A Novel Study of Synthesis and Experimental Investigation on Hybrid Biocomposites for Biomedical Orthopedic Application
Table 2
Summary of flexural strength and influence of input parameters.
| Exp. runs | Fiber types | Laminate count | Infill density (%) | Raster angle | Flexural strength (MPa) | S/N ratio |
| 1 | KF + RH | 2 | 30 | 0/60 | 15.23 | 23.6540 | 2 | KF + RH | 4 | 60 | 30/120 | 18.34 | 25.2680 | 3 | KF + RH | 6 | 90 | 50/140 | 17.35 | 24.7860 | 4 | KF + RH | 8 | 120 | 70/160 | 20.47 | 26.2224 | 5 | RH + FX | 2 | 60 | 50/140 | 22.91 | 27.2005 | 6 | RH + FX | 4 | 30 | 70/160 | 21.05 | 26.4650 | 7 | RH + FX | 6 | 120 | 0/60 | 18.40 | 25.2964 | 8 | RH + FX | 8 | 90 | 30/120 | 17.39 | 24.8060 | 9 | FX + CF | 2 | 90 | 70/160 | 19.08 | 25.6116 | 10 | FX + CF | 4 | 120 | 50/140 | 20.05 | 26.0423 | 11 | FX + CF | 6 | 30 | 30/120 | 18.73 | 25.4508 | 12 | FX + CF | 8 | 60 | 0/60 | 17.34 | 24.7810 | 13 | CF + KF | 2 | 120 | 30/120 | 20.31 | 26.1542 | 14 | CF + KF | 4 | 90 | 0/60 | 23.07 | 27.2610 | 15 | CF + KF | 6 | 60 | 70/160 | 24.89 | 27.9205 | 16 | CF + KF | 8 | 30 | 50/140 | 19.57 | 25.8318 |
|
|