Copolymers Formation by Photopolymerization of (Meth)acrylates Containing Dissolved Polyheteroarylenes

Table 1

The rate constants of MMA and EA photopolymerisation in the presence of Diimide, PI 1, and PI 2 determined by DSPC.

Monomer

Added compound

Parameter

—

Diimide, wt%

PI 1, wt%

PI 2, wt%

at T, ^˚C

5

10

20

42

5

10

5

10

20

42

MMA

k, min^−1

30

0.68±0.03

0.53±0.04

0.52±0.02

0.56±0.07

0.39±0.04

0.72±0.00

0.72±0.14

0.45±0.02

0.42±0.01

0.45±0.07

0.28±0.02

40

0.80±0.01

0.72±0.01

0.61±0.02

0.65±0.10

0.54±0.07

0.75±0.02

0.72±0.16

0.52±0.09

0.44±0.05

0.53±0.05

0.28±0.01

50

0.81±0.01

0.71±0.11

0.53±0.10

0.58±0.00

0.45±0.01

0.79±0.07

0.89±0.20

0.59±0.11

0.47±0.08

0.52±0.07

0.27±0.06

60

0.83±0.14

0.84±0.01

0.68±0.12

0.74±0.04

0.50±0.05

0.78±0.06

0.73±0.05

0.48±0.09

0.45±0.02

0.58±0.07

0.41±0.08

70

1.02±0.03

0.65±0.02

0.67±0.08

0.56±0.02

0.45±0.02

0.98±0.12

0.74±0.02

0.62±0.05

0.61±0.00

0.60±0.08

0.47±0.02

EA

k, min^-1

30

1.61±0.34

1.23±0.20

1.71±0.03

2.04±0.21

1.88±0.33

1.62±0.07

1.67±0.14

1.24±0.13

0.97±0.10

0.84±0.02

1.36±0.08

40

1.69±0.40

1.27±0.32

1.77±0.06

1.94±0.29

1.77±0.16

1.69±0.03

1.64±0.02

1.10±0.08

0.95±0.01

0.88±0.05

1.43±0.49

50

1.98±0.09

1.36±0.36

1.90±0.15

2.21±0.06

1.84±0.06

1.75±0.09

1.77±0.43

1.24±0.21

1.07±0.05

0.84±0.01

1.51±0.17

60

1.84±0.01

1.40±0.07

2.08±0.07

2.16±0.09

1.86±0.25

1.69±0.04

1.64±0.24

1.41±0.08

1.21±0.14

0.99±0.08

1.41±0.15

70

2.31±0.08

1.58±0.35

2.17±0.14

2.27±0.17

2.14±0.14

1.98±0.18

1.73±0.39

1.58±0.28

1.22±0.03

1.08±0.08

1.40±0.20