Synthesis and Characterization of Cerium Doped Titanium Catalyst for the Degradation of Nitrobenzene Using Visible Light

Ellappan, Padmini; Miranda, Lima Rose

doi:https://doi.org/10.1155/2014/756408

International Journal of Photoenergy

On this page

Abstract Introduction Results and Discussion Conclusion References Copyright Related Articles

Special Issue

Advanced Oxidation Processes for Wastewater Treatment 2013

View this Special Issue

Research Article | Open Access

Volume 2014 | Article ID 756408 | https://doi.org/10.1155/2014/756408

Synthesis and Characterization of Cerium Doped Titanium Catalyst for the Degradation of Nitrobenzene Using Visible Light

Padmini Ellappan¹and Lima Rose Miranda¹

Academic Editor: Manickavachagam Muruganandham

Received22 May 2013

Accepted03 Oct 2013

Published06 Jan 2014

Abstract

Cerium doped catalyst was synthesized using Titanium isopropoxide as the Titanium source. The metal doped nanoparticles semiconductor catalyst was prepared by sol-sol method with the sol of Cerium. The synthesized catalyst samples were characterized by powder X-ray diffraction, BET surface area, thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and UV-vis diffuse reflectance measurements (DRS) and compared with undoped TiO₂ catalyst. The photocatalytic activity of the sample was investigated for the decomposition of nitrobenzene (NB) using visible light as the artificial light source. Cerium doped catalyst was found to have better degradation of nitrobenzene owing to its shift in the band gap from UV to visible region as compared to undoped TiO₂ catalyst. The operational parameters were optimized with catalyst dosage of 0.1 g L⁻¹, pH of 9, and light intensity of 500 W. The degradation mechanism followed the Langmuir Hinshelwood kinetic model with the rate constant depending nonlinearly on the operational parameters as given by the relationship (theoretical) = 2.29 * 10⁻⁴ * Intensity^0.584 * Concentration^−0.230 * Dosage^0.425 * pH^0.336.

1. Introduction

The mechanism of photocatalysis using a semiconductor is by charge carrier generation resulting in the formation of holes, charge carrier trapping to form hydroxyl radicals, and recombination of electrons and holes where heat is generated.

Heterogeneous photocatalytic systems based on TiO₂ catalysts show some limitations that reduce their impact in the domain of environmental protection. Important limitations are low photonic yield and little efficiency under visible light. These limitations have recently been the source of great development in the area of the production and characterization of TiO₂-based photocatalysts, capable of being efficiently used under visible irradiation or showing a higher photochemical yield in the near UV region.

Any semiconductor material could be activated using a light whose wavelength greatly depends on the band gap of the semiconductor catalyst. Apart from the band gap, there have been other properties like surface area, crystal composition, particle size distribution, and porosity which have an influential effect on the degradation of the compound. Band gap reduction could be done by dye sensitization, doping, bimetallic semiconductor, and surface modification. By reducing the band gap, use of visible light could be employed as an alternative to UV light which may result in better economics. Various nonmetal elements, such as B [1], C [2], N [3], V [4], and S [5], have been successfully doped into TiO₂ nanomaterials. Surface area, crystal composition, and particle size distribution can be varied by varying the preparation methods like preparation using solgel method wherein uniform crystal structure with better properties could be achieved. Several researchers have modified TiO₂ with transition metals. Deposition of noble metals Ag, Au, Pt, and Pd [6, 7] on the surface of TiO₂ enhances the photocatalytic efficiency by acting as an electron trap, promoting interfacial charge transfer and therefore delaying recombination of the electron-hole pair. Another technique involves TiO₂ doping with transition metals such as Fe, Cu, Co, Ni, Cr, V, Mn, Mo, Nb, W, Ru, Pt, and Au [8, 9]. The incorporation of transition metals in the titania crystal lattice may result in the formation of new energy levels between valence band and conduction band, inducing a shift of light absorption towards the visible light region. Photocatalytic activity depends on the nature and the amount of doping agent. Possible limitations are photocorrosion and promoted charge recombination at metal sites. Choi et al. [10] has made an extensive study by doping with Fe³⁺, Mo⁵⁺, Ru³⁺, Os³⁺, Re⁵⁺, V⁴⁺, and Rh³⁺ and concluded that there was an increase in the photoreactivity for both oxidation and reduction of the organic compound.

