- About this Journal ·
- Abstracting and Indexing ·
- Aims and Scope ·
- Article Processing Charges ·
- Articles in Press ·
- Author Guidelines ·
- Bibliographic Information ·
- Citations to this Journal ·
- Contact Information ·
- Editorial Board ·
- Editorial Workflow ·
- Free eTOC Alerts ·
- Publication Ethics ·
- Submit a Manuscript ·
- Subscription Information ·
- Table of Contents
Volume 2012 (2012), Article ID 705803, 4 pages
Enhancement of Resistance Switching in Electrodeposited Co-ZnO Films
School of Materials Science and Engineering, University of New South Wales, Sydney, NSW 2052, Australia
Received 12 April 2012; Accepted 27 June 2012
Academic Editors: K. S. Coleman and C.-L. Hsu
Copyright © 2012 Dewei Chu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
High quality Co-doped ZnO films were prepared with electrodeposition. The correlation among the surface morphology, lattice structure, Co-dopant distribution, and resistance switching properties of the as-deposited films were investigated. It is found that resistance switching behaviour could be manipulated by controlling the composition of Co in the ZnO films. The significant enhancement of resistance switching was achieved with 5 at% Co doping in the films, and the possible switching mechanism was also discussed.
Resistive switching random access memory (RRAM) has attracted enormous interests, due to its simple structure and compatibility with complementary metal oxide semiconductor technology [1–5]. In comparable with the traditional nonvolatile memories (flash), RRAM exhibits unique advantages including much faster writing rate, smaller bit cell size, and lower operating voltages. In particular, the resistive transition induced by applying electric pulses can complete within tenths of nanoseconds at room temperature while the resultant resistance states could be retained for 10 years [2, 6, 7].
RRAM devices are usually structured with an insulating layer sandwiched by two electrodes, which generate reversible electrical field to induce the resistance switching. In this case, the performance of RRAM strongly depends on the resistively switching materials. Therefore, the primary requirement for RRAM is to develop a material that possesses resistive switching effect. To date, a number of materials have been found to have resistive switching behavior, for example, ferromagnetic oxide (Pr1−xCaxMnO3), doped perovskite oxide (SrZrO3), and binary transition metal oxide (TiO2, NiO, ZnO, and Cu2O) [1, 2, 4, 6, 8–11]. Among these materials, only the transition metal oxides are transparent to the visible light due to their large optical band gap. More importantly, their compositions are easier to be controlled compared to the ferromagnetic or perovskite oxides. Hence, such materials have a great potential for the applications of transparent RRAM devices [12, 13].
In this work, high quality Co-doped ZnO films were prepared with electrodeposition at low temperature, and their resistive switching behaviors were characterized. The morphology and size of metal oxide crystals were optimized by manipulating the potential, current, and concentration of the reactant. Co was strategically doped into ZnO to enlarge the memory window via increasing the resistivity of the high resistance state.
Electrodeposition was carried out in an Autolab 302N electrochemical workstation. A standard three-electrode setup in an undivided cell was applied. ITO (9.3~9.7 Ω, Asashi Glass Corporation, Japan, 1.1 mm 26 mm 30 mm) was used as the working electrode while platinum foil (0.2 mm 10 mm 20 mm) was employed as the counter electrode. The two electrodes were separated with a distance of 30 mm. Ag/AgCl electrode was used as a reference electrode in 4 M KCl solution.
The ITO substrates were first cleaned with ethanol and acetone sonication/ultra violet ozone, and the electrodeposition was implemented in a solution of 0.1 M Zn(NO3)2·6H2O with Co in different composition at 1 mA for 30 min, at 75°C. The crystal structure of the as-deposited materials was determined by X-ray powder diffraction (Philips X’pert Multipurpose X-ray Diffraction System (MPD) with Cu Kα). The morphologies of the as-deposited materials were characterized using scanning electron microscopy (SEM, Hitachi S3400). To measure the electrical property of the materials, Au top electrodes were patterned and deposited by DC magneton sputter with a metal shadow mask. Voltage-current curves of the films were measured using an Autolab 302N electrochemical workstation controlled with Nova software. During the measurement, the working electrode and sensor electrode were connected to the top Au electrodes while the reference and counter electrode were connected to the ITO substrate. A schematic of the setup for I-V measurement is shown in Figure 1.
3. Results and Discussion
The electrochemical synthesis of ZnO is a four-step process: first, nitrate ions and H2O are electrochemically reduced at the surface of the working electrode, resulting in an increase of local pH value in the vicinity of the electrode as shown in (1) and (2). Subsequently, the increase of the local pH leads to the precipitation of zinc ions as zinc hydroxide [Zn(OH)2, (3)] at 75°C and Zn(OH)2 can be transformed into ZnO eventually. In the presence of Co2+, part of the Co2+ ions would be incorporated into ZnO lattices accordingly as follows:
Figure 2 shows the XRD spectra of pure and 5 at % Co-doped ZnO films on ITO substrates. No impurity is detected in these spectra. The predominant peak in the spectra demonstrates that the films grew with the preferential orientation of . It is discernible that the characteristic peaks of Co doped ZnO shift to the higher diffraction angles, showing the occurrence of shrinkage induced by Co-doping, which are associated with the different the different ionic radii between Co2+ (0.058 nm) and Zn2+ (0.060 nm). This finding is in a good agreement with the reported observation in Co-doped ZnO thin films .
The SEM surface morphologies of 5 at% Co-doped ZnO films in Figure 3 show that the films are composed of nanorods those grow densely and vertically on the substrate. These nanorods are well crystalline with an average diameter of ~250 nm. In addition, Energy Dispersive Spectrometry (EDS) elemental mapping was employed to verify whether the Co has been incorporated into the as-deposited ZnO films homogenously and the results shown in Figures 3(b), 3(c), and 3(d) evidence that the O, Zn, and Co elemental maps have the identical spatial distribution. This indicates that the doped Co has incorporated in ZnO films homogenously.
Figure 4(a) presents a typical I-V character of RRAM cell with the as-prepared structure of Au/5 at % Co-ZnO/ITO/Au capacitor, which was measured by sweeping voltage, at a speed of 0.01 V/s, in the sequence of V. During the measurements, the bias voltages were applied on the TE with BE grounded, and neither a forming process nor a current compliance was necessary for activating the memory effort. For the Co-doped ZnO, with the increase of the positive bias, a sudden jump in resistance occurs at 2.6 V, indicating the switching to a low-resistance state (LRS). The sample remains in the LRS with increasing bias while a drop of current is observed at 4 V and the backward transition to a high resistance state (HRS) for subsequent bias descending. Sweeping the voltage to negative region exhibits a symmetrical behaviour, as expected from the symmetric stack structure. For comparison, I-V behaviours of the pure ZnO and 2 at% Co-doped ZnO are also measured. Figure 3(b) shows that the pure ZnO has a much smaller memory window compared with 2 at% and 5 at% Co-doped ZnO, demonstrating that the Co-doped ZnO is an excellent candidate for RRