Research Article
Evaluation of Some Conducting Polymers as Novel Antioxidants for Rubber Vulcanizates
Table 6
SBR Formulations containing prepared P(An-co-T) and PT.
| Formulation no. | 15 | 16 | 17 | 18 | 19 |
| Control (without) | — | — | — | — | — | PN | — | 1 | — | — | — | TMQ | — | — | 1 | — | — | P(An-co-T) | — | — | — | 1 | — | PT | — | — | — | — | 1 |
| Rheometric characteristics at °C | Minimum torque, , dN·m | 2 | 1 | 1 | 1 | 1 | Maximum torque, , dN·m | 70 | 69 | 69.5 | 70 | 72 | Optimum cure time, , min | 13 | 12 | 11 | 12 | 11 |
| Physicomechanical properties at the optimum cure time | Stress at rupture, , MPa | 15.61 | 15.93 | 15.97 | 27.4 | 25.10 | Strain at rupture, , % | 624 | 662 | 651 | 670 | 647 |
|
|
Base recipe (phr): SBR, 100; stearic acid, 2; zinc oxide, 5; HAF, 30; processing oil, 3; CBS, 1; S, 2.
|