Preparation of Higher Molecular Weight Poly (L-lactic Acid) by Chain Extension
Table 2
DSC data of the PLA prepolymer and the chain-extended PLA.
| Run | (×10−4 g/mol) | Insoluble content (wt%) | (°C) | (°C) | Δ (J/g) | (%) |
| Prepolymer | 2.0 | 0 | 59.0 | 170.3 | 52.9 | 56.8 | 1 | 16.3 | 2.2 | 57.2 | 161.1 | 39.6 | 42.5 | 2 | 12.1 | 3.0 | 57.2 | 164.5 | 41.1 | 44.1 | 3 | 20.3 | 3.6 | 56.6 | 163.5 | 39.4 | 42.3 | 6 | 9.6 | 4.4 | 55.5 | 158.8 | 42.2 | 45.3 | 8 | 10.7 | 3.6 | 56.2 | 163.5 | 43.8 | 47.1 | 9 | 12.5 | 3.8 | 55.8 | 164.1 | 43.5 | 46.7 | 10 | 12.6 | 4.1 | 56.2 | 164.5 | 42.9 | 46.1 |
|
|