ISRN Nanomaterials
Volume 2012 (2012), Article ID 193836, 8 pages
http://dx.doi.org/10.5402/2012/193836
Review Article

Influence of Nanofinishes on the Antimicrobial Properties of Fabrics

NIFT TEA College of Knitwear Fashion, Tirupur 641 606, India

Received 20 September 2012; Accepted 12 November 2012

Academic Editors: A. Fidalgo, A. A. Ismail, and A. Kelarakis

Copyright © 2012 N. Gokarneshan et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

This paper critically reviews the influence of the various types of nanomaterials on the antibacterial property of the treated fabrics. The merits of each type of nanomaterial have been compared. The synthesis and application method of each type are highlighted. As the number of microorganisms is growing increasingly resistant to antibiotics, the need to treat fabrics with nano materials becomes important in order to improve the antibacterial efficacy over a range of bacterium and fungi. The various researches reported herein show a promise for wider applications in medical textiles. Nano finishes have been applied on natural materials such as cotton, wool, and silk and also synthetic materials such as PET fabrics, with interesting results.

1. Introduction

Textile materials tend to act as a good medium for the growth and multiplication of microorganisms. The basic chemical constituents present in the natural fibers provide nutrition to microorganisms and thereby promote their growth. The growth of microorganisms in the textile materials cause innumerable problems such as unacceptable odor, loss of strength in fabric, and stains and, moreover, affect the health of the wearer. It is therefore important to impart antimicrobial effect on textile materials so as to protect the health of the wearer. A number of antimicrobial agents have been used in textile applications [1]. Of these silver nanoparticles have one of the best antimicrobial characteristics and cover a wide range of pathogenic microorganisms. They react with the sulfur-based proteins of the cell wall in microorganisms, inhibit with their metabolism, and thereby destroy them [2, 3]. Cotton, wool, and silk fabrics have been effectively treated with silver nanoparticles to get the desired antimicrobial efficts [46]. However, the use of silver nanoparticles in textile applications has its own restrictions, as particle size below 50 nm can have a harmful impact on humans and the environment [7, 8]. Inorganic materials such as metal and metal oxides have attracted lots of attention over the past decade due to their ability to withstand harsh process conditions [9, 10]. Of the inorganic materials, metal oxides such as TiO2, ZnO, MgO, and CaO are of a particular interest as they are not only stable under harsh process conditions but also generally regarded as safe materials to human beings and animals [11]. The use of nanoparticles of silver and zinc oxide has been seen as a viable solution to stop infectious diseases due to the antimicrobial properties of these nanoparticles. The intrinsic properties of a metal nanoparticle are mainly determined by size, shape, composition, crystallinity, and morphology [12]. With growth in world population and the spread of disease, the number of antibiotic resistant microorganisms is rising along with the occurrence of infections from these microorganisms. With this increase in health awareness, many people focused their attention on educating and protecting themselves against harmful pathogens. It soon became more important for antimicrobially finished textiles to protect the wearer from bacteria than it was to simply protect the garment from fiber degradation [13]. The need for antimicrobial textiles goes hand-in-hand with the rise in resistant strains of microorganisms.

2. Finishes on Natural Fibres and Blends

2.1. Finish with Titanium Oxide
2.1.1. Synthesis of Titanium Oxide

In one of the methods reported [14], titanium tetrachloride has been used, which has been gradually added onto distilled water, four times its volume, maintained at ice cool temperature, and then taken to room temperature. Stirring has been done for 30 minutes to get a homogenous solution. The temperature of the bath has been raised to and maintained till the process of nanoparticle has been completed. Also urea has been dissolved in distilled water in the ratio of 1 : 12. The urea solution so prepared has been added to the previously prepared solution under constant stirring. The solution changed into a white colloid without any precipitation. When the reaction has been completed, the solution was allowed to settle and washed five times with distilled water.

2.1.2. Method of Application

Woven and knitted fabric comprising of 100% cotton and polyester/cotton (45/55) has been applied with titanium dioxide nanoparticles by spraying, using the pad dry cure method. The nanoparticles have been applied on the face side of the fabric with 1% concentration and material liquor ratio of 1 : 20 and 1% acrylic binder. Fabrics comprising of 100% cotton as well as 45/55% polyester/cotton produced as woven and knits have been coated with titanium dioxide nanoparticles in a dispersion form by using a spray gun. The fabric substrate has been fixed on a vertical board and nanoparticle solution evenly sprayed over the fabric by using a spray gun. A constant distance has been maintained between the fabric and spray gun nozzle. A padding mangle running at a speed of 15 m/min and with pressure of 15 kgs/cm2 has been used to squeeze out the excess solution [16]. The fabrics have then been dried naturally and cured for 3 min at .

