A Suitable Polysulfide Electrolyte for CdSe Quantum Dot-Sensitized Solar Cells
Table 6
Performance parameters of CdSe QDSSC with different polysulfide electrolyte compositions reported by various groups.
| Photoanode configuration | Electrolyte composition | (mA/cm2) | (V) | Fill factor (%) | Efficiency (%) | Reference |
| TiO2/CdSe | 0.5 M Na2S, 0.1 M S, 0.05 M GuSCN in ethanol/water (8 : 2 by volume) | 6.80 | 0.470 | 44.0 | 1.41 | This work | TiO2/CdSe | 0.5 M Na2S, 0.1 M S, 0.2 M KCl in methanol/water (3 : 7 by volume) | 10.61 | 0.378 | 36.0 | 1.40 | [16] | TiO2/CdS/CdSe/ZnS | 0.5 M Na2S, 0.1 M S, 0.2 M KCl in methanol/water (3 : 7 by volume) | 11.66 | 0.503 | 49.0 | 2.90 | [16] | TiO2/CdSe | 1 M Na2S, 1 M S in aqueous | 6.03 | 0.680 | 39.0 | 1.60 | [19] | TiO2/F/CdSe/F/ZnS | 1 M Na2S, 1 M S in aqueous | 7.51 | 0.710 | 50.0 | 2.70 | [19] | TiO2/CdSe | 1 M Na2S, 0.1 M S, 0.1 M NaOH in ultrapure water | 3.06 | 0.430 | 21.0 | 0.28 | [20] | TiO2/CdSe/ZnS | 1 M Na2S, 0.1 M S, 0.1 M NaOH in ultrapure water | 7.13 | 0.510 | 48.0 | 1.83 | [20] | TiO2/CdSe | 1 M Na2S, 0.1 M S, 0.1 M KOH in aqueous | 2.70 | 0.554 | 26.0 | 0.40 | [21] | TiO2/CdSe/ZnS | 1 M Na2S, 0.1 M S, 0.1 M KOH in aqueous | 9.00 | 0.554 | 35.0 | 1.70 | [21] |
|
|