Flexural Properties of PVC/Bamboo Composites under Static and Dynamic-Thermal Conditions: Effects of Composition and Water Absorption
Table 3
DMTA properties of composites.
| Composites | DMTA | (MPa) at temperature (°C) | Peak | | 30 | 50 | 70 | 90 |
| | PVC | 2443 | 2186 | 1543 | 13 | 1.38 | 87 | WS-PVC | 2046 | 1840 | 1285 | 15 | 1.40 | 88 |
| C1 | 75 µm, 25% | 2751 | 2534 | 1940 | 601 | 0.92 | 87 | 75 µm, 50% | 3380 | 3113 | 2342 | 248 | 0.56 | 85 | 1 mm, 25% | 3137 | 2901 | 1905 | 50 | 1.06 | 86 | 1 mm, 50% | 3641 | 3371 | 2592 | 528 | 0.50 | 86 |
| C1 - WS | 75 µm, 25% | 2700 | 2408 | 1847 | 132 | 0.69 | 89 | 75 µm, 50% | 3422 | 3055 | 2429 | 377 | 0.49 | 89 | 1 mm, 25% | 2192 | 1989 | 1572 | 114 | 0.68 | 89 | 1 mm, 50% | 3303 | 2915 | 2394 | 387 | 0.46 | 89 |
| C2 | 75 µm, 25% | 2704 | 2357 | 1709 | 54 | 0.94 | 85 | 75 µm, 50% | 3647 | 3195 | 2352 | 174 | 0.64 | 85 | 1 mm, 25% | 2972 | 2683 | 1837 | 62 | 0.95 | 84 | 1 mm, 50% | 3737 | 3314 | 2540 | 297 | 0.50 | 86 |
|
|
Note: WS = water soaked.
|