2.1.3. Influence on Antibacterial Property

The coating of titanium dioxide in nanoform on the fabric surface enables improvement in the antimicrobial, UV blocking, and self-cleaning properties [2]. Nanotitanium dioxide solution and finishing agent have been prepared by sol-gel method. In this method of preparation tetrabutyl titanate have been used as the precursor and ethanol as the solvent. A padding technique has been adopted to impregnate polyester fabric with the agent [16]. Investigations for antimicrobial activity has been carried out on 100% cotton and polyester/cotton (45/55) woven and knitted fabrics. Titanium dioxide have normally been preferred over other titanium compounds owing to its higher effectiveness in preventing infections. The treated fabrics showed the growth of both types of organisms, namely, Staphylococcus aureus and Klebseilla pneumoniae. The growth of the bacteria has been found on both the fabric as well as surrounding it. In the case of titanium dioxide treated fabric, no bacterial growth has been observed on the fabric, but was surrounding it. Treated woven fabrics exhibit better bacterial reduction than their knitted counterpart, due to their construction. The blended fabric having 45/55 polyester/cotton exhibits better bacterial reduction than 100% cotton due to the resistance property of polyester (Table 1).

tab1
Table 1: Antibacterial activity of titanium dioxide nanoparticles treated fabrics [14].
2.2. Finish with Zinc Oxide
2.2.1. Method of Synthesis

The zinc oxide nanoparticles have been synthesized by two methods. The synthesis involved the use of zinc chloride, caustic soda (in pellet form), ethanediol, and propanol [17].The synthesis has been done under a state of very high saturation in such a way that the rate of nucleation achieved has been far higher than the growth rate [18]. Zinc chloride has been dissolved in 200 mL of water by maintaining a temperature of in an oil bath. Subsequently caustic aqueous solution has been added to zinc chloride solution with mild stirring for a period of about 10 minutes maintaining temperature at . Sedimentation technique has been adopted to isolate the particles from the supernatant dispersion.

The supernatant solution has been dispensed with and the suspension that remained has been washed with distilled water five times so as to reduce the concentration of sodium chloride below 10−6 mole (M). The dilution ratio between the concentrated suspension and the washing solution has been kept at 1 : 10, during every wash. The complete removal of the sodium chloride from the suspension was checked using the solution of silver nitrate. The purified particles were then peptized with 2-propanol in an ultrasonic bath for 10 min at room temperature. The peptization process is necessary to disrupt the microagglomerates and to release the nano particles of zinc oxide [19]. The particles were then collected by centrifugation at 6000 rpm for 15 min. The washing procedure was repeated three times. Thermal treatment of the particles at for 5 hours leads to the formation of zinc oxide. This method of synthesis of zinc oxide nano particles using water medium is for synthesis 1. In the second method of synthesis zinc oxide nano particles were synthesized using 1,2-ethanediol (instead of water) medium at keeping all other parameters same as described in synthesis 1.

In another research work [13], zinc oxide nano particles have been synthesized by the use of zinc nitrate and sodium hydroxide (precursors) and soluble starch (stabilizing agent) by adopting the wet chemical method. Soluble starch in varying concentrations (0.1%, 0.5%, and 1.0%) has been dissolved by 500 mL of distilled water, in a microwave oven. Zinc nitrate in suitable proportion has been added with constant stirring, so as to completely dissolve it in the solution. Sodium hydroxide solution of 0.2 M has then been added under constant stirring in a dropwise manner. After the complete addition of sodium hydroxide, the reaction was allowed to proceed for two hours. The solution has been allowed to settle overnight and the supernatant solution then discarded carefully. The remaining solution has been centrifuged and the nano particles so obtained have been washed with distilled water thrice. The washed nano particles have then been dried at 80°C overnight, resulting in a complete conversion of zinc hydroxide into zinc oxide [20].

