Polysaccharide Fibers as Matrices for Solid-Surface Fluorescence

Rogacheva, Svetlana M.; Shipovskaya, Anna B.; Strashko, Anna V.; Gubina, Tamara I.; Volkova, Elena V.; Melnikov, Andrey G.

doi:https://doi.org/10.1155/2014/183413

International Journal of Polymer Science

On this page

Abstract Introduction Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 183413 | https://doi.org/10.1155/2014/183413

Polysaccharide Fibers as Matrices for Solid-Surface Fluorescence

Svetlana M. Rogacheva,¹Anna B. Shipovskaya,^1,2Anna V. Strashko,¹Tamara I. Gubina,¹Elena V. Volkova,¹and Andrey G. Melnikov¹

Academic Editor: Vitor Sencadas

Received01 Sept 2014

Accepted20 Nov 2014

Published08 Dec 2014

Abstract

Fibers of cellulose diacetate (CDA) and chitosan (CTS) of polycationic and polybasic forms were tested as matrices for solid-surface fluorescence (SSF) of several fluorescent probes—eosin Y, trypaflavine, and pyrene. The morphology and surface potential of these matrices were examined. The influence of structural and energetic characteristics of the fibrous polysaccharide materials at SSF of the probes was shown. Fluorescence was studied in aqueous solutions of eosin Y and trypaflavine, in water-ethanolic and water-micellar surfactant media of pyrene, before and after dynamic sorption of the dyes on fibers and in the adsorbed state. The surface of CDA fiber was shown to be capable of sorbing trypaflavine from water and pyrene from water-micellar surfactant media of various types, so it can be a promising matrix for SSF of pyrene and trypaflavine and their chemical analogs. The Coulomb interactions were proposed to determine eosin Y and trypaflavine concentration on the surface of CTS matrices and the SSF of these probes. The CTS fibers were permeable to hydrophobic pyrene dissolved in an ethanol-water medium or solubilized in the micelles of ionic surfactants.

1. Introduction

Analytical methods usually include sample separation and preconcentration, which have a direct impact on their accuracy, precision, and detection limits. At present, considerable attention is paid to solid-phase extraction (SPE), which involves adsorption of analytes on solid sorbents. SPE is widely applied in the analysis of various chemical compounds from environmental samples, body fluids, food, and so forth [1–5].

SPE can be the first stage of the spectrofluorimetric determination of an analyte in a solid phase. Nowadays, solid-surface [6] or solid-matrix [7] luminescence is successfully applied for trace quantification of organic and inorganic compounds in various media. Data are available on the solid-surface fluorescent (SSF) analysis of polycyclic aromatic hydrocarbons (PAH) in aqueous media [3, 8], anticonvulsant carbamazepine and its main metabolite in human serum [9], retinol in aqueous micellar media with a low quantity of a short-chain alcohol [10], caffeine in urine, plasma and serum [11], doxycycline in water media [12], explosives in a vapor phase [13], Al(III), Be(II), and Ga(III) in water [14], and so forth. Since SSF combines sorption preconcentration with the direct measurement of the analyte fluorescence, it can be used in chemical sensors [15] or even nanosensors [16] for intracellular analysis.

There are many solid materials with various properties which are suitable for SSF applications. Among them are silica gel [12, 17], zeolite [18], foamed polyurethane [19], cellulose [14], and so forth. Decyl methacrylate was used as a matrix for fluorescent nanosensors [16]. The unique electrical, mechanical, and chemical properties of nanomaterials have sparked great interest in their usage for SSF as well [11, 20, 21].

The availability and low cost of the raw materials which a matrix is made of are important for its selection. Therefore, the interest in materials based on natural polysaccharides and their derivatives is growing. The cellulose matrix, being a solid particulate material of a microfiber structure, is most popular as a sorbent for SSF [14, 22, 23]. Cellulose’s disadvantages, however, are its disposability and the relatively low efficiency of sorption due to the hydrophilic nature of the material. Therefore, searching for other promising polysaccharide materials to design matrices for analyte sorption is important.

Polymeric materials based on cellulose diacetate (CDA) have a number of valuable properties. They are widely used as sorbents in various industries and as membranes for the purification and preconcentration of proteins, enzymes, and antibiotics [24, 25]. The aminopolysaccharide chitosan (CTS) is promising as well. Materials on its basis exhibit a high sorption capacity [26, 27] and serve effective sorbents of some nonpolar compounds (dyes, surfactants), heavy metal ions, and so forth [28, 29]. Depending on the technique of formation, CDA and CTS materials can be prepared in various morphological forms such as films or fibers [25, 27]. This allows one to vary the surface characteristics of the polymeric sorbent. The presence of such a complex of useful properties determines good prospects of CDA and CTS for the design of new materials for purification, concentration, and analysis purposes.

The aim of this study was to assess the ability of polysaccharide matrices based on CDA and CTS fibers to interact with substances of different types for their application in solid-surface fluorescent analysis.

2. Experimental Methods

2.1. Polysaccharide Matrices

Fibrous materials made of CDA and CTS were used in the study. Polymer characteristics are as follows: CDA with a viscosity-average molecular weight of 77 kDa, an acetylation degree of 55%, and a 3% moisture, used for the production of acetate filaments of textile purposes (Technofilter Ltd., Vladimir, Russia); CTS with , a deacetylation degree of 82 mol.%, and a 9% moisture (JSC “Bioprogress,” Shchelkovo, Russia). CDA and CTS fibers were prepared from polymer solutions in 70% acetic acid (reagent grade) by electrospinning at the Educational & Research Institute of Nanostructures and Biosystems (Chernyshevsky Saratov State University, Russia). CTS in these fibers existed in two chemical forms, namely, polycationic or polybasic. To convert CTS from polycationic to polybasic form, the samples were incubated in 1 N NaOH solution for an hour. Then they were washed with distilled water until pH 7 and dried at 20°C during one day.

2.2. Materials

Eosin Y, trypaflavine (Sigma, USA), and pyrene (Fluka, Germany) of the Purum brand were used as fluorescent probes. The main component content in all probes was 96%. 2.96 × 10⁻⁶ M aqueous solutions of eosin Y (pH = 5.3), 1.21 × 10⁻⁶ M aqueous solution of trypaflavine (pH = 7.4), and water-ethanolic (pH = 6.9) and water-micellar surfactant solutions of pyrene with a concentration of 2.24 × 10⁻⁵ M were used in our experiments.

A stock solution of pyrene was prepared by dissolving an accurate weight in ethanol. The resulting solution was stored in a dark place to prevent photochemical destruction. Water-ethanolic pyrene solutions for tests were prepared by diluting the stock solution with distilled water immediately prior to use.

Aqueous micellar solutions of pyrene were prepared using such surfactants as sodium dodecyl sulfate, SDS (LenReaktiv, St. Petersburg, Russia), cetyltrimethylammonium bromide, CTAB (Sigma, Alfa Aesar Manufacturer, Great Britain), and polyoxyethylene (10) mono-4-isooctylphenyl ether, TX-100 (ACROS ORGANICS, USA). The pure substance content was 98-99% for all surfactants. The weight of pyrene was dissolved in 0.5 M solution of the surfactant, diluted with distilled water to the final surfactant concentration of 10⁻² M. The pH of the aqueous micellar solutions of pyrene was 8.8, 8.1, and 8.5 for SDS, CTAB, and TX-100, respectively. The pH of the solutions was measured with a pH meter pH-673 M (“Measurement Equipment” Ltd., Moscow).

2.3. Testing Methods for CDA and CTS Fibers

Surface morphology was evaluated by scanning electron micrographics (SEM) on MIRA LMU electron scanning microscope (Tescan, Czech Republic) at a voltage of 8 kV and a conductive current of 60 pA. A gold layer of 5 nm thickness was sprayed onto the samples with a K450X carbon coater device (Germany); the spraying current was 20 mA, with the spraying duration of 1 min.

The surface potential (, mV) of fibrous matrices was measured with a surface potential sensor (Nima KSV, Finland).

2.4. Conditions of the Solid-Phase Sorption of Probes

The sorption of fluorescent probes was performed in the dynamic mode. To this purpose, the solutions ( = 10 mL) were passed through the fiber five times, using a disposable sterile syringe Master UNI “PharmLine Limited” (Cornwall Buildings, Birmingham, Great Britain) with a sorbent holder and a receiving reservoir. The mass of the sorbents was 0.05 ± 0.01 g. The fibrous matrices were then dried at room temperature until constant weight was reached.

