International Journal of Polymer Science / 2011 / Article / Tab 2 / Research Article
Investigation of the Effects of Titanate as Coupling Agent and Some Inorganic Nanoparticles as Fillers on Mechanical Properties and Morphology of Soft PVC Table 2 Mechanical properties of prepared composites.
Formulation: PVC resin (
)—Plasticizer (DOP)—Filler (CaCO3 ) Property Modulus, psi % Elongation at break Tensile strength, psi Energy, J Control 6.3 92.2 5.8 1175 C1 8.9 88.9 7 1548 C2 9.8 86.5 7.6 1698 C3 11.3 82 9.26 2003 C4 12.7 79 10.3 2240 C5 14.4 76.5 11 2457 C6 14.8 63 9.32 1590 Formulation: PVC resin (
)—Plasticizer (DOP)—Filler (TiO2 ) Property Modulus, psi % Elongation at break Tensile strength, psi Energy, J Control 6.3 92.2 5.8 1175 T1 7.25 87.9 6.37 1448 T2 7.67 81.2 6.22 1450 T3 10.4 78.01 8.1 1820 T4 11.2 74.86 8.37 1853 T5 11.4 70.8 8.12 1515 T6 12.38 70.4 8.71 1435 Formulatuon: PVC resin (
)—Plasticizer (DOP)—Filler (ZnO) Property Modulus, psi % Elongation at break Tensile strength, psi Energy, J Control 6.3 92.2 5.8 1175 Z1 9.6 69.9 6.71 1032 Z2 10.7 65.4 7.05 1029 Z3 11.37 65.07 7.39 1035 Z4 13.27 62.6 8.31 1436 Z5 13.31 62.4 8.31 1427 Z6 13.86 43.16 5.98 528