2.2.2. Method of Application

Four types of fabrics have been produced using 100% cotton as well as 45/55 polyester/cotton in the form of knits and woven fabrics. These have been dyed using reactive blue dyes under identical conditions. The fabrics have been conditioned at 21°C and 65% RH and then soaked for 10 minutes in 2-propanol dispersion zinc oxide nano particles (5% w/w) under gentle magnetic stirring. The fabrics then have been squeezed on a padding mangle and oven-dried at 130°C for 15 min at an atmospheric pressure. The treated fabrics have then been washed five times as per the method described (UNI EN ISO 26330 : 1996). Laundering has been done and the washing cycles performed at 30°C with reference detergent without optical brighteners. The drying has been done on a flat surface, and the fabrics were tested before and after washing cycles using TEM and UV spectrophotometry in order to characterize the size and shape of the nano particles deposited.

2.2.3. Influence on Antibacterial Property

Qualitative antibacterial evaluation by agar diffusion method has shown that 100% cotton woven fabrics treated with zinc oxide nanoparticles showed a maximum inhibitory effect against S. aureus [21]. The results are indicative that ZnO treated fabric exhibits a higher antibacterial activity in comparison with ZnO bulk treated fabrics, while the untreated fabrics exhibited no antibacterial activity. The antibacterial activity has been observed to be higher in the case of S. aureus than E. coli, for both the fabrics treated with ZnO nanoparticles as well as the bulk treated ones, in all the trials carried out. Earlier study [21] seems to indicate that active oxygen species generated by ZnO particles could be a mechanism although there is no direct evidence from the reported study. A study has revealed the presence of active oxygen species [22]. It has already been proved that nanosized and micro sized ZnO suspensions are active in inhibiting the growth of bacteria. The nanosized ZnO suspension clearly has a much higher activity than the microsized ZnO suspension [22]. These results correlated with the subsequent investigation [21], as in both cases, that is, ZnO particle treated fabrics and bulk treated fabrics, exhibited an antibacterial activity. However, the ZnO nanoparticle treated fabrics showed a much higher antibacterial activity than its counterpart. Antimicrobial evaluation by parallel streak method revealed that ZnO nanoparticle treated fabric exhibited a maximum inhibitory effect against S. aureus with a zone of inhibition of 5.8 cm followed by E. coli, with a zone of inhibition of 3.7 cms. The percentage reduction test has been used to investigate the bacterial reduction quantitatively (Table 2). The results of this test correspond with those of the other methods, namely, the agar diffusion and parallel streak method. The ZnO nanoparticle treated fabrics exhibit a reduction percentage of 94.16% for S. aureus followed by 86.5% for E. coli. On the other hand the ZnO bulk treated fabrics exhibit comparatively a lower reduction percentage, while the untreated fabrics have negative values for the percentage reduction as the final number of bacterial cells will be much higher than the initial number, since it will have no bactericidal activity reflecting zero result. The improved bioactivity of ZnO nanoparticles has been investigated by researchers and its antimicrobial activity has been evaluated [23] and their antibacterial activity has been established. SEM observations have revealed that the ZnO particles produced by the wet chemical method are almost spherical, the particle size between 60 and 75 nm. SEM photographs have revealed that the treated fabrics show ZnO nanoparticles embedded onto fabrics. Tests on wash durability have shown that a considerable antimicrobial activity has been considerably retained in the ZnO nanoparticles treated fabrics up to 10 washes even after repeated wash cycles. The extent of bacterial reduction has been very low after 10 washes, and after 20 wash there has been no activity. In the case of ZnO bulk treated fabrics, the antibacterial activity has been retained only upto 5 repeated wash cycles.

tab2
Table 2: Agar diffusion test for treated and washed cotton fabrics [4].

A number of methods are available for the preparation of ZnO powder [2428]. The nanoparticle size differs with each method (60–100 nm) and is influenced by parameters such as precursor type, solvent, pH, and the temperature of reacting solution. The choice of method depends on the final application. The improved bioactivity of the smaller ZnO nanoparticles is due to the higher surface area to volume ratio. For smaller ZnO nanoparticles, more particles are needed to cover a bacterial colony (2 μm) which results in the generation of a larger number of active oxygen species (released from ZnO on the surface of the colony), which kill bacteria more effectively. ZnO nanoparticles were found to be more abrasive than bulk ZnO and thus contribute to the greater mechanical damage of the cell membrane and the enhanced bactericidal effect of ZnO nanoparticles.