2.5. Fluorescent Analysis

The fluorescence spectra of fluorescent probes in solution and in an adsorbed state on solid matrices were recorded on a LS 55 fluorescent spectrometer from Perkin-Elmer (Perkin-Elmer Life and Analytical Sciences, Inc., USA). A xenon lamp operating in pulse mode with a frequency of 50 Hz served as a source of radiation. The Monk-Gillieson monochromators were employed. The fluorescence of solutions was measured in a standard quartz cuvette with = 1 cm, whilst a holder for solid samples was used for solid matrices.

The fluorescence of trypaflavine, eosin Y, and pyrene was measured within the spectral range of 475–575, 520–580, and 350–450 nm, respectively; the wavelength setting accuracy was 1 nm. The excitation radiation wavelength for trypaflavine, eosin Y, and pyrene was 460, 500, and 320 nm, respectively. The scanning rate was 200 nm/min.

The extraction degree (, %) of the probes was determined as [23] where and are the maximum values of fluorescence intensity () of the substance in the source solution and in that after sorption concentration on the fiber. , that is, the value of of the fifth vibronic band in the spectrum, was used for pyrene.

The relative fluorescence intensity () of pyrene in solution was determined as /1000, where is the maximum value of of the fifth vibronic band in the spectrum.

3. Results and Discussion

3.1. Material Morphology and Surface Potential

Fibrous materials on the basis of polysaccharides of vegetable and animal origin were used in our studies. CDA is the product of cellulose acetylation, with 50–60% of the hydroxyl groups replaced by acetate groups. It is insoluble in water, hydrophobic, and highly soluble in process solvents (acetone, methylene chloride), which allows obtaining fibers, films, and membranes on an industrial scale [24, 25].

The macromolecule of CTS has a heterochain structure and is built from -glucosamine units (mainly) and -acetyl--glucosamine units linked by β-1,4-glycoside bonds. The presence of an amino group in the elementary unit leads to two possible chemical forms of CTS in ready fibers, namely, the polycationic and polybasic forms, depending on the preparation technique used [27]. Polycationic CTS is well soluble in water, whereas the polybasic form is hydrophobic. Fibers made of these two forms of CTS differ in other physicochemical characteristics as well.

We examined the morphology and surface-energy characteristics of several fibrous materials based on CDA and CTS; Figure 1 shows their SEM images.

(a)

(b)

(c)

The material made of CDA is seen to have the highly ordered stacking of fibers whose diameter varies within the range = 300–3000 nm (Figure 1(a)). The material made of the polycationic CTS is characterized by the weakly ordered stacking of fibers with = 150–400 nm (Figure 1(b)). The material made of the polybasic CTS has a cellular structure (Figure 1(c)). When the chemical form of CTS switches from polycationic to polybasic form, the fibers are curved, their diameter increases, and the pore sizes in the material reduce.

The surface potential of our fibrous materials at the interface with air was estimated (Table 1). Bound water in the surface layer of the material was taken into account. The measurement results indicate that the surface of the polycationic and polybasic CTS fibers has a positive and a negative charge, respectively. The absolute value of of the fibrous material of both chemical forms of CTS varies slightly. The CDA fiber surface is characterized by a positive value of the potential, whose modulus by 2.2–3.6 times exceeds this value for the CTS fibers.

Thus, the fibrous polysaccharide materials have different structural and energetic characteristics, which can affect their interaction with organic substrates during SSF analysis.

3.2. Fluorescence of Hydrophilic Dyes in Water and Solid Phases

Two hydrophilic fluorescent dyes of different families, namely, trypaflavine (acriflavine chloride) and eosin Y, were used in our experiments [30].

Trypaflavine is an acridine dye, readily soluble in water. The application areas of trypaflavine are as follows: an antiseptic and an intercalating dye for DNA and proteins investigation [31]. On the basis of probes of a structure similar to methylacridinium-9-carboxamide N-methylacridinium-9-methyl carboxylate, fluorescent molecular sensors for halide ions (except F⁻) based on collisional quenching of a dye have been designed [30].

Eosin Y is a dye of the xanthene family, soluble in water, very sensitive to pH, and used as a pH fluorescent probe. It is known as a fluorophore undergoing neither photoinduced proton transfer nor photoinduced electron transfer. When pH increases, the absorption and emission bands of its acidic form decrease with a concomitant increase in the absorption and emission bands of the basic form [30].