Cerium, among the lanthanides, has a band gap of ~3 eV. Hence, it has strong absorption and shows better optical properties. Ce (III) and Ce (IV) have the high oxygen storage capacity which enhances the catalytic potential, also its oxidation ability of Ce³⁺ to Ce⁴⁺ states leads to high oxygen mobility resulting in better catalytic performance [11, 12]. It has also been demonstrated by many researchers that there are many advantages because of Cerium doping [13]. Chen et al. [14] and Liu et al. [15] have also established that there was a shift towards visible region due to doping of titania with Cerium.

Nitrobenzene, an aromatic compound used in the manufacture of aniline, has moderate to low water solubility. This nitroaromatic compound has been listed as a carcinogen by the National Institute of Environmental Health Sciences. The maximum permissible limit for Nitrobenzene in drinking water is 17 ppm as recommended by the US EPA. Nitrobenzene has been widely used as solvent and in manufacture of dye intermediates and pesticides. Due to its carcinogenic and mutagenic properties, it has to be eliminated from the water streams. Prolonged exposure causes damage to lung by irritation, anaemia, and liver damage. A number of workers illustrate the removal or degradation of this compound by different biological methods like bioaugmentation and oxidative reduction by bioremediation. Works has been carried out on the degradation of nitrobenzene using white root fungus and glow discharge plasma. Owing to the disadvantages of these procedures due to noneconomical degradation time and complicated equipment designs leading to increased cost, there has been extensive research in identifying techniques which would show better performance. One such technique found to be effective over the years is the use of advanced oxidation process, photocatalysis. Authors like Tayade et al. [6], Priya and Madras [7], and Bhatkhande et al. [16] have worked on the degradation of Nitrobenzene using semiconductor catalysts and an artificial light source.

The main objectives of the present research work are (i) synthesis and characterization of TiO₂ doped with Cerium photocatalysts, (ii) photocatalytic degradation of Nitrobenzene pollutant in aqueous suspensions using the doped catalyst and undoped catalyst under visible light, (iii) optimization of operational parameters, and (iv) detailed kinetic study using Langmuir Hinshelwood model.

2. Experimental Procedures

2.1. Chemical Reagents and Apparatus

All chemicals used in this experiment were of analytical grade. Titanium isopropoxide, Titanium dioxide, Cerium oxide, ethanol, and glacial acetic acid are supplied by SRL chemicals, Mumbai, India. In all the experiments double distilled water was used.

2.2. Catalyst Characterization

X-ray diffraction (XRD) (Siemens D5000) was performed on fresh synthesized catalyst. The X-ray powder diffraction pattern of the powder sample was measured employing CuKα radiation. The data were collected over diffraction angle of 5° to 80° in with a step scanning. The accelerating voltage and the applied current were 40 kV and 40 mA, respectively.

The surface chemical analysis of the samples was made by X-ray Photoelectron Spectroscopy (AXIS His; Kratos Analytical) using MgKα X-ray source () and an analyzer pass energy of 40 eV. The physical adsorption of nitrogen was performed on a NOVA 1000 system (Quantachrome) at 77 K. Surface areas of the samples were calculated based on the BET model.

The DRS spectra of all the samples were recorded to determine the sample’s UV-VIS light absorption capacity, on a Jasco-V650 diode array, computer controlled (with SpectraManager software) spectrophotometer equipped with an ILV-724 integration sphere. The recorded spectral data was acquired in the 220–800 nm range, with 0.5 nm data pitch and 100 nm/min scan speed. When higher resolution of the spectra was needed (usually in the 400–525 nm) the data pitch was changed to 0.05 nm and the scan speed to 50 nm/min.

SEM-EDX analysis was performed to evaluate the morphology of the amorphous starting material and the obtained well crystallized catalysts on a Hitachi S-4700 Type II cold field emission scanning electron microscope equipped with a Röntec QX2-EDS spectrometer.

2.3. Photoreactor

The experiments were performed in an annular photoreactor with a separate immersion well for the visible lamp. The lamps were cooled using circulating water. The reactor was of 500 mL capacity. The samples were taken at known intervals of time and absorbance was measured using UV-spectrophotometer.