2.3. Finish with Silver Oxide
2.3.1. Method of Synthesis

In a recent research [29], silver nanoparticles have been synthesized by adopting sonochemical method. The solution has been prepared in deionized water. Silver nitrate solution of containing 2% Poly vinyl Pyrrolidone has been sonicated in an ultra sonicator for a duration of 3 hours. The sonicated solution has then been boiled and 1% trisodium citrate has been added subsequently in a dropwise manner, until the color of the solution changed to yellow. The formation of silver nanoparticles is indicated by the yellow color of the solution. The silver nanoparticles obtained in the solution form have then been converted as powder (50–60 nm) by means of spray drying.

2.3.2. Method of Application

The silver nanoparticles that have been converted to powder have been dissolved in water so as to achieve a concentration of 50 ppm silver content. This has been applied on cotton and wool fabrics by exhaustion method. The fabrics have then been treated for 45 minutes at boiling temperature and then washed with normal water. The durability of the treated fabrics has been assessed according to AATCC 124-2001 procedure, for 5, 10, and 20 washes. The antimicrobial effect of the treated wool and cotton fabrics has been evaluated qualitatively by the agar diffusion method and quantitatively by the AATCC 100 [30].

2.3.3. Influence on Antibacterial Property

The results of the agar diffusion test for the assessment of antimicrobial efficacy for treated cotton fabrics as well as varyingly washed fabrics with regard to the inhibition zone are shown in Table 2 [30]. The results show a clear zone of inhibition ranging between 35 and 40 mm diameter for the fabrics treated against the selected microorganisms. Even after 20 washes the zone of inhibition remains visible in the fabrics so treated. The quantitative test results for the evaluation of antimicrobial efficacy of treated wool fabrics are shown in Table 2. It could be observed that the treated wool fabrics exhibit 100%, 97%, and 99% efficacy against S. aureus, E. coli and P. aeruginosa, respectively. The antimicrobial efficacy has been observed even after 20 washes in the treated fabrics. The PVP in the nanosilver powder forms hydrogen bond with hydroxyl groups of the cotton and the wool and also forms a coordinate bond with the silver nanoparticles and thereby enhances the durability of the antimicrobial finish. The PVP coated silver nanoparticles offer advantages such as the durability of finish and operational benefits that include simple handling, ease of application, and avoidance of agglomeration of nanoparticles.

Silver nanoparticles have been applied on silk fabrics [4]. The nanoparticles have been produced using a chemical method by reducing silver nitrate with reducing agents such as hydrazine and glucose. Silk fabric has been treated with silver nitrate in acidic pH between 3 and 4. Good antimicrobial activity has been observed against S. aureus and the fabrics have been maintained up to 80% antimicrobial activities after 5 cycles of washing. In yet another interesting recent work [31], antimicrobial activities have been observed on cotton fabrics by applying meso silver particles and silver chloride compounds (SILPURE). Evaluation has been done on the antibacterial assessment with treated as well as untreated fabrics. The zone of inhibition has been considered and the bacterial growth has been assessed as shown in Table 3.

tab3
Table 3: Evaluation of antimicrobial activity for fabrics treated with nanosilver [15].
2.4. Finish with Silver Nanocolloids
2.4.1. Method of Synthesis

A measured amount of silver sulphate (1  10-3 M) solution has been kept in a specially designed reaction chamber. The solution has then been reduced by the addition of cold and dilute solution of sodium borohydride in a nitrogen atmosphere, in a dropwise manner [15]. The mixture of the solution has been vigorously stirred during the reaction process. As the solution colour turned to light yellow, a small amount of trisodium citrate (1%) has been added dropwise with vigorous stirring. Distilled water has been used for preparing the solutions. The reaction equation is chemically represented below

2.4.2. Method of Application

Silver nanoparticles have been applied onto cotton, wool, and silk fabrics by dipping them in the dispersion for a duration of 10 minutes [15]. The fabrics have then been padded adopting a double dip and nip sequence at 70% expression. The padded fabrics have then been dried in air and cured at for 20 minutes.