Eosin Y fluorescence and trypaflavine fluorescence were studied in aqueous solutions before and after their dynamic sorption on fibers and in an adsorbed state. As an example, presented are the fluorescence spectra of trypaflavine (Figure 2) and eosin Y (Figure 3) in aqueous solutions before and after sorption on the CDA and CTS fibers, respectively, and in the adsorbed state. We note that eosin Y is hardly sorbed on CDA, while trypaflavine is poorly sorbed on the CTS fiber.

The spectra of trypaflavine and eosin Y have one fluorescence maximum () at wavelengths of 505 and 537 nm, respectively, in both aqueous phase and sorbent phase. The polycationic CTS fiber is an exception, which is found to shift the eosin Y to = 543 nm. This allows one to evaluate the content of substances in solution and on the surface of the sorbent from the value of the fluorescence intensity at the maximum of the spectrum and to estimate the extraction degree (, %) of substances.

To compare the signal intensity of a substance in the sorbent phase with its extraction degree, the ratio /% was calculated, where is the of the substance in solution before sorption and is the of the substance in the adsorbed state on the fibrous matrix. This ratio represents the change in the signal intensity of the substance in its adsorbed state.

Table 2 shows that the extraction degree of trypaflavine and eosin Y on the CDA fiber is 24.2 and 3.3%, respectively. Consequently, the CDA fiber interacts better with trypaflavine than with eosin Y. On the contrary, the CTS fibers showed higher affinity for eosin Y than for trypaflavine: the extraction degree of eosin Y on the polybasic and polycationic CTS fibers was 95.5 and 31.8%, respectively.

Trypaflavine concentration on the fiber surface is supported by the appearance of its fluorescence signal on the matrix. The SSF intensity somewhat exceeds the value by which has decreased due to sorption. Note that the CDA fiber surface is hydrophobic and has a total positive charge +419.0 ± 1.0 mV while acriflavinium chloride in a neutral medium (pH = 7.4) exists in a dissociated state. Chloride ions possibly recharge the fiber surface, and trypaflavine cations partially remain on the surface of the matrix by electrostatic attractions.

At similar extraction degrees of trypaflavine by the CTS fibers of both forms, the intensity of its signal in the adsorbed state on the polybasic CTS fiber was 3 times higher than on the polycationic CTS fiber. The polycationic CTS fiber is hydrophilic with a total surface charge of +116.5 ± 1.5 mV. Possibly, therefore trypaflavine well penetrates through the pores of the sorbent and sorbs in the bulk of the fibrous matrix rather than on its surface. The surface of the hydrophobic polybasic CTS fibers has a total negative charge, so trypaflavine cations concentrate in the water layer at the surface of the matrix, which results in an increased SSF signal.

A similar effect is observed for eosin Y sorption on the polycationic CTS fiber. When pH > 5, eosin Y is a negatively charged dianion, which favors its concentration at the surface of the matrix with a total positive charge. Its SSF signal amplifies. The polybasic CTS fiber absorbs 95.5% of eosin Y, that is, three times more than the polycationic CTS fiber. But the SSF signal is increased by 1.5 times only, which, in our opinion, means distribution of the probe inside the bulk of the sorbent, promoted by the cellular structure of this material.

The porous structure of chitosan fibers can be useful for the design of hydrophilic fluorescent probe matrices on their basis for usage in chemical sensors. Porous silica films doped with small molecule fluorophoric metalloporphyrins are examples of high-sensitivity sensors of explosives [13].

3.3. Fluorescence of Pyrene in Water-Ethanolic and Water-Micellar Solutions and on Solid Phases

Pyrene is known as a hydrophobic dye used to explore the polarity of a medium [30, 32]. It is commonly used as a model compound in studies on PAH [23]. The fluorescence emission spectrum of pyrene is known to have a vibronic structure with five bands within the wavelength range 360–450 nm. The concentration and extraction degree of pyrene are usually determined by the fluorescence intensity () of the fifth band ( = 395 nm). The intensity ratio () of the first ( = 375 nm) and third ( = 385 nm) bands, called the polarity index, is used to evaluate the polarity of the microenvironment of the probe [32].

We examined the fluorescence of the hydrophobic pyrene probe in water-ethanolic and aqueous micellar solutions before and after dynamic sorption on the fibers and in the solid phase of the sorbents under study.

