Kinetics of Phase Transformation of Indium in the Presence of Polytetrafluoroethylene: Implications for DSC Measurements on Polymers and Their Composites

<div>DSC melting peaks of In in absence (bold and sharp peak) and in the presence of PTFE 0.5 mm thick. The scan rate was 0.167°C s<sup>−1</sup>.</div>