2.4.3. Influence on Antibacterial Property

The antibacterial efficacy of the untreated as well as treated fabrics has been evaluated by measuring the loss in breaking load due to soil burial test (Figure 1) [15]. The results show that the treated fabrics exhibit the reduction of loss in breaking load in the case of cotton, wool, and silk fabrics. This indicates that treatment with silver nanocolloids improves the bacterial resistance in the treated fabrics. It could be attributed to the metallic ions and metallic compounds exhibiting a certain degree of a sterilizing effect. The oxygen present in the atmosphere is partially converted to active oxygen due to catalysis with the metallic ion and thus dissolves the organic substance to produce a sterilizing effect [32]. The antibacterial effect is greatly improved on account of the very large relative surface area, increasing their contact with bacteria or fungi. Nano silver has been found to be highly reactive with proteins. It therefore interferes with cell growth by seriously affecting cellular metabolism, through its contact with bacteria or fungus. Moreover, the respiration, basal metabolism of the electron system, and the transport of substrate in the microbial cell membrane get suppressed by the nanosilver particles. They also prevent the growth and division of bacteria and fungi that cause infection, odour, itchiness, and sores.

193836.fig.001
Figure 1: Effect of silver nanoparticles on resistance towards bacterial attack [32].

3. Finishes on Synthetic Fibres

3.1. Finish on Polyethylene Terephthalate (PET)
3.1.1. Method of Preparation and Application

PET fabrics have been subjected to single- and double-sided corona air treatment at the atmospheric pressure using a device meant for the purpose [34]. Fabrics have been placed on a backing electrode roller covered with silicon coating and rotating at a speed of 4 m/min. The distance between electrodes has been maintained at 2 mm. Corona plasma has been generated in the gap between the electrode and backing roller. Blank dyed fabrics with nano silver particles have been tested for bacterial reduction as per ASTM-E 2149-01 method [35]. The percentage reduction of the organisms resulting from contact with the specimen has been calculated. Corona plasma treatment has been used for the preparation of surfaces of PET fabrics so as to obtain better adhesive properties to nano silver particles. Nano silver particles of size 80 nm have been used.

3.1.2. Influence on Antibacterial Properties

Raw, washed, and washed-thermostabilized fabrics have been tested for antimicrobial efficacy. The microbial reduction is based on the concentration of the nanosilver in the case of raw plasma treated fabrics [34]. These fabrics exhibit the highest adsorption of silver. The increase adsorption of nanosilver in the case of raw plasma treated fabrics can be attributed by the increase in the surface area and a change in the surface composition and chemical bonding resulting from the corona air plasma treatment. The raw fabrics become more porous and seem to be conducive for silver absorption. Thus the raw plasma treated fabrics exhibit the highest adsorption of silver in comparison to washed and washed-thermostabilized fabrics and therefore give the best microbial reduction. The bacterial cultures examined are Staphylococcus aureus, Escherichia coli, Streptococcus faecalis, Pseudomonas aeruginosa. Of these, Staphylococcus aureus and Streptococcus faecalis show a significant reduction of more than 60% of the treated PET fabrics. The long-term changes of fabric surfaces obtained by plasma treatment can hold good promise for industrial applications.

In another work [33, 36], two types of bacteria, namely, Staphylococcus aureus, Escherichia coli, have been used to assess the antibacterial activity of PET fabrics finished with nanometer titanium dioxide/nanometer silver/water borne polyurethane composite emulsion. The antibacterial activity of the standard as well as the treated fabrics (mixture of nano-TiO2 and nano-Ag) is shown in Figures 2(a) and 2(c), against S. aureus. Figures 2(b) and 2(d) exhibit the antibacterial activity in the case of E. coli. In both cases the test fabrics have been irradiated with UV light for 6 hours prior to evaluation. Figures 2(c) and 2(d) clearly indicate that the fabrics treated with the mixture of nano-TiO2 and nano-Ag particle exhibit a higher level of antibacterial activity, but the standard samples shown in Figures 2(a) and 2(b) exhibited little or no antibacterial activity. The comparative figures reveal that the circle in the middle area is the fabric sample and the curvimaterials are the bacteria on the standard bacterial liquid. The curvimaterial in Figures 2(a) and 2(c) on the circular area is continuous and clear. This phenomenon indicates that the antibacterial activity of the standard fabric is almost ineffective. The curvimaterial in Figures 2(b) and 2(d) is disappearing. This shows that in the case of the treated fabric, the antibacterial agent has destroyed the bacteria and thus rendered the fabric significantly effective. It could also be visualized that the UV light irradiation before antibacterial testing could photo-sensitize the nano-TiO2/nano-Ag to destroy the bacteria.

fig2
Figure 2: Antibacterial activity for ((a) and (c)) S. aureus and ((b) and (d)) E. coli. (a) and (c): control samples; (b) and (d): fabric samples finished with mixed nano-TiO2/nano-Ag (2.0 wt%/125 ppm) [33].

