁴Jun Cao,²and Jian Li¹

Academic Editor: Elias Stathatos

Received20 Jan 2013

Revised14 Mar 2013

Accepted15 Mar 2013

Published03 Apr 2013

Abstract

We report a bulky macroporous TiO₂ particles with cellular structure prepared in the presence of wood slices as template. Firstly, TiO₂ sol was coated onto the wood slices by repeated dip-coating process. Then, after calcinations at 550°C, the wood template could be removed, and the bulky TiO₂ structure was obtained. The prepared samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), and transmission electron microscope (TEM) techniques. XRD pattern confirmed the crystalline phase of the wood-templated TiO₂ is anatase phase. And interestingly, from the observation of SEM image, the wood-templated TiO₂ inherited the initial cellular structures of birch lumber (B. albosinensis Burk), and numerous macropores were observed in the sample. Meanwhile, the wood-templated TiO₂ presented a superior photocatalytic ability to decompose Rhodamine B (RhB) under ultraviolet irradiation.

1. Introduction

Template-directed synthesis is currently one of the most widely used methods for fabricating inorganic materials on account of its facility and versatility [1–4]. In addition to some artificial templates like latex particles [5], polymer foams [6], ion-exchange resins [7], and carbon fibers [8], many natural templates have been attracted to much attention for constructing a number of inorganic materials. The natural species utilized as templates for the formation of inorganic materials are available from bacterial superstructures [9], insect wings [10], wool and cotton/cloth textile [11], diatoms [12], dog and human hair [13], living cells [14], mushroom gills [13], plant leaves [10], paper [15], pollen grains [16], shell membrane [17], silk fiber [13], skeletal plates [18], spider silk [8, 10], and wood [19–24]. These materials from nature combine many inspiring properties, such as sophistication, miniaturization, hierarchical organizations, hybridization, resistance, and adaptability, after billions of years of stringent selection processes [4]. From the research results, using natural species as template for building inorganic materials is an effective strategy to obtain morphology controllable materials with structural specialty, complexity, and related unique properties.

Among these natural templates, wood is a naturally grown composite material possessing complex hierarchical cellular and pit structures that are comprised principally of biopolymers, mainly cellulose, hemicellulose, and lignin [25, 26]. The wood vessels and fibers are hollow tubes, and the arrangement of these vessels and fibers varies considerably different with different wood species. The cellular structural hierarchy of wood ranges from the millimeter scale of the growth ring and longitudinal tracheid, the micrometer scale of the cell wall and diameter, to the nanometer scale of the molecular fiber and membrane structure of the cell wall. The open porosity is accessible for liquid or gaseous infiltration [3, 20]. These features of wood make it a perfect candidate as a template for generating porous inorganic materials with both structural and morphological complexities. Previously some efforts have been made toward transforming wood cellular structures into inorganic SiC [27, 28], TiC [29], and macroporous zeolites [20]. By impregnating the wood templates with metal alkoxide solutions and applying standard sol-gel chemistry, various metal oxide porous materials, such as TiO₂ [30], Al₂O₃ [31], Fe₂O₃ [21], and Cr₂O₃ [32], have been produced using this approach.

In these inorganic materials, TiO₂ is one of the most promising functional materials and extensively used in photocatalysis [33, 34], solar cells [35], and paints [36] because of its superior chemical stability and nontoxicity [37, 38]. TiO₂ exists mainly in four polymorphs in nature, anatase (tetragonal, space group I4₁/amd), rutile (tetragonal, space group P4₂/mnm), brookite (orthorhombic, space group Pbca), and TiO₂(B) (monoclinic, space group C2/m) [39–42]. In photocatalytic study, anatase TiO₂ is generally considered to be more active than rutile crystalline [43]. Moreover, anatase TiO₂ with higher crystallinity is preferred for photocatalysis, since higher crystallinity means fewer defects for the recombination of photogenerated electrons and holes [36]. In the current research, different kinds of TiO₂ nanomaterials like nanoparticles, nanosheet, nanotube, or nanofiber have been fabricated using different method. However, TiO₂ with wood structures has been seldom reported.

To this purpose, we developed an efficient pathway to synthesize wood-templated TiO₂. The morphology, chemical compositions, and crystalline phase of the prepared TiO₂ were characterized by SEM, EDS, HRTEM, and XRD, respectively. Furthermore, the photocatalytic activity of the wood-templated TiO₂ was measured under UV irradiation.