The pyrene signal intensity in water-ethanolic solutions after sorption on the CDA and CTS fibers decreases slightly. Figure 4 shows the fluorescence spectra of pyrene in water-ethanolic solutions before and after sorption on the CDA fibers, which have a typical vibronic structure [23, 32]. The pyrene signal in the ethanolic solution on the CDA matrix is weak but much higher than expected, given that is 10% (Figure 4). The pyrene signal on both types of CTS fibers is almost zero. Consequently, the sorption of pyrene from its ethanolic solution on the fibers proceeds weakly. But after sorption on the CDA fibers the pyrene signal intensity increased, which was also observed with cellulose used as a matrix [23].

To improve the sorption characteristics of the matrix, surfactants of different nature were used: the anionic SDS, the cationic CTAB, and the nonionic TX-100. A similar approach is described in earlier papers [23, 33]. The actual surfactant concentration (10⁻² M) was above the critical micelle concentration (CMC). The fluorescence spectra of pyrene in aqueous micellar media before sorption, after sorption, and in an adsorbed state on the fibers tested are shown in Figures 5 and 6.

(a)

(b)

(c)

(a)

(b)

(c)

When the spectra of pyrene in the aqueous micellar medium are recorded before sorption (Figures 5 and 6), one can conclude that the maximum intensity of fluorescence is observed in the presence of CTAB, while the lowest one is in the case of SDS at the same concentration of pyrene in the medium. This gives evidence of the highest concentration of pyrene in the micelles of the cationic surfactant.

From the changes in the signal intensity after sorption and the values of the extraction degree of pyrene given in Table 3 it is evident that the CDA fibers have a greater sorption capacity than the CTS ones. Pyrene sorption on the CDA fibers proceeds better from the aqueous micellar media with TX-100 (the extraction degree was 82.9%). When the CTS fiber was used, the maximum extraction degrees of pyrene (74.2%, 72.1%) were observed for the TX-100 solution as well.

Moreover, it is clear from Figures 5 and 6 that the pyrene signal is greatly enhanced in the adsorbed state on CDA. It is much higher than the signal in solution, which is probably due to concentration of pyrene molecules at the surface of the CDA fibers in a micellar layer [21, 23]. The solutions with SDS are exceptions. At the same time, the values of the fluorescence intensity of pyrene sorbed on the CTS fibers of both forms are close to zero, in spite of the high extraction degree of the probe in the medium with TX-100, which may be due to probe penetration into the pores of the fibrous material and fluorescence quenching.

3.4. Effect of the Surfactant Nature on the SSF of Pyrene

To compare the effect of the surfactants selected on the fluorescence of pyrene in the CDA phase, we calculated the values of the pyrene fluorescence intensity () in relative terms (). Figure 7 shows that the maximum SSF signal was observed after sorption from the aqueous micellar solution of TX-100 while the minimum signal was from the aqueous micellar solution of SDS. It is noted that the use of the cationic CTAB leads to the maximum enhancement of the pyrene SSF signal at the minimum extraction degree for CDA in this experiment.

Transition of PAH molecules from the aqueous macrophase to the micellar micropseudophase is known to occur in surfactant micellar media; for example, the transfer efficiency of pyrene into SDS micelles reaches 99% [33]. Micelles can be adsorbed on the matrix and concentrate pyrene on the sorbent surface. Consequently, an increased SSF signal indicates effective interaction of the micelles with the fiber surface. These results tell us that the CTS-based fiber, probably due to its mesh structure, is well permeable to ionic surfactants and pyrene. The highly ordered fibrous CDA material, on the contrary, retains micelles with solubilized pyrene at its surface.

Of course, the nature and CMC of surfactants shall affect the extraction degree of pyrene from aqueous solution. The CMC₁/CMC₂ of the surfactants in water at 25°C are known to be 8.0/50 mM for SDS [34], 0.9/21 mM for CTAB [35, 36], and 0.2/1.4 mM for TX-100 [37]; that is, the surfactant concentration used (10 mM) was almost equal to CMC₁ for SDS, 10 CMC₁ for CTAB, and 1.5 CMC₂ for TX-100. Apparently, this explains the differences in the pyrene fluorescence intensity in various aqueous micellar media and on our CDA fibers modified with various surfactants.

The influence of surfactants on the pyrene SSF on the CDA fibers is the subject of special studies. We have established the fact of the effective sorption of pyrene from water-micellar media on this matrix and the intense fluorescence of the probe in the sorbed state, which can be used in chemical sensors.

