Characterization and Some Insights into the Reaction Chemistry of Polymethylsilsesquioxane or Methyl Silicone Resins
Table 4
QR-ES-Metflex GC quantification summary.
| Composition | Number | FW w/o cap | FW w/cap | PMSQ-1 wt% w/o cap | PMSQ-NA wt% w/o cap | PMSQ-QC Si mol% w/o cap |
| T0 | a | 94 | 310 | — | — | 0.02 | | b | 402 | 402 | — | 0.18 | 0 | | c | 228 | 444 | — | — | 0.01 | | d | 170 | 454 | — | — | 0.03 | | e | 478 | 550 | 0.37 | 1.12 | 0.32 | | f | 478 | 550 | — | 0.09 | 0.07 | | g | 478 | 550 | 0.81 | 2.13 | 0.48 | | h | 420 | 564 | — | 1.64 | 0.55 | | j | 420 | 564 | — | 1.92 | 1.80 | | k | 536 | 536 | 0.11 | — | — | | l | 362 | 578 | — | — | 0.28 | | m | 344 | 416 | — | — | 0.33 | | n | 362 | 578 | — | — | 0.25 | | o | 304 | 592 | — | — | 0.41 | | p | 362 | 578 | — | — | 0.30 | | q | 304 | 592 | — | — | 0.36 | | r | 362 | 578 | — | 0.31 | 0.87 | | s | 362 | 578 | — | — | 0.20 | | t | 478 | 550 | 0.13 | trace? | — | | u | 478 | 550 | 0.07 | trace? | — | | v | 612 | 684 | 1.20 | 0.47 | 0.12 | | w | 554 | 698 | 0.41 | 0.38 | 0.32 | | x | 554 | 698 | 1.37 | 1.28 | 0.35 | | y | 554 | 698 | — | 0.35 | 0.20 | | z | 554 | 698 | 1.33 | 1.19 | 0.31 | | a2 | 612 | 684 | 0.26 | 0.22 | 0.13 | | b2 | 554 | 698 | — | — | 0.11 | | c2 | 612 | 684 | — | 0.22 | 0.13 | | d2 | 612 | 684 | — | 0.21 | 0.11 | | e2 | 554 | 698 | 0.12 | 0.65 | 0.31 | | f2 | 670 | 670 | 0.12 | — | — | | g2 | 496 | 712 | 0.17 | 0.79 | 0.60 | | h2 | 496 | 712 | 0.37 | 1.19 | 0.75 | | i2 | 496 | 712 | — | 0.25 | 0.23 | | j2 | 496 | 712 | 0.26 | 0.94 | 0.44 | | k2 | 496 | 712 | — | — | 0.20 | | l2 | 496 | 712 | 0.52 | 2.22 | 1.11 | | m2 | 438 | 726 | — | 0.82 | 1.67 | | n2 | 438 | 726 | — | 0.51 | 1.24 | | o2 | 438 | 726 | — | 0.29 | 0.66 | | p2 | 438 | 726 | — | 0.17 | 0.44 | | q2 | 380 | 740 | — | — | 0.29 | | r2 | 380 | 740 | — | — | 0.20 | | s2 | 688 | 832 | 0.08 | — | — | | t2 | 688 | 832 | 0.18 | — | — |
| Total | | | | 7.87 | 19.57 | 16.36 |
|
|