Research Article
Preparation and Characterization of Some Hyperbranched Polyesteramides/Montmorillonite Nanocomposites
Table 1
Formation of HPEA1–6/clay nanocomposites at different clay (MMT) percent.
| | Entry | Conditions | (XRD)
nm |
| | M1 | HPEA1-MMT (4%) | 1.935 | | M2 | HPEA1-MMT (10%) | 1.879 | | M3 | HPEA1-MMT (15%) | 1.850 | | M4 | HPEA2-MMT (4%) | 2.143 | | M5 | HPEA2-MMT (10%) | 1.913 | | M6 | HPEA2-MMT (15%) | 1.531 | | M7 | HPEA3-MMT (4%) | 1.384 | | M8 | HPEA3-MMT (10%) | 1.372 | | M9 | HPEA3-MMT (15%) | 1.344 | | M10 | HPEA4-MMT (4%) | 1.856 | | M11 | HPEA4-MMT (10%) | 1.731 | | M12 | HPEA4-MMT (15%) | 1.661 | | M13 | HPEA5-MMT (4%) | 1.865 | | M14 | HPEA5-MMT (10%) | 1.857 | | M15 | HPEA5-MMT (15%) | 1.846 | | M16 | HPEA6-MMT (4%) | Exfoliation | | M17 | HPEA6-MMT (10%) | 1.850 | | M18 | HPEA6-MMT (15%) | 1.840 |
|
|
HPEA1, 3, 5 are DEA-based hyperbranched polymers.
HPEA2, 4, 6 are DIPA-based hyperbranched polymers.
|