4. Conclusions

The experimental results show that the material made of CDA has a highly ordered stacking of fibers with = 300–3000 nm and the surface potential = +419.0 ± 1.0 mV. The material made of polycationic CTS is characterized by = +116.5 ± 1.5 mV and a weakly ordered stacking of fibers with = 150 nm. The polycationic-polybasic switch in CTS leads to distortion of the fibers, their increased diameter, reduced pore sizes in the material, and an inversed sign of the surface potential: = −192.5 ± 0.5 mV.

CDA fibers are capable of sorbing trypaflavine on their surface; that is, they can be used as a matrix for SSF of this dye and similar (by chemical structure) probes. CDA fibers are also good sorbents for pyrene from water-micellar surfactant media of various types and promising matrices for its SSF.

For the CTS fibers it is shown that the SSF signal of eosin Y anions increases on the surface with the total positive charge (the polycationic form) and that of trypaflavine cations does on the surface with the total negative charge (the polybasic form); that is, the Coulomb interactions determine concentration and fluorescence of these probes on CTS matrices. The polybasic CTS fibers have the highest sorption capacity ( = 95.5%) relative to the negatively charged eosin Y.

The CTS fibers are permeable to hydrophobic pyrene dissolved in a water-ethanolic medium or solubilized in the micelles of ionic surfactants at concentrations below CMC₂.

These results can be used in the design of chemical sensors.

Acronyms

CDA:	Cellulose diacetate
CMC:	Critical micelle concentration
CTAB:	Cetyltrimethylammonium bromide
CTS:	Chitosan
PAH:	Polycyclic aromatic hydrocarbons
SEM:	Scanning electron micrographics
SDS:	Sodium dodecyl sulfate
SPE:	Solid-phase extraction
SSF:	Solid-surface fluorescence
TX-100:	Polyoxyethylene (10) mono-4-isooctylphenyl ether.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

The results of this work were obtained in the framework of the State Task no. 4.1299.2014/K of the Russian Ministry of Education and Science, and this study is also supported by the RFBR Grant MОЛ_a no. 12-02-31196.