2. Materials and Method

2.1. Raw Materials

All the chemicals were supplied by Shanghai Boyle Chemical Co. Ltd. and used as received. The air-dried birch lumber (B. albosinensis Burk) was cut into slices with a size of 20 mm (tangential) × 20 mm (radial) × 2 mm (longitudinal). The wood slices were pretreated in a Soxhlet apparatus with 95% ethanol at 80°C for 6 h under reflux to remove the extracts like the fats and fatty acids in the wood. Then these slices were rinsed with deionized water. Finally, the treated wood slices were vacuumly dried at 60°C for over 24 hours.

2.2. Preparation of TiO₂ Sol

Tetrabutylorthotitanate (TBOT), diethanolamine (DEA), and absolute ethanol were used as starting materials. The 34 mL of TBOT and 11 mL of DEA were dissolved in 100 mL ethanol to prepare the precursor solution. After stirring for 2 h at room temperature, a mixed solution of 55 mL water and 9 ml ethanol was dropwise added following stirred another 3 h. Then TiO₂ sol was obtained.

2.3. Fabrication of Wood-Templated TiO₂

Firstly, wood slices were coated by TiO₂ sol through a repeated dip-coating process. The pretreated wood slices were immersed into the as-prepared TiO₂ sol for 5 min. After that, these slices were dried at 80°C for 3 h. This process was repeated for 5 times to ensure TiO₂ sol densely and evenly covered onto the wood slices. Then, calcination process was employed to remove the wood template. To get wood-templated TiO₂, wood coated by TiO₂ sol was calcined in a muffle furnace at the temperature of 550°C for 3 h in air atmosphere and air cooled to room temperature. Finally, the calcined samples were taken out from the muffle furnace, and the wood-templated TiO₂ was obtained.

2.4. Characterizations

The morphology of the samples was observed by scanning electron microscopy (SEM, FEI, Quanta 200) and transmission electron microscopy (TEM, FEI Tecnai F20). The chemical compositions of the untreated and treated wood were measured by energy dispersive spectroscopy (EDS, attached to the SEM). The crystalline structures were identified by X-ray diffraction (XRD, Rigaku, D/MAX 2200) operating with Cu Kα radiation ( Å) at a scan rate (2θ) of 4°/min with an accelerating voltage of 40 kV and an applied current of 30 mA ranging from 10° to 70°.

2.5. Evaluation of Photocatalytic Activity

The photocatalytic activity of the samples was estimated through the decomposition of Rhodamine B (RhB) in a reactor with a volume of 100 mL. The irradiation source was an ultraviolet 100 W lamp (Shanghai Rongbo Co., China) with a wavelength of 254 nm. The photocatalytic activities of the prepared products were judged by measuring the loss of RhB in aqueous solution. A suspension involving 100 mg of catalyst and 100 mL RhB solution with an original concentration of 50 mg/L was magnetically stirred on the dark for 1 h without interrupting before irradiation. The change of solution concentration in every 30 min was measured to judge the absorbability of catalysts in the dark. At every interval during the process of 3 h, a certain sample of the mixture was collected, centrifuged, and then measured. The degradation rate for denoting the degradation efficiency of RhB was obtained by measuring the change in absorbance on a UV-Vis spectrophotometer (TU-190, Beijing Purkinje, China), and its maximum absorption wavelength of RhB was 554.5 nm. The schematic diagram of the photocatalytic reactor was represented in Figure 1.

3. Results and Discussion

Figure 2 showed the morphologies of the cross-section of the original wood, wood coated by TiO₂ sol, and wood-templated TiO₂, respectively. As shown in Figure 2(a), the cellular structures of the original wood could be clearly observed. The wood vessels with the diameter of about 20~50 μm are irregular circular. The wood fibers with the diameter of about 5~20 μm are uniformly arranged among the wood vessels. In Figure 2(b), the wood structure has not obviously changed after the dip-coating process by TiO₂ sol. It can be clearly seen from the Figure 2(c) that the structures of the original wood were commendably remained after the calcined process. In the magnified SEM image (Figure 2(d)), calcined wood vessels with a little collapse could be obviously observed with the diameter of about 35 μm. Simultaneously, the calcined wood fibers shown in Figure 2(e) with a thinner cellular wall compared to the original wood were well arranged without any collapse. The diameters of these fibers are about 15 μm. In a word, TiO₂ with the wood cellular structure was successfully prepared by dip-coating and calcination process. The microscopic structures of the original wood could not be destroyed with the previous process.