2.4. Preparation of Catalyst

Titanium dioxide was prepared by solgel method using Titanium isopropoxide as precursor. Titanium dioxide sol was prepared using Titanium isopropoxide as precursor. 8 mL of Titanium isopropoxide was mixed with 42 mL of ethanol and stirred well. To this 100 mL of 50% ethanol was added slowly and continuously stirred for 30 min at a temperature of 80°C for the hydrolysis reaction to take place, a method modified and adopted from Saif and Abdel-Mottaleb [17]. A modified method was adopted for Cerium sol preparation from Alouche [18]. 65 g of Cerium nitrate was dissolved in 1 L of glacial acetic acid. This solution was added to 1 L of 10% ammonia. This is the sol of Cerium. This sol was then added to TiO₂ sol and stirred uniformly and continuously. It was then left for ageing for 24 hours and then calcined at 400°C for 4 hours. This catalyst is referred to as TiO₂-Ce.

2.5. Degradation Experiment

The batch degradation experiment was performed in an annular photoreactor by taking a known quantity of catalyst to aqueous solution of concentrations ranging between 25 and 200 mg L⁻¹. Visible light of 150 W, 300 W, and 500 W was used for degradation and the solution was irradiated for 7 hours. Samples were collected at different intervals of time and the solution was analysed for concentration of nitrobenzene by reading the absorbance at 264.5 nm in an UV spectrophotometer. The percentage degradation was the reduction in concentration compared to the original concentration as given in where is the initial concentration of the aqueous solution and is the concentration at any time . The unknown concentration of the solution at any time can be predicted from the standard plot of absorbance and concentration of the solution.

3. Results and Discussion

3.1. Catalyst Characterization

XRD patterns were recorded for the prepared and calcined samples on a graphite crystal monochromator, operating with a Cu anode and a sealed X-ray tube as shown in Figure 1. For the range of 20–80° with 0.05° step size, the scans were recorded at several resolutions using CuK_α radiation of wavelength 1.54 Å. Average particle size was determined by using full width at half maximum (FWHM) data. Scherer’s formula (2) was used to determine average particle size as follows: where is the diameter of the particle, is a constant equal to 0.89, is the X-ray wavelength equal to 0.154 nm, is the full width at half maximum, and is the half diffraction angle [4]. The XRD pattern of solgel-TiO₂ showed primary anatase peaks at 25.06°, 47.54°, 54.46°, and 61.72°. The rutile phase of solgel-TiO₂ was indicated by the peaks 37.4° and 53.63°. Titanium dioxide in the anatase form is generally accepted to be the most active polymorph [19]. This better efficiency is attributed to a higher degree of hydroxylation of anatase when compared with that of the rutile phase. The XRD patterns of Ce doped TiO₂ samples almost coincide with those of pure solgel-TiO₂ but show diffraction peaks due to cerium doping. The average particle sizes of solgel-TiO₂ and TiO₂-Ce were calculated and tabulated in Table 1.

The particle size was also calculated using surface area calculated from BET isotherms determined using BET Quantachrome instruments as given in (3). The surface area, average pore area, and particle size calculated are shown in Table 1. Consider the following: where is the surface area (cm² g⁻¹) and is the density of the catalyst which is approximately 4.2 gc m⁻³ for titania based particles. The ionic radii of Ce³⁺ and Ti²⁺ are 0.101 nm and 0.068 nm, respectively. Ce³⁺ could not be incorporated into the lattice of TiO₂ and hence there was an increase in particle size. As the particle size increases, the surface area decreases as seen from Table 1.

The valence state of Cerium in the TiO₂-Ce sample was examined by XPS. The XP spectrum in Figure 2 shows the characteristic Ce 3d peak that has a binding energy of 887.3 eV; XPS peaks corresponding to Ce⁴⁺ ion were not found. This result confirms the presence of Cerium deposits on the TiO₂ surface of the TiO₂-Ce sample. The binding energies for Ti 2p were 458.3 eV and 464.1 eV as shown in Figure 2. Combined with the XRD analysis, it could be understood that the doping cerium atoms presented in the forms of Ce₂O₃ and were distributed on the surface of titania.

(a)

(b)

Figure 3 shows SEM photograph of the typical samples of TiO₂ (a) and TiO₂-Ce (b). From the image, the sample TiO₂-Ce existed approximately in the form of spherical particle and presented porous structures similar to those of TiO₂. According to the statistical estimation, the average size was about 14.5 nm, which was in accordance with the value determined by XRD (19.14 nm). The morphological study shows that for both TiO₂ and TiO₂-Ce catalyst, the surface looked almost the same with slightly whitish portion indicating the deposition of Ce. On the basis of the SEM results, the Ti Ka-fluorescence signals for the pure TiO₂ and TiO₂-Ce samples were also obtained by EDX analysis and the spectra are shown in Figure 4, which gave both qualitative and quantitative information about the elemental and atomic percentages in the TiO₂ and TiO₂-Ce samples, as presented in Table 2.