References

M. Safarikova and I. Safarik, “Magnetic solid-phase extraction,” Journal of Magnetism and Magnetic Materials, vol. 194, no. 1, pp. 108–112, 1999.
View at: Publisher Site | Google Scholar
A. Poliwoda, A. M. Chrzanowska, K. Orlowska, and P. P. Wieczorek, “Membrane extraction and solid-phase extraction as effective methods for extraction and concentration of organic compounds from samples with complex matrix composition,” Chemik, vol. 68, no. 4, pp. 312–320, 2014.
View at: Google Scholar
J. L. Whitcomb and A. D. Campiglia, “Screening potential of solid-phase extraction and solid surface room temperature fluorimetry for polycyclic aromatic hydrocarbons in water samples,” Talanta, vol. 55, no. 3, pp. 509–518, 2001.
View at: Publisher Site | Google Scholar
H. Wang and A. D. Campiglia, “Determination of polycyclic aromatic hydrocarbons in drinking water samples by solid-phase nanoextraction and high-performance liquid chromatography,” Analytical Chemistry, vol. 80, no. 21, pp. 8202–8209, 2008.
View at: Publisher Site | Google Scholar
P. P. Vazquez, A. R. Mughari, and M. M. Galera, “Solid-phase microextraction (SPME) for the determination of pyrethroids in cucumber and watermelon using liquid chromatography combined with post-column photochemically induced fluorimetry derivatization and fluorescence detection,” Analytica Chimica Acta, vol. 607, no. 1, pp. 74–82, 2008.
View at: Publisher Site | Google Scholar
J. N. Miller, “Luminescence measurements on surfaces,” Pure and Applied Chemistry, vol. 57, no. 3, pp. 515–522, 1984.
View at: Google Scholar
R. J. Hurtubise, “Solid-matrix luminescence analysis: photophysics, physicochemical interactions and applications,” Analytica Chimica Acta, vol. 351, no. 1–3, pp. 1–22, 1997.
View at: Publisher Site | Google Scholar
J. F. Fernández-Sánchez, A. Segura Carretero, C. Cruces-Blanco, and A. Fernández-Gutiérrez, “The development of solid-surface fluorescence characterization of polycyclic aromatic hydrocarbons for potential screening tests in environmental samples,” Talanta, vol. 60, no. 2-3, pp. 287–293, 2003.
View at: Publisher Site | Google Scholar
G. M. Escandar, D. G. Gómez, A. E. Mansilla, A. M. De La Peña, and H. C. Goicoechea, “Determination of carbamazepine in serum and pharmaceutical preparations using immobilization on a nylon support and fluorescence detection,” Analytica Chimica Acta, vol. 506, no. 2, pp. 161–170, 2004.
View at: Publisher Site | Google Scholar
M. Torre, M. Sánchez-Hernández, S. Vera, and M. P. San Andrés, “Improvement in retinol analysis by fluorescence and Solid Phase Extraction (SPE) in micellar medium,” Journal of Fluorescence, vol. 18, no. 2, pp. 487–497, 2008.
View at: Publisher Site | Google Scholar
M. C. Talio, M. Alesso, M. Acosta, M. G. Acosta, M. O. Luconi, and L. P. Fernández, “Caffeine monitoring in biological fluids by solid surface fluorescence using membranes modified with nanotubes,” Clinica Chimica Acta, vol. 425, pp. 42–47, 2013.
View at: Publisher Site | Google Scholar
I. I. Parashchenko, T. D. Smirnova, S. N. Shtykov, V. I. Kochubei, and N. N. Zhukova, “Doxycycline-sensitized solid-phase fluorescence of europium on silica in the presence of surfactants,” Journal of Analytical Chemistry, vol. 68, no. 2, pp. 112–116, 2013.
View at: Google Scholar
M. E. Germain and M. J. Knapp, “Optical explosives detection: from color changes to fluorescence turn-on,” Chemical Society Reviews, vol. 38, no. 9, pp. 2543–2555, 2009.
View at: Publisher Site | Google Scholar
V. G. Amelin, N. S. Aleshin, O. I. Abramenkova, Y. N. Nikolaev, and I. A. Lomonosov, “Solid-phase fluorometric determination of Al(III), Be(II), and Ga(III) using dynamic preconcentration on reagent cellulose matrix,” Journal of Analytical Chemistry, vol. 66, no. 8, pp. 709–713, 2011.
View at: Publisher Site | Google Scholar
C. McDonagh, C. S. Burke, and B. D. MacCraith, “Optical chemical sensors,” Chemical Reviews, vol. 108, no. 2, pp. 400–422, 2008.
View at: Publisher Site | Google Scholar
M. Brasuel, R. Kopelman, T. J. Miller, R. Tjalkens, and M. A. Philbert, “Fluorescent nanosensors for intracellular chemical analysis: Decyl methacrylate liquid polymer matrix and ion-exchange-based potassium PEBBLE sensors with real-time application to viable rat C6 glioma cells,” Analytical Chemistry, vol. 73, no. 10, pp. 2221–2228, 2001.
View at: Publisher Site | Google Scholar
R. K. Bauer, R. Borenstein, P. de Mayo et al., “Surface photochemistry: translational motion of organic molecules adsorbed on silica gel and its consequences,” Journal of the American Chemical Society, vol. 104, no. 17, pp. 4635–4644, 1982.
View at: Publisher Site | Google Scholar
S. Beltyukova, O. Teslyuk, A. Egorova, and E. Tselik, “Solid-phase luminescence determination of ciprofloxacin and norfloxacin in biological fluids,” Journal of Fluorescence, vol. 12, no. 2, pp. 269–272, 2002.