EDS spectra were also recorded for the original wood, wood coated by TiO₂ sol, and wood-templated TiO₂, respectively. As shown in Figure 3(a), the carbon, oxygen, and gold elements could be detected from the EDS spectrum of the original wood. The elements of carbon and oxygen are originated from the wood substrate, and the element of gold is from the coating layer used for SEM observation. Besides the signal of carbon and oxygen elements, titanium and nitrogen elements were displayed in the spectrum of TiO₂ sol-coated wood slices (Figure 3(b)). The elements of titanium and nitrogen are stemmed from TBOT and DEA in the TiO₂ sol, respectively. After calcination at 550°C, only oxygen and titanium elements could be probed from the EDS spectrum (Figure 3(c)), and no other elements were detected which confirmed that the components of the original wood and the TiO₂ precursor were completely removed during the calcination process.

(a)

(b)

(c)

XRD patterns of the original wood, the wood coated by TiO₂ sol, and wood-templated TiO₂ were presented in Figure 4. Figure 4(a) revealed a typical XRD pattern of the original wood. The diffraction peaks at 16° and 22.6° were believed to represent the crystalline region of the cellulose in wood [25]. In Figure 4(b), no other new diffraction peaks were founded except for the diffractive characteristics of the initial wood, which might be due to that the crystal phase of TiO₂ sol is consisted of amorphous TiO₂ before the calcination. Apparently, in Figure 4(c), the diffraction peaks at 16° and 22.6° belonging to the original wood sample disappeared. New strong diffraction peaks were observed for the calcined sample, which indicated the formation of new crystal structures of the calcined wood sample. As shown in pattern of wood-templated TiO₂, the diffraction peaks at 25°, 38°, 48°, and 54° could be assigned to the diffractions of the (101), (004), (200), and (211) planes of anatase TiO₂ (JCPDS number 21-1272) [36, 40], respectively. XRD pattern of the wood-templated TiO₂ also confirmed that the components of the pristine wood were completely got rid of through the calcination process.

TEM images in Figure 5(a) revealed a much more fine structure of the obtained TiO₂ sintered at 550°C for 3 h. Though TiO₂ sample has been pulverized, the slices were found in the TEM image, just like the cellular framework of the original wood. Consequently, we could safely conclude that the cellular structure of the original wood has been preserved after the calcination process. The selected area electron diffraction (SAED) of the slice in Figure 5(b) illuminated the crystalline phase of the wood-templated TiO₂ is polycrystalline with the coexistence of the diffraction rings and spots at the SAED pattern. The HRTEM image in Figure 5(c) revealed that the distance between the adjacent lattice fringes of (101) planes is about 0.352 nm which is corresponding to the anatase TiO₂ crystal (a = 0.325 nm, c = 0.521 nm).

(a)

(b)

(c)

The photocatalytic ability of the obtained cellular-structured TiO₂ was investigated by decomposing RhB dye, a very difficult degradable and highly toxic organic pollutant. The photodegradation curves of RhB were exhibited in Figure 6. The wood-templated TiO₂ could photodegrade the RhB under UV light irradiation. The original wood shown in Figure 6(a) had a little photocatalytic activity of about 4.6% on RhB. It was mainly ascribed to the physical absorption effect because of porous wood. In Figure 6(b), the wood coated by TiO₂ sol showed a photocatalytic activity of about 8.21% on RhB. However, wood-templated TiO₂ expressed a superior photocatalytic activity of about 92.5% on RhB (Figure 6(c)). The photocatalytic efficiency of the obtained TiO₂ was greatly enhanced probably, since the prepared TiO₂ remained the original wood cellular structures. The original wood porous structure could be affording a portable carrier for absorbing and degrading much organic pollutants.

Meanwhile, the photocatalytic activity of wood-templated TiO₂ was compared to the commercially available TiO₂ P25 (Degussa, Germany) that consist of both anatase (80%) and rutile (20%) phases of TiO₂. The same experimental conditions were selected for P25. From the comparison between catalysts wood-templated TiO₂ and P25 (Figure 6(d)), it can be seen that RhB underwent decomposition of a little faster in the case of the latter catalyst. But the problem with the P25 powder is that the TiO₂ disperses in water forming a white colloidal solution, and it is difficult to separate from the reaction mixture for reuse. The separation performance test showed that the wood-templated TiO₂ has a good sedimentation ability and can decanted from the suspension in about 15 min, while the P25 do not decant after 45 min.