(a)

(b)

In order to estimate the band gap distance, UV-vis spectroscopy was employed. An Oriel Instruments spectrometer with an integrating sphere was used for UV-Vis spectrometry measurements to analyze the red-shifts in the absorption regions. The UV-Vis transmittance measurements were taken and converted into absorption readings as given in Figure 5. For pure TiO₂, the band gap energy correpsonding to 388.8 nm indicates 3.18 eV which was found to be in accordance with that of other researchers [20–22], while for TiO₂-Ce, the band gap energy reduced due to the shift of absorbance further away from UV region. The band gap energy corresponding to the wavelength of 551.4 nm was determined to be 2.25 eV. The results show that cerium does improve visible light absorbance of TiO₂ due to cerium plasmon absorption.

3.2. Control Experiment

Photocatalytic degradation studies were performed using TiO₂-Ce and compared with undoped TiO₂. The catalyst dosage was uniformly taken to be 0.1 g L⁻¹ for all the experiments with solution concentration to be 50 mg L⁻¹, pH of 6.8, and different light intensities (150, 300, and 500 W). From Figure 6, it could be seen that using TiO₂-Ce and 500 W light, the degradation achieved was 79.09% which was higher than the other catalysts studied. Addition of Cerium to TiO₂ has increased the percentage of degradation by 14% when compared to TiO₂. The photolytic degradation of nitrobenzene was performed in the absence of the catalyst varying the intensity of the visible light for comparing the performance of cerium doped catalyst as shown in Figure 6. The degradation using 150, 300, and 500 W was found to be 23, 25, and 29%, respectively. This was much lower than the degradation using Cerium doped catalyst.

Though the particle size of TiO₂-Ce was higher than TiO₂ (solgel), it showed better degradation because, in photocatalysis, doping a semiconductor changed the photocatalytic process by suppressing electron-hole recombination and when the electron formed due to excitation migrates to the metal, it gets trapped within. The organic compound diffuses to the free hole on the semiconductor surface and oxidation of nitrobenzene occurs. The presence of cerium species on TiO₂ influences the photoreactivity by altering the electron-hole pair recombination rate through the following equations (4)–(7). The reduction in band gap energy from 3.2 eV to 2.25 eV also contributed to this increase in degradation. Consider

The present study revealed that the cerium doped TiO₂ in sol-sol method could be effectively used as compared to other catalysts as discussed in Table 3. Better shift of the catalyst towards visible region has resulted in 100% degradation at a pH of 9 and catalyst dosage of 0.1 gL⁻¹ (as summarized in Section 3.3.5).

The TOC removal % was studied for different intervals of time. The photomineralization of the compounds were measured using Total Organic Carbon analyzer (Shimadzu TOC 5000 A). The extent of TOC removal % was compared with the undoped and Cerium doped TiO₂ catalyst. The TOC removal % was maximum using Cerium doped catalyst at an intensity of 500 W.

3.3. Optimization of Operational Parameters

3.3.1. Effect of Solution Concentration

The most important operational parameter to be studied is the influence of initial concentration of the solution. NB photocatalytic degradation studies were carried out using 25–200 mg L⁻¹ initial concentration of NB and 0.1 g L⁻¹ of catalyst loading. The plot of degradation % for different solution concentration was made and from Figure 7 it could be inferred that as concentration increased, percentage degradation decreased. This may be due to the fact that with the increase in initial concentration of NB, while the irradiation period and catalyst dose are kept constant, more NB molecules are present on the surface of TiO₂. Thus, an increase in the number of substrate ions accommodating in interlayer spacing inhibits the action of the catalyst, which thereby decreases the number of reactive ^•OH and O₂^•− free radicals attacking the NB molecules, and, hence, lowers the photodegradation efficiency [23].