View at: Publisher Site | Google Scholar
S. G. Dmitrienko, E. Y. Gurariy, R. E. Nosov, and Y. A. Zolotov, “Solid-phase extraction of polycyclic aromatic hydrocarbons from aqueous samples using polyurethane foams in connection with solid-matrix spectrofluorimetry,” Analytical Letters, vol. 34, no. 3, pp. 425–438, 2001.
View at: Publisher Site | Google Scholar
A. Moghimi and M. Alijanianzadeh, “Preconcentration of benzene and phenolic compounds in water sample by adsorption on carbon nanotubes coated fiber,” African Journal of Pure and Applied Chemistry, vol. 7, no. 6, pp. 208–217, 2013.
View at: Google Scholar
G. I. Romanovskaya, A. Y. Olenin, and S. Y. Vasil'Eva, “Concentration of polycyclic aromatic hydrocarbons by chemically modified silver nanoparticles,” Russian Journal of Physical Chemistry A, vol. 85, no. 2, pp. 274–278, 2011.
View at: Publisher Site | Google Scholar
A. H. Ackerman and R. J. Hurtubise, “Methods for coating filter paper for solid-phase microextraction with luminescence detection and characterization of the coated filter paper by infrared spectrometry,” Analytica Chimica Acta, vol. 474, no. 1-2, pp. 77–89, 2002.
View at: Publisher Site | Google Scholar
O. A. Dyachuk, T. I. Gubina, and G. V. Melnikov, “Adsorption preconcentration in the luminescence determination of polycyclic aromatic hydrocarbons,” Journal of Analytical Chemistry, vol. 64, no. 1, pp. 7–11, 2009.
View at: Publisher Site | Google Scholar
P. Zugenmaier, “Characterization and physical properties of cellulose acetates,” Macromolecular Symposia, vol. 208, pp. 81–166, 2004.
View at: Google Scholar
S. Fischer, K. Thümmler, B. Volkert, K. Hettrich, I. Schmidt, and K. Fischer, “Properties and applications of cellulose acetate,” Macromolecular Symposia, vol. 262, no. 1, pp. 89–96, 2008.
View at: Publisher Site | Google Scholar
M. Rinaudo, “Chitin and chitosan: properties and applications,” Progress in Polymer Science, vol. 31, no. 7, pp. 603–632, 2006.
View at: Publisher Site | Google Scholar
V. K. Mourya and N. N. Inamdar, “Chitosan-modifications and applications: opportunities galore,” Reactive and Functional Polymers, vol. 68, no. 6, pp. 1013–1051, 2008.
View at: Publisher Site | Google Scholar
M. Jabli, M. H. V. Baouab, M. S. Roudesli, and A. Bartegi, “Adsorption of acid dyes from aqueous solution on a chitosan-cotton composite material prepared by a new pad-dry process,” Journal of Engineered Fibers and Fabrics, vol. 6, no. 3, pp. 1–12, 2011.
View at: Google Scholar
C. Gerente, V. K. C. Lee, P. Le Cloirec, and G. McKay, “Application of chitosan for the removal of metals from wastewaters by adsorption—mechanisms and models review,” Critical Reviews in Environmental Science and Technology, vol. 37, no. 1, pp. 41–127, 2007.
View at: Publisher Site | Google Scholar
B. Valeur, Ed., Molecular Fluorescence: Principles and Applications, Wiley-VCH Verlag GmbH, 2001.
R. F. Weiner and H. H. Selige, “Oxygen quenching of trypaflavine luminescence,” Photochemistry and Photobiology, vol. 4, no. 6, pp. 1207–1216, 1965.
View at: Google Scholar
K. Kalyanasundaram and J. K. Thomas, “Environmental effects on vibronic band intensities in pyrene monomer fluorescence and their application in studies of micellar systems,” Journal of the American Chemical Society, vol. 99, no. 7, pp. 2039–2044, 1977.
View at: Google Scholar
I. Y. Goryacheva, S. N. Shtykov, A. S. Loginov, and I. V. Panteleeva, “Preconcentration and fluorimetric determination of polycyclic aromatic hydrocarbons based on the acid-induced cloud-point extraction with sodium dodecylsulfate,” Analytical and Bioanalytical Chemistry, vol. 382, no. 6, pp. 1413–1418, 2005.
View at: Publisher Site | Google Scholar
A. P. Romani, A. E. da Hora MacHado, N. Hioka et al., “Spectrofluorimetric determination of second critical micellar concentration of SDS and SDS/Brij 30 systems,” Journal of Fluorescence, vol. 19, no. 2, pp. 327–332, 2009.
View at: Publisher Site | Google Scholar
R. Guo, X. J. Zhu, and X. Guo, “The effect of β-cyclodextrin on the properties of cetyltrimethylammonium bromide micelles,” Colloid & Polymer Science, vol. 281, no. 9, pp. 876–881, 2003.
View at: Publisher Site | Google Scholar
T. Liu and J. Wu, “Effect of CTAB and procain hydrochloride on neutral red microstructure in CTAB micelle,” Colloid Journal, vol. 70, no. 3, pp. 311–316, 2008.
View at: Publisher Site | Google Scholar
D. Yu, F. Huang, and H. Xu, “Determination of critical concentrations by synchronous fluorescence spectrometry,” Analytical Methods, vol. 4, no. 1, pp. 47–49, 2012.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Svetlana M. Rogacheva et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1279

Downloads

909

Citations