4. Conclusions

In the present paper, the anatase wood-templated TiO₂ was successfully fabricated by using a facile dip-coating and subsequent calcination process. The as-prepared TiO₂ possessed the typical cellular structure with unbroken vessels and uniformly arranged wood fibers. Also, this wood-templated TiO₂ presented a superior photocatalytic degradation of RhB. This paper probably provided another way for fabricating inorganic materials using the natural wood as template.

Acknowledgments

This work was financially supported by The National Natural Science Foundation of China (Grant nos. 31270590 and 21207073) and National Basic Research Program of China (973 Program, Grant no. 2009CB220000).

References

S. V. N. T. Kuchibhatla, A. S. Karakoti, D. Bera, and S. Seal, “One dimensional nanostructured materials,” Progress in Materials Science, vol. 52, no. 5, pp. 699–913, 2007.
View at: Publisher Site | Google Scholar
J. Li, Q. Xu, J. Wang, J. Jiao, and Z. Zhang, “Controlled synthesis of monolithic hierarchical porous materials using wood as a template with assistance of supercritical carbon dioxide,” Industrial and Engineering Chemistry Research, vol. 47, no. 20, pp. 7680–7685, 2008.
View at: Publisher Site | Google Scholar
O. Paris, I. Burgert, and P. Fratzl, “Biomimetics and biotemplating of natural materials,” MRS Bulletin, vol. 35, no. 3, pp. 219–225, 2010.
View at: Google Scholar
H. Zhou, T. Fan, and D. Zhang, “Biotemplated materials for sustainable energy and environment: current status and challenges,” ChemSusChem, vol. 4, no. 10, pp. 1344–1387, 2011.
View at: Publisher Site | Google Scholar
L. Huang, Z. Wang, J. Sun et al., “Fabrication of ordered porous structures by self-assembly of zeolite nanocrystals,” Journal of the American Chemical Society, vol. 122, no. 14, pp. 3530–3531, 2000.
View at: Publisher Site | Google Scholar
Y. J. Lee, J. S. Lee, Y. S. Park, and K. B. Yoon, “Synthesis of large monolithic zeolite foams with variable macropore architectures,” Advanced Materials, vol. 13, no. 16, pp. 1259–1263, 2001.
View at: Publisher Site | Google Scholar
L. Tosheva, B. Mihailova, V. Valtchev, and J. Sterte, “Zeolite beta spheres,” Microporous and Mesoporous Materials, vol. 48, no. 1–3, pp. 31–37, 2001.
View at: Publisher Site | Google Scholar
Y. J. Wang, Y. Tang, X. D. Wang, W. L. Yang, and Z. Gao, “Fabrication of hollow zeolite fibers through layer-by-layer adsorption method,” Chemistry Letters, no. 11, pp. 1344–1345, 2000.
View at: Google Scholar
S. A. Davis, S. L. Burkett, N. H. Mendelson, and S. Mann, “Bacterial templating of ordered macrostructures in silica and silica-surfactant mesophases,” Nature, vol. 385, no. 6615, pp. 420–423, 1997.
View at: Publisher Site | Google Scholar
G. Cook, P. L. Timms, and C. Göltner-Spickermann, “Exact replication of biological structures by chemical vapor deposition of silica,” Angewandte Chemie—International Edition, vol. 42, no. 5, pp. 557–559, 2003.
View at: Publisher Site | Google Scholar
H. Imai, M. Matsuta, K. Shimizu, H. Hirashima, and N. Negishi, “Preparation of TiO₂ fibers with well-organized structures,” Journal of Materials Chemistry, vol. 10, no. 9, pp. 2005–2006, 2000.
View at: Publisher Site | Google Scholar
M. W. Anderson, S. M. Holmes, N. Hanif, and C. S. Cundy, “Hierarchical pore structures through diatom zeolitization,” Angewandte Chemie—International Edition, vol. 39, no. 15, pp. 2707–2710, 2000.
View at: Publisher Site | Google Scholar
Y. Kim, “Small structures fabricated using ash-forming biological materials as templates,” Biomacromolecules, vol. 4, no. 4, pp. 908–913, 2003.
View at: Publisher Site | Google Scholar
