The Curing Kinetics of Multiscale [Ni(EDTA)]^-2 Intercalated Zn-Al Layered Double Hydroxides: Glass Fiber–Epoxy Composite Prepreg

Table 2

The values of α_p, α_m, and α_p^inf obtained from DSC analysis based on the Malek model at various heating rates.

Samples		5 K/min	10 K/min	15 K/min	20 K/min
GEP	αp^inf	0.598	0.624	0.618	0.644	0.24
	αp	0.564	0.596	0.58	0.619
	αm	0.31	0.168	0.18	0.116
GELP	αp^inf	0.625	0.634	0.612	0.674	0.31
	αp	0.624	0.608	0.541	0.632
	αm	0.241	0.201	0.319	0.197
GELNiP	αp^inf	0.704	0.619	0.627	0.668	0.37
	αp	0.679	0.574	0.59	0.637
	αm	0.201	0.246	0.407	0.217