Rheological Properties of Hydrophobically Associative Copolymers Prepared in a Mixed Micellar Method Based on Methacryloxyethyl-dimethyl Cetyl Ammonium Chloride as Surfmer

Table 3

Values of the slopes of the storage modulus 𝐺^′ and the loss modulus 𝐺^′′ in the terminal zone and values of the crossing time 𝑡_𝑐 for the polymers.

Polymer	Slope		𝐺𝑐 (Pa)	𝑡𝑐 (s)
	𝐺^′ (Pa)	𝐺^′′ (Pa)
PAM	2.2	0.98	/	<0.01
0.5DM4.5	1.6	1.17	1.51	0.32
0.5DM9.3	1.35	1.05	2.27	0.86
0.5DM12.7	1.27	0.86	2.45	2.85
0.75DM4.6	1.46	1.15	1.79	0.82
0.75DM9.3	1.25	0.93	2.78	1.92
0.75DM12.8	1.32	0.96	3.56	6.25