3.3.2. Effect of Light Intensity

The influence of light intensity on the degradation efficiency has been examined at constant Nitrobenzene concentration (50 mg L⁻¹), at pH (6.5) and catalyst loading (0.1 g L⁻¹). It is evident that the degradation rate increases with increase in the light intensity as shown in Figure 6. The photons required for the electron transfer were generated by UV irradiation which results in electron transfer from valence band to conduction band of the catalyst. The degradation % increases when more radiations fall on the catalyst surface and hence more hydroxyl radicals are produced [24].

3.3.3. Effect of Catalyst Dosage

Photocatalyst dosage added to the reaction vessel is a major parameter affecting the photocatalytic degradation efficiency. The aqueous solution of 50 mg L⁻¹ of solution was degraded using different catalyst dosages (0.025, 0.05, 0.1, 0.15, and 0.2 g L⁻¹). From Figure 8 it can be seen that maximum degradation was achieved for the catalyst dosage of 0.1 g L⁻¹. It could also be inferred that further increase in catalyst dosage did not yield an increase in degradation percentage.

The increase in degradation percentage for 0.025 to 0.1 g L⁻¹ may be due to an increase in the amount of active sites on the surface of the photocatalyst particles. The number of NB molecules adsorbed as well as the number of photons absorbed increase with the increase in catalyst concentration thereby enhancing the rate of degradation. Addition of catalyst beyond 0.1 g L⁻¹ leads to decrease in the degradation. Aggregation of TiO₂ particles occurs at higher dosage causing decrease in the number of surface active sites and also there is an increase in the opacity of the solution and light scattering of TiO₂ particles at high dosage through the solution [25].

3.3.4. Effect of pH of the Solution

pH of the solution greatly influences the degradation rate. It tends to change the surface property of the catalyst. The effect of change in initial pH (2, 4, 6.5, 8, 9, 10, and 11) of 50 mg L⁻¹ of the nitrobenzene solution was studied by adding 0.1 g L⁻¹ of catalyst. The plot of % degradation against pH (Figure 9) showed that as pH increased the degradation increased. A maximum of 100% degradation was achieved at pH 9. The degradation was lower in lower acidic and higher alkaline pH.

pH of the catalyst dispersions majorly affects the surface properties on the particles, agglomerate size formed, and the conductance and valence bands positions [26]. The nitrobenzene solution was degraded by hydroxyl attack and direct oxidation at the holes and reduction at the conduction band. In alkaline pH, the surface of TiO₂-Ce acquires a negative charge leading to greater adsorption and hence increasing the degradation rate in the alkaline media.

3.3.5. Kinetic Modelling Using Langmuir Hinshelwood Model

The degradation percentage was calculated and for heterogeneous catalyst, the Langmuir Hinshelwood model was used to calculate the apparent rate constant. The Langmuir Hinshelwood model, derived based on the monolayer activity assumption, was used to estimate the kinetic parameters in terms of reaction rate constant () and Langmuir Hinshelwood adsorption constant () which is as given in where is rate of disappearance of organic substrate, mg L⁻¹min⁻¹, and is concentration of organic substrate, mg L⁻¹,

Linearization of (8) yields an equation from which a plot of ln () against time will result in a linear relationship resulting in zero intercept and apparent rate constant () derived from the slope of the line. Figure 10 is the representation of the plot from which the apparent rate constant was determined using slope of the line. Similarly for all the conditions of pH (2–11), concentration (25–200 mg L⁻¹), catalyst dosage (0.025–0.2 g L⁻¹), and intensity of visible light (150–500 W), the plot of ln () against time was evaluated. The apparent rate constant was found to increase with light intensity and decrease with solution concentration. The maximum degradation could be achieved at the following parameter condition: pH: 9, dosage: 0.1 g L⁻¹, solution concentration: 25 mg L⁻¹, and light intensity: 500 W. The nonlinear fit between the apparent rate constant and the operational parameters was determined and were found that the experimental values when compared with the theoretical values as in Figure 11, the theoretical values had less than 3% error and hence the following equation (10) could be chosen for approximating the experimental conditions. Equation (10) could be used for a condition of pH 2 to 9, dosage of 0.05 to 0.1 g L⁻¹, light intensity of 150, 300, or 500 W, and concentration of solution from 25 to 200 mg L⁻¹. The nonlinear equation was

