Efficiency Enhancement of Nanoporous Silicon/Polycrystalline-Silicon Solar Cells by Application of Trenched Electrodes

<table>Photocurrent and dark current of the NPS/poly-Si cells with and without a trenched-electrode-contact (TEC) structure. The photocurrent is measured by a solar simulator under <svg height="12.3115pt" id="M5" style="vertical-align:-3.31355pt" version="1.1" viewbox="-0.0498162 -8.99795 48.0359 12.3115" width="48.0359pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.0135,0,0,-0.0135,0,0)"><path d="M600 480C600 590 528 650 384 650H143L137 622C222 614 225 607 210 531L130 127C113 41 106 36 23 28L17 0H294L300 28C204 36 195 42 212 127L243 284L314 263C327 263 339 263 352 264C465 271 600 337 600 480ZM508 481C508 351 402 304 329 304C289 304 265 311 250 317L295 559C302 594 310 606 323 611C335 616 350 619 367 619C455 619 508 573 508 481Z" id="g113-81"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="617" vert-adv-y="617"></glyph.data></g><g transform="matrix(.0095,0,0,-0.0095,6.937,3.264)"><path d="M567 167L534 181C505 122 482 94 454 70C428 46 385 42 330 42C288 42 248 44 235 55C216 70 213 91 220 130L295 528C310 609 314 611 401 618L409 650H140L131 618C222 611 224 609 209 528L133 126C118 47 108 41 25 33L18 0H497C514 33 554 126 567 167Z" id="g50-77"></path><glyph.data ascent="3443" descent="-2856" horiz-adv-x="579" vert-adv-y="579"></glyph.data></g><g transform="matrix(.0135,0,0,-0.0135,16.56,0)"><path d="M535 323V373H52V323H535ZM535 138V188H52V138H535Z" id="g117-34"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="587" vert-adv-y="587"></glyph.data></g><g transform="matrix(.0135,0,0,-0.0135,28.298,0)"><path d="M384 0V27C293 34 287 42 287 114V635C232 613 172 594 109 583V559L157 557C201 555 205 550 205 499V114C205 42 199 34 109 27V0H384Z" id="g113-50"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g><g transform="matrix(.0135,0,0,-0.0135,34.801,0)"><path d="M241 635C89 635 35 457 35 312C35 153 89 -12 240 -12C390 -12 443 166 443 312C443 466 390 635 241 635ZM238 602C329 602 354 454 354 312C354 172 330 22 240 22C152 22 124 173 124 313S148 602 238 602Z" id="g113-49"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g><g transform="matrix(.0135,0,0,-0.0135,41.304,0)"><path d="M241 635C89 635 35 457 35 312C35 153 89 -12 240 -12C390 -12 443 166 443 312C443 466 390 635 241 635ZM238 602C329 602 354 454 354 312C354 172 330 22 240 22C152 22 124 173 124 313S148 602 238 602Z" id="g113-49"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g></svg> mA/cm<sup>2</sup> at AM1.5.</table>

International Journal of Photoenergy

fig5

Figure 5

Figure 5: Efficiency Enhancement of Nanoporous Silicon/Polycrystalline-Silicon Solar Cells by Application of Trenched Electrodes 