Copolymers Formation by Photopolymerization of (Meth)acrylates Containing Dissolved Polyheteroarylenes
Table 5
SEC results of polymers based on MMA and EA.
| Sample | Mn × 10-3 | Mw × 10-3 | Mw/Mn |
| PMMA* | 12.6 | 27.8 | 2.2 | MMA + 20 wt.% Diimide | 21.9 | 49.4 | 2.3 | MMA + 10 wt.% PI 1 | 28.6 | 96.7 | 3.4 | MMA + 20 wt.% PI 2 | 31.6 | 75.7 | 2.4 | MMA + 5 wt.% PAr | 16.0 | 34.6 | 2.2 | PEA* | 39.7 | 107.6 | 2.7 | EA + 11 wt.% Diimide | 56.2 | 143.1 | 2.6 | EA + 42 wt.% Diimide | 62.6 | 138.4 | 2.2 | EA + 5 wt.% PI 1 | 86.9 | 348.4 | 4.0 | EA + 11 wt.% PI 1 | 70.3 | 252.2 | 3.6 | EA + 5 wt.% PI 2 | 50.9 | 269.2 | 5.3 | EA + 11 wt.% PI 2 | 24.9 | 200.6 | 8.1 | EA + 20 wt.% PI 2 | 42.6 | 300.1 | 7.0 | EA + 42 wt.% PI 2 | 55.1 | 300.2 | 5.5 |
| PI 1* | 186.7 | 345.5 | 1.9 | PI 2* | 31.5 | 54.0 | 1.7 | PAr* | 54.5 | 99.9 | 1.8 |
|
|
For the comparison.
|