4. Conclusion

The undoped and cerium doped titania photocatalyst was prepared through the sol-gel route. The cerium doped photocatalyst could absorb the visible light and showed high photoactivity in the visible region because of the band gap narrowing. Cerium atoms existed in the state of Ce₂O₃ and were dispersed on the surface of titania, suppressing the recombination of electron-hole pairs and increasing the photoactivity as confirmed using XPS and DRIFT analysis. The average crystal size and the surface area were determined and compared between two types of catalysts. The operational parameters were optimized and the following condition was suggested to obtain maximum degradation: pH: 9, dosage: 0.1 g L⁻¹, solution concentration: 25 mg L⁻¹, and light intensity: 500 W. The kinetic study revealed that the degradation followed Langmuir Hinshelwood model. The apparent rate constant was determined and evaluated theoretically using the nonlinear fit which depends on the operational parameters. Based on the previously mentioned experiments and characterization it could be concluded that Cerium doped TiO₂ catalyst prepared by solgel method could be efficiently used for degradation of Nitrobenzene using visible light.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

References

S. C. Moon, H. Mametsuka, S. Tabata, and E. Suzuki, “Photocatalytic production of hydrogen from water using TiO₂ and B/TiO₂,” Catalysis Today, vol. 58, no. 2, pp. 125–132, 2000.
View at: Publisher Site | Google Scholar
C. Lettmann, K. Hildenbrand, H. Kisch, W. Macyk, and W. F. Maier, “Visible light photodegradation of 4-chlorophenol with a coke-containing titanium dioxide photocatalyst,” Applied Catalysis B, vol. 32, no. 4, pp. 215–227, 2001.
View at: Publisher Site | Google Scholar
R. Asahi, T. Morikawa, T. Ohwaki, K. Aoki, and Y. Taga, “Visible-light photocatalysis in nitrogen-doped titanium oxides,” Science, vol. 293, no. 5528, pp. 269–271, 2001.
View at: Publisher Site | Google Scholar
C.-S. Wu and C. Chen, “A visible-light response vanadium-doped titania nanocatalyst by sol-gel method,” Journal of Photochemistry and Photobiology A, vol. 163, no. 3, pp. 509–515, 2004.
View at: Publisher Site | Google Scholar
T. Umebayashi, T. Yamaki, S. Tanaka, and K. Asai, “Visible light-induced degradation of methylene blue on S-doped TiO₂,” Chemistry Letters, vol. 32, no. 4, pp. 330–331, 2003.
View at: Google Scholar
R. J. Tayade, R. G. Kulkarni, and R. V. Jasra, “Photocatalytic degradation of aqueous nitrobenzene by nanocrystalline TiO₂,” Industrial and Engineering Chemistry Research, vol. 45, no. 3, pp. 922–927, 2006.
View at: Publisher Site | Google Scholar
M. H. Priya and G. Madras, “Photocatalytic degradation of nitrobenzenes with combustion synthesized nano-TiO₂,” Journal of Photochemistry and Photobiology A, vol. 178, no. 1, pp. 1–7, 2006.
View at: Publisher Site | Google Scholar
S. Ikeda, N. Sugiyama, B. Pal et al., “Photocatalytic activity of transition-metal-loaded titanium(IV) oxide powders suspended in aqueous solutions: correlation with electron-hole recombination kinetics,” Physical Chemistry Chemical Physics, vol. 3, no. 2, pp. 267–273, 2001.
View at: Publisher Site | Google Scholar
A. Fuerte, M. D. Hernández-Alonso, A. J. Maira et al., “Visible light-activated nanosized doped-TiO₂ photocatalysts,” Chemical Communications, no. 24, pp. 2718–2719, 2001.
View at: Google Scholar
W. Choi, A. Termin, and M. R. Hoffmann, “The role of metal ion dopants in quantum-sized TiO₂: correlation between photoreactivity and charge carrier recombination dynamics,” Journal of Physical Chemistry, vol. 98, no. 51, pp. 13669–13679, 1994.
View at: Google Scholar
B. M. Reddy, P. M. Sreekanth, Y. Yamada, Q. Xu, and T. Kobayashi, “Surface characterization of sulfate, molybdate, and tungstate promoted TiO₂-ZrO₂ solid acid catalysts by XPS and other techniques,” Applied Catalysis A, vol. 228, no. 1-2, pp. 269–278, 2002.