S. Chia, J. Urano, F. Tamanoi, B. Dunn, and J. I. Zink, “Patterned hexagonal arrays of living cells in sol-gel silica films,” Journal of the American Chemical Society, vol. 122, no. 27, pp. 6488–6489, 2000.
View at: Publisher Site | Google Scholar
A. N. Shigapov, G. W. Graham, R. W. McCabe, and H. K. Plummer Jr., “The preparation of high-surface area, thermally-stable, metal-oxide catalysts and supports by a cellulose templating approach,” Applied Catalysis A, vol. 210, no. 1-2, pp. 287–300, 2001.
View at: Publisher Site | Google Scholar
S. R. Hall, H. Bolger, and S. Mann, “Morphosynthesis of complex inorganic forms using pollen grain templates,” Chemical Communications, vol. 9, no. 22, pp. 2784–2785, 2003.
View at: Google Scholar
D. Yang, L. Qi, and J. Ma, “Eggshell membrane templating of hierarchically ordered macroporous networks composed of TiO₂ tubes,” Advanced Materials, vol. 14, no. 21, pp. 1543–1546, 2002.
View at: Publisher Site | Google Scholar
F. C. Meldrum and R. Seshadri, “Porous gold structures through templating by echinoid skeletal plates,” Chemical Communications, no. 1, pp. 29–30, 2000.
View at: Google Scholar
T. Ota, M. Imaeda, H. Takase et al., “Porous titania ceramic prepared by mimicking silicified wood,” Journal of the American Ceramic Society, vol. 83, no. 6, pp. 1521–1523, 2000.
View at: Google Scholar
A. Dong, Y. Wang, Y. Tang et al., “Zeolitic tissue through wood cell templating,” Advanced Materials, vol. 14, no. 12, pp. 926–929, 2002.
View at: Publisher Site | Google Scholar
Z. Liu, T. Fan, W. Zhang, and D. Zhang, “The synthesis of hierarchical porous iron oxide with wood templates,” Microporous and Mesoporous Materials, vol. 85, no. 1-2, pp. 85–88, 2005.
View at: Publisher Site | Google Scholar
Z. Liu, T. Fan, and D. Zhang, “Synthesis of biomorphous nickel oxide from a pinewood template and investigation on a hierarchical porous structure,” Journal of the American Ceramic Society, vol. 89, no. 2, pp. 662–665, 2006.
View at: Publisher Site | Google Scholar
Z. Liu, T. Fan, D. Zhang, X. Gong, and J. Xu, “Hierarchically porous ZnO with high sensitivity and selectivity to H₂S derived from biotemplates,” Sensors and Actuators B, vol. 136, no. 2, pp. 499–509, 2009.
View at: Publisher Site | Google Scholar
Z. Liu, T. Fan, J. Ding, D. Zhang, Q. Guo, and H. Ogawa, “Synthesis and cathodoluminescence properties of porous wood (fir)-templated zinc oxide,” Ceramics International, vol. 34, no. 1, pp. 69–74, 2008.
View at: Publisher Site | Google Scholar
J. Li, Y. Lu, D. Yang, Q. Sun, Y. Liu, and H. Zhao, “Lignocellulose aerogel from wood-ionic liquid solution (1-allyl-3-methylimidazolium chloride) under freezing and thawing conditions,” Biomacromolecules, vol. 12, no. 5, pp. 1860–1867, 2011.
View at: Publisher Site | Google Scholar
Y. Lu, Q. Sun, D. Yang et al., “Fabrication of mesoporous lignocellulose aerogels from wood via cyclic liquid nitrogen freezing-thawing in ionic liquid solution,” Journal of Materials Chemistry, vol. 22, no. 27, pp. 13548–13557, 2012.
View at: Publisher Site | Google Scholar
J. M. Qian, J. P. Wang, and Z. H. Jin, “Preparation and properties of porous microcellular SiC ceramics by reactive infiltration of Si vapor into carbonized basswood,” Materials Chemistry and Physics, vol. 82, no. 3, pp. 648–653, 2003.
View at: Publisher Site | Google Scholar
P. Greil, T. Lifka, and A. Kaindl, “Biomorphic cellular silicon carbide ceramics from wood—I: processing and microstructure,” Journal of the European Ceramic Society, vol. 18, no. 14, pp. 1961–1973, 1998.
View at: Publisher Site | Google Scholar
B. Sun, T. Fan, and D. Zhang, “Porous TiC ceramics derived from wood template,” Journal of Porous Materials, vol. 9, no. 4, pp. 275–277, 2002.
