Research Article
Influence of Carbon Black Structure and Specific Surface Area on the Mechanical and Dielectric Properties of Filled Rubber Composites
Table 4
Mechanical properties of the investigated vulcanizates.
| | NR1 | NR2 | NR3 | NR4 | NR5 | NR6 | NR7 | NR8 |
| M100, MPa | 0.8 | 1.2 | 1.2 | 1.4 | 2.1 | 3.5 | 2.6 | 3.8 | M300, MPa | 2.7 | 3.2 | 4.5 | 4.8 | 8.3 | 12.2 | 9.3 | 10.8 | Tensile strength, MPa | 17.7 | 18.5 | 15.2 | 16.5 | 16.1 | 15.5 | 18.5 | 19.2 | Elongation at break, % | 740 | 680 | 530 | 520 | 500 | 440 | 650 | 550 | Residual elongation, % | 15 | 15 | 10 | 10 | 10 | 10 | 10 | 10 | Shore A hardness | 50 | 52 | 53 | 56 | 61 | 67 | 60 | 65 |
|
|