View at: Publisher Site | Google Scholar
V. M. Orera, R. I. Merino, and F. Peña, “Ce3+↔Ce4+ conversion in ceria-doped zirconia single crystals induced by oxido-reduction treatments,” Solid State Ionics, vol. 72, no. 2, pp. 224–231, 1994.
View at: Google Scholar
W. M. Yen, M. Raukas, S. A. Basun, W. Van Schaik, and U. Happek, “Optical and photoconductive properties of cerium-doped crystalline solids,” Journal of Luminescence, vol. 69, no. 5-6, pp. 287–294, 1996.
View at: Google Scholar
S. W. Chen, J. M. Lee, K. T. Lu et al., “Band-gap narrowing of TiO₂ doped with Ce probed with x-ray absorption spectroscopy,” Applied Physics Letters, vol. 97, no. 1, Article ID 012104, 2010.
View at: Publisher Site | Google Scholar
H. Liu, X. Z. Li, Y. J. Leng, and W. Z. Li, “An alternative approach to ascertain the rate-determining steps of TiO₂ photoelectrocatalytic reaction by electrochemical impedance spectroscopy,” Journal of Physical Chemistry B, vol. 107, no. 34, pp. 8988–8996, 2003.
View at: Google Scholar
D. S. Bhatkhande, V. G. Pangarkar, and A. A. C. M. Beenackers, “Photocatalytic degradation of nitrobenzene using titanium dioxide and concentrated solar radiation: chemical effects and scaleup,” Water Research, vol. 37, no. 6, pp. 1223–1230, 2003.
View at: Publisher Site | Google Scholar
M. Saif and M. S. A. Abdel-Mottaleb, “Titanium dioxide nanomaterial doped with trivalent lanthanide ions of Tb, Eu and Sm: preparation, characterization and potential applications,” Inorganica Chimica Acta, vol. 360, no. 9, pp. 2863–2874, 2007.
View at: Publisher Site | Google Scholar
A. Alouche, “Preparation and characterization of Copper and/or Cerium catalysts supported on Alumina or Ceria,” Jordan Journal of Mechanical and Industrial Engineering, vol. 2, pp. 111–116, 2008.
View at: Google Scholar
R. J. Tayade, P. K. Surolia, R. G. Kulkarni, and R. V. Jasra, “Photocatalytic degradation of dyes and organic contaminants in water using nanocrystalline anatase and rutile TiO₂,” Science and Technology of Advanced Materials, vol. 8, no. 6, pp. 455–462, 2007.
View at: Publisher Site | Google Scholar
X.-Z. Shen, Z.-C. Liu, S.-M. Xie, and J. Guo, “Degradation of nitrobenzene using titania photocatalyst co-doped with nitrogen and cerium under visible light illumination,” Journal of Hazardous Materials, vol. 162, no. 2-3, pp. 1193–1198, 2009.
View at: Publisher Site | Google Scholar
W. Wang, Y. Huang, and S. Yang, “Photocatalytic degradation of nitrobenzene wastewater with H₃PW₁₂O₄₀/TiO₂,” in Proceedings of the International Conference on Mechanic Automation and Control Engineering (MACE '10), pp. 1303–1305, June 2010.
View at: Publisher Site | Google Scholar
P. K. Surolia, R. J. Tayade, and R. V. Jasra, “Photocatalytic degradation of nitrobenzene in an aqueous system by transition-metal-exchanged ETS-10 zeolites,” Industrial and Engineering Chemistry Research, vol. 49, no. 8, pp. 3961–3966, 2010.
View at: Publisher Site | Google Scholar
W. Bahnemann, M. Muneer, and M. M. Haque, “Titanium dioxide-mediated photocatalysed degradation of few selected organic pollutants in aqueous suspensions,” Catalysis Today, vol. 124, no. 3-4, pp. 133–148, 2007.
View at: Publisher Site | Google Scholar
A. E. Cassano and O. M. Alfano, “Reaction engineering of suspended solid heterogeneous photocatalytic reactors,” Catalysis Today, vol. 58, no. 2, pp. 167–197, 2000.
View at: Publisher Site | Google Scholar
A. A. Adesina, “Industrial exploitation of photocatalysis: progress, perspectives and prospects,” Catalysis Surveys from Asia, vol. 8, no. 4, pp. 265–273, 2004.
View at: Publisher Site | Google Scholar
Y. Ku and C. B. Hsieh, “Photocatalytic decomposition of 2,4-dichlorophenol in aqueous TiO₂ suspensions,” Water Research, vol. 26, no. 11, pp. 1451–1456, 1992.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Padmini Ellappan and Lima Rose Miranda. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3711

Downloads

1644

Citations