View at: Publisher Site | Google Scholar
J. Huang and T. Kunitake, “Nano-precision replication of natural cellulosic substances by metal oxides,” Journal of the American Chemical Society, vol. 125, no. 39, pp. 11834–11835, 2003.
View at: Publisher Site | Google Scholar
C. R. Rambo and H. Sieber, “Novel synthetic route to biomorphic Al₂O₃ ceramics,” Advanced Materials, vol. 17, no. 8, pp. 1088–1091, 2005.
View at: Publisher Site | Google Scholar
T. Fan, X. Li, Z. Liu, J. Gu, D. Zhang, and Q. Guo, “Microstructure and infrared absorption of biomorphic chromium oxides templated by wood tissues,” Journal of the American Ceramic Society, vol. 89, no. 11, pp. 3511–3515, 2006.
View at: Publisher Site | Google Scholar
M. Anpo and M. Takeuchi, “Design and development of second-generation titanium oxide photocatalysts to better our environment—approaches in realizing the use of visible light,” International Journal of Photoenergy, vol. 3, no. 2, pp. 89–94, 2001.
View at: Google Scholar
A. D. Paola, S. Ikeda, G. Marcì, B. Ohtani, and L. Palmisano, “Transition metal doped TiO₂: physical properties and photocatalytic behaviour,” International Journal of Photoenergy, vol. 3, no. 4, pp. 171–176, 2001.
View at: Google Scholar
C. C. Hu, T. C. Hsu, and L. H. Kao, “One-step cohydrothermal synthesis of nitrogen-doped titanium oxide nanotubes with enhanced visible light photocatalytic activity,” International Journal of Photoenergy, vol. 2012, Article ID 391958, 9 pages, 2012.
View at: Publisher Site | Google Scholar
X. Chen and S. S. Mao, “Titanium dioxide nanomaterials: synthesis, properties, modifications and applications,” Chemical Reviews, vol. 107, no. 7, pp. 2891–2959, 2007.
View at: Publisher Site | Google Scholar
N. Al Dahoudi, Q. Zhang, and G. Cao, “Alumina and hafnia ald layers for a niobium-doped titanium oxide photoanode,” International Journal of Photoenergy, vol. 2012, Article ID 401393, 6 pages, 2012.
View at: Publisher Site | Google Scholar
V. K. Sharma, K. Winkelmann, Y. Krasnova, C. Lee, and M. Sohn, “Heterogeneous photocatalytic reduction of ferrate(VI) in UV-irradiated titania suspensions: role in enhancing destruction of nitrogen-containing pollutants,” International Journal of Photoenergy, vol. 5, no. 3, pp. 183–190, 2003.
View at: Google Scholar
D. J. Yang, Z. F. Zheng, H. Y. Zhu, H. W. Liu, and X. P. Gao, “Titanate nanofibers as intelligent absorbents for the removal of radioactive ions from water,” Advanced Materials, vol. 20, no. 14, pp. 2777–2781, 2008.
View at: Publisher Site | Google Scholar
D. Yang, H. Liu, Z. Zheng et al., “An efficient photocatalyst structure: TiO₂(B) nanofibers with a shell of anatase nanocrystals,” Journal of the American Chemical Society, vol. 131, no. 49, pp. 17885–17893, 2009.
View at: Publisher Site | Google Scholar
D. Yang, C. Chen, Z. Zheng et al., “Grafting silica species on anatase surface for visible light photocatalytic activity,” Energy and Environmental Science, vol. 4, no. 6, pp. 2279–2287, 2011.
View at: Publisher Site | Google Scholar
D. Yang, S. Sarina, H. Zhu et al., “Capture of radioactive cesium and iodide ions from water by using titanate nanofibers and nanotubes,” Angewandte Chemie—International Edition, vol. 50, no. 45, pp. 10594–10598, 2011.
View at: Publisher Site | Google Scholar
H. Yang, S. Zhu, and N. Pan, “Studying the mechanisms of titanium dioxide as ultraviolet-blocking additive for films and fabrics by an improved scheme,” Journal of Applied Polymer Science, vol. 92, no. 5, pp. 3201–3210, 2004.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2013 Qingfeng Sun et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2079

Downloads

1649

Citations