4. Conclusion

Nano finishes have been applied onto fabrics for the attainment of desirable functional properties. Of these, the antimicrobial property has been one of the most prominent and promising. Recent research findings in the area of antimicrobial finishes have been reviewed in this paper. Important nanomaterials used include titanium dioxide, zinc oxide, silver oxide, and silver nanocolloids. Each type of nanomaterial applied on fabrics has been analyzed for specific bacterium cultures. In the case of nanotitanium dioxide, the bacterial cultures examined were Staphylococcus aureus and Klebseilla pnrumoniae. Nanotitanium dioxide has been applied on 100% cotton and 45/55 cotton/polyester blend fabric. In the case of blend fabric, the polyester component exhibited better microbial reduction than its cotton counterpart. Zinc oxide nanoparticles have been applied on cotton fabrics. Antimicrobial evaluation by different methods has proved that a higher antimicrobial activity has been observed in the case of bacterium S. aureus than E. coli. Silver nanoparticles have been applied on wool and silk fabrics. The bacterium observed were S. aureus, E. coli and P. aeruginosa. The antimicrobial efficacy has been observed even after 20 washes in the treated fabrics. Nano silver colloids have been applied onto cotton, silk, and wool fabrics. The sterilizing effect produced by the silver ions and compounds contributed to the antimicrobial efficacy. Besides being applied on natural materials such as cotton, wool, and silk fabrics, nano finishes have also been applied onto PET fabrics. In one case fabrics have been treated with air plasma. Raw plasma treated fabrics have shown the best adsorption of silver as compared to washed and washed-thermostabilized fabrics and hence give the best antimicrobial efficacy. In another case PET fabrics have been treated with nanometer titanium dioxide/nanometer silver/water borne polyurethane composite emulsion and have shown a good antimicrobial efficacy. The foregoing discussions clearly point out that various types of nanomaterials applied to fabrics produce good antimicrobial effects, which are considered even better than antibiotic effects. The researches on the antimicrobial treatment of textiles clearly hold promise in medical applications in the near future. However, the impact of the different nanomaterials on the human health and environment needs to be well researched and established before they gain a commercial acceptance.

References

  1. Y. Gao and R. Cranston, “Recent advances in antimicrobial treatments of textiles,” Textile Research Journal, vol. 78, no. 1, pp. 60–72, 2008. View at Publisher · View at Google Scholar · View at Scopus
  2. H. J. Lee and S. H. Jeong, “Bacteriostasis and skin innoxiousness of nanosize silver colloids on textile fabrics,” Textile Research Journal, vol. 75, pp. 551–556, 2005. View at Publisher · View at Google Scholar
  3. H. Y. Ki, J. H. Kim, S. C. Kwon, and S. H. Jeong, “A study on multifunctional wool textiles treated with nano-sized silver,” Journal of Materials Science, vol. 42, pp. 8020–8024, 2000. View at Publisher · View at Google Scholar
  4. M. L. Gulrajani, D. Gupta, S. Periyasamy, and S. G. Muthu, “Preparation and application of silver nanoparticles on silk for imparting antimicrobial properties,” Journal of Applied Polymer Science, vol. 108, no. 1, pp. 614–623, 2008. View at Publisher · View at Google Scholar · View at Scopus
  5. N. Vigneshwaran, A. A. Kathe, P. V. Varadarajan, R. P. Nachane, and R. H. Balasubramanya, “Functional finishing of cotton fabrics using silver nanoparticles,” Journal of Nanoscience and Nanotechnology, vol. 7, no. 6, pp. 1893–1897, 2007. View at Publisher · View at Google Scholar · View at Scopus
  6. E. Falletta, M. Bonini, E. Fratini et al., “Clusters of poly(acrylates) and silver nanoparticles: Structure and applications for antimicrobial fabrics,” Journal of Physical Chemistry C, vol. 112, no. 31, pp. 11758–11766, 2008. View at Publisher · View at Google Scholar · View at Scopus
  7. M. K. Yeo and M. Kang, “Effects of nanometer sized silver materials on biological toxicity during zebrafish embryogenesis,” Bulletin of the Korean Chemical Society, vol. 29, pp. 1179–1184, 2008. View at Publisher · View at Google Scholar
  8. P. Nagendar Reddy, E. M. Pena-Mendez, and J. Havel, “Silver or silver nanoparticles: a hazardous threat to the environment and human health?” Journal of Applied Biomedicine, vol. 6, pp. 117–119, 2008.
  9. L. Fu, Z. Liu, Y. Liu et al., “Beaded cobalt oxide nanoparticles along carbon nanotubes: Towards more highly integrated electronic devices,” Advanced Materials, vol. 17, no. 2, pp. 217–221, 2005. View at Publisher · View at Google Scholar · View at Scopus
  10. S. Makhluf, R. Dror, Y. Nitzan, Y. Abramovich, R. Jelinek, and A. Gedanken, “Microwave-assisted synthesis of nanocrystalline MgO and its use as a bacteriocide,” Advanced Functional Materials, vol. 15, no. 10, pp. 1708–1715, 2005. View at Publisher · View at Google Scholar · View at Scopus
  11. P. K. Stoimenov, R. L. Klinger, G. L. Marchin, and K. J. Klabunde, “Metal oxide nanoparticles as bactericidal agents,” Langmuir, vol. 18, no. 17, pp. 6679–6686, 2002. View at Publisher · View at Google Scholar · View at Scopus
  12. R. M. Dickson and L. A. Lyon, “Unidirectional plasmon propagation in metallic nanowires,” Journal of Physical Chemistry B, vol. 104, no. 26, pp. 6095–6098, 2000. View at Scopus
  13. A. Yadav, V. Prasad, A. A. Kathe et al., “Functional finishing in cotton fabrics using zinc oxide nanoparticles,” Bulletin of Materials Science, vol. 29, no. 6, pp. 641–645, 2006. View at Publisher · View at Google Scholar · View at Scopus
  14. V. Parthasarathi and G. Thilagavathi, “Synthesis and characterization of titanium dioxide nano-particles and their applications to textiles for microbe resistance,” Journal of Textile and Apparel, Technology and Management, vol. 6, no. 2, 2009. View at Scopus
  15. D. P. Chattopadhyay and B. H. Patel, “Improvement in physical and dyeing properties of natural fibres through pre-treatment with silver nanoparticles,” Indian Journal of Fibre and Textile Research, vol. 34, no. 4, pp. 368–373, 2009. View at Scopus
  16. L. Haixia, D. Hua, and Z. Jing, “Performance research of polyester fabric treated by nano titanium dioxide (N ano-TiO2) anti-ultraviolet finishing,” International Journal of Chemistry, vol. 1, p. 57, 2009.
  17. S. Kathirvelu, L. D'Souza, and B. Dhurai, “UV protection finishing of textiles using ZnO nanoparticles,” Indian Journal of Fibre and Textile Research, vol. 34, no. 3, pp. 267–273, 2009. View at Scopus
  18. M. Moroni, D. Borrini, L. Calamai, and L. Dei, “Ceramic nanomaterials from aqueous and 1,2-ethanediol supersaturated solutions at high temperature,” Journal of Colloid and Interface Science, vol. 286, no. 2, pp. 543–550, 2005. View at Publisher · View at Google Scholar · View at Scopus
  19. Y. J. Kwon, K. H. Kim, C. S. Lim, and K. B. Shim, “Characterization of ZnO nanopowders synthesized by the polymerized complex method via an organochemical route,” Journal of Ceramic Processing Research, vol. 3, no. 3, pp. 146–149, 2002. View at Scopus
  20. R. Rajendran, C. Balakumar, M. A. Hasabo, S. Jayakumar, K. Vaideki, and E. M. Rajesh, “Use of zinc oxide nano particles for production of antimicrobial textiles,” International Journal of Engineering, Science and Technology, vol. 2, no. 1, pp. 202–208, 2010.
  21. L. Zhang, Y. Jiang, Y. Ding et al., Journal of Nanoparticle Research, vol. 10, pp. 9711–9711, 2009.
  22. O. Yamamoto, J. Sawai, and T. Sasamoto, “Change in antibacterial characteristics with doping amount of ZnO in MgO-ZnO solid solution,” International Journal of Inorganic Materials, vol. 2, no. 5, pp. 451–454, 2000. View at Publisher · View at Google Scholar · View at Scopus
  23. N. Padmavathy and R. Vijayaraghavan, “Enhanced bioactivity of ZnO nanoparticles—an antimicrobial study,” Science and Technology of Advanced Materials, vol. 9, no. 3, Article ID 035004, 2008. View at Publisher · View at Google Scholar · View at Scopus
  24. T. Q. Liu, O. Sakurai, N. Mizutani, and M. Kato, “Preparation of spherical fine ZnO particles by the spray pyrolysis method using ultrasonic atomization techniques,” Journal of Materials Science, vol. 21, no. 10, pp. 3698–3702, 1986. View at Publisher · View at Google Scholar · View at Scopus
  25. T. Trindade, J. D. Pedrosa De Jesus, and P. O'Brien, “Preparation of zinc oxide and zinc sulfide powders by controlled precipitation from aqueous solution,” Journal of Materials Chemistry, vol. 4, no. 10, pp. 1611–1617, 1994. View at Scopus
  26. M. A. Vergés and M. M. Gallego, “Spherical and rod-like zinc oxide microcrystals: morphological characterization and microstructural evolution with temperature,” Journal of Materials Science, vol. 27, no. 14, pp. 3756–3762, 1992. View at Publisher · View at Google Scholar · View at Scopus
  27. D. Chen, X. Jiao, and G. Cheng, “Hydrothermal synthesis of zinc oxide powders with different morphologies,” Solid State Communications, vol. 113, no. 6, pp. 363–366, 2000. View at Scopus
  28. S. Mahamuni, K. Borgohain, B. S. Bendre, V. J. Leppert, and S. H. Risbud, “Spectroscopic and structural characterization of electrochemically grown ZnO quantum dots,” Journal of Applied Physics, vol. 85, no. 5, pp. 2861–2865, 1999. View at Scopus
  29. A. S. M. Raja, G. Thilagavathi, and T. Kannaian, “Synthesis of spray dried polyvinyl pyrrolidone coated silver nanopowder and its application on wool and cotton for microbial resistance,” Indian Journal of Fibre and Textile Research, vol. 35, no. 1, pp. 59–64, 2010. View at Scopus
  30. G. Thilagavathi, K. Rajendrakumar, and R. Rajendran, “Development of ecofriendly antimicrobial textile finishes using herbs,” Indian Journal of Fibre and Textile Research, vol. 30, no. 4, pp. 431–436, 2005. View at Scopus
  31. S. Ghosh, S. Yadav, and N. Reynolds, “Antibacterial properties of cotton fabric treated with silver nanoparticles,” Journal of the Textile Institute, vol. 101, no. 10, pp. 917–924, 2010. View at Publisher · View at Google Scholar · View at Scopus
  32. M. Saito, “Antibacterial, deodorizing, and UV absorbing materials obtained with zinc oxide (ZnO) coated fabrics,” Journal of Coated Fabrics, vol. 23, pp. 150–164, 1993. View at Scopus
  33. N. Gokarneshan, P. P. Gopalakrishnan, and B. Jeyanthi, “Influence of various nano finishes on the functional properties of textile materials,” International Journal of Basic and Applied Chemical Sciences, vol. 2, no. 2, pp. 8–24, 2012.
  34. M. Gorensek, M. Gorjanc, V. Bukosek, K. Janez, P. Jovancic, and M. Darka, “Functionalization of PET fabrics by corona and nano silver,” Textile Research Journal, vol. 80, no. 3, pp. 253–262, 2010. View at Publisher · View at Google Scholar
  35. ASTM Designation: E 2149-01 method, “Standard test method for determining the antimicrobial activity of immobilized antimicrobial agents under dynamic contact conditions”.
  36. C. C. Chen, C. C. Wang, and J. T. Yeh, “Improvement of odor elimination and anti-bacterial activity of polyester fabrics finished with composite emulsions of nanometer titanium dioxide-silver particles-water-borne polyurethane,” Textile Research Journal, vol. 80, no. 4, pp. 291–300, 2010. View at Publisher · View at Google Scholar · View at Scopus