The Curing Kinetics of Multiscale [Ni(EDTA)]-2 Intercalated Zn-Al Layered Double Hydroxides: Glass Fiber–Epoxy Composite Prepreg
Table 1
The kinetic parameters of the curing of GEP, GELP, and GELNiP based on the FR and KAS model at various heating rates.
| Samples | 5 K/min | 10 K/min | 15 K/min | 20 K/min | Mean | FR | KAS | FR | KAS | FR | KAS | FR | KAS | FR | KAS |
| GEP | | | 61.2 | 56.9 | LnA | 10.34 | 8.4 | 9.43 | 10.02 | 9.3 | 9.67 | 9.4 | 8.9 | 9.6 | 9.24 | | 0.24 | 0.32 | 0.29 | 0.27 | 0.25 | 0.29 | 0.23 | 0.31 | 0.25 | 0.29 | | 1 | 1.06 | 1.22 | 1.14 | 1.04 | 1.25 | 0.95 | 1.01 | 1.05 | 1.11 |
| GELP | | | 48.8 | 40.5 | LnA | 9.2 | 8.1 | 8.6 | 7.8 | 8.71 | 7.84 | 8.78 | 7.9 | 8.8 | 7.91 | | 0.45 | 0.34 | 0.32 | 0.38 | 0.31 | 0.27 | 0.31 | 0.29 | 0.35 | 0.32 | | 1.43 | 1.2 | 1.03 | 0.98 | 0.97 | 0.82 | 0.99 | 1.03 | 1.1 | 1 |
| GELNiP | | | 35.8 | 27.3 | LnA | 10.53 | 0.76 | 8.55 | 0.67 | 7.4 | 0.7 | 7.3 | 0.68 | 8.44 | 0.7 | | 0.36 | 0.28 | 0.37 | 0.34 | 0.33 | 0.31 | 0.3 | 0.29 | 0.34 | 0.3 | | 0.97 | 1.03 | 1 | 1.2 | 0.9 | 0.83 | 0.8 | 0.91 | 0.92 | 0.99 |
|
|