Research Article
Designing of Collagen Based Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) Scaffolds for Tissue Engineering
Table 4
Variables of P(3HB-co-4HB)/collagen blend scaffold fabrication and response.
| Run | Scaffold thickness (mm)
| 4HB molar fraction (mol%)
| Collagen concentration (5 mg/mL)
| Water contact angle (°) |
| 1 | 0.1 | 35 | 10 | 57.2 ± 1.7 | 2 | 0.1 | 50 | 0 | 73.2 ± 1.2 | 3 | 0.2 | 35 | 15 | 51.3 ± 0.9 | 4 | 0.1 | 20 | 5 | 80.1 ± 1.1 | 5 | 0.2 | 20 | 15 | 64.0 ± 1.3 | 6 | 0.2 | 50 | 5 | 68.3 ± 0.5 | 7 | 0.1 | 20 | 15 | 62.3 ± 1.6 | 8 | 0.1 | 20 | 0 | 81.2 ± 1.3 | 9 | 0.2 | 82 | 0 | 53.2 ± 1.0 | 10 | 0.1 | 50 | 5 | 68.9 ± 1.2 | 11 | 0.1 | 50 | 15 | 44.5 ± 1.1 | 12 | 0.1 | 35 | 15 | 52.4 ± 1.3 | 13 | 0.2 | 50 | 15 | 61.3 ± 1.7 | 14 | 0.1 | 82 | 10 | 49.2 ± 1.6 | 15 | 0.2 | 20 | 10 | 74.1 ± 0.8 | 16 | 0.2 | 82 | 15 | 48.1 ± 1.3 | 17 | 0.2 | 50 | 0 | 69.8 ± 1.4 | 18 | 0.2 | 20 | 0 | 79.8 ± 1.1 | 19 | 0.2 | 20 | 5 | 77.5 ± 1.2 | 20 | 0.2 | 82 | 10 | 53.0 ± 1.8 | 21 | 0.1 | 50 | 10 | 64.6 ± 1.3 | 22 | 0.2 | 35 | 5 | 73.3 ± 1.7 | 23 | 0.2 | 35 | 0 | 76.6 ± 0.6 | 24 | 0.2 | 35 | 10 | 64.3 ± 0.9 | 25 | 0.2 | 82 | 5 | 51.9 ± 0.6 | 26 | 0.1 | 35 | 5 | 63.3 ± 1.1 | 27 | 0.1 | 82 | 5 | 55.2 ± 1.3 | 28 | 0.2 | 50 | 10 | 68.7 ± 1.6 | 29 | 0.1 | 82 | 0 | 56.7 ± 1.9 | 30 | 0.1 | 82 | 15 | 45.4 ± 1.3 | 31 | 0.1 | 35 | 0 | 78.4 ± 1.5 | 32 | 0.1 | 20 | 10 | 73.6 ± 1.7 |
|
|