Morphology and Properties of Nylon 6 Blown Films Reinforced with Different Weight Percentage of Nanoclay Additives

<table class="table-group" id="tab4"><tr><td><table class="table"><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr class="thead"><td align="left">Sample</td><td align="center">Peak force (gms)</td><td align="center">Peak elongation (%)</td><td align="center">Modulus (GPa)</td></tr><tr><td class="thead-hr" colspan="4"><hr/></td></tr><tr><td align="left">CN6F</td><td align="center">6155</td><td align="center">323</td><td align="center">2.0</td></tr><tr><td align="left">N6CF2</td><td align="center">7879</td><td align="center">230</td><td align="center">2.4</td></tr><tr><td align="left">N6CF5</td><td align="center">8972</td><td align="center">16</td><td align="center">2.9</td></tr><tr><td align="left">N6CF10</td><td align="center">7539</td><td align="center">14</td><td align="center">2.8</td></tr><tr class="table-tr"><td colspan="4"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Tensile strength results of nylon-6 nanocomposite films.

International Journal of Polymer Science

tab4

Table 4

Table 4: Morphology and Properties of Nylon 6 Blown Films Reinforced with Different Weight Percentage of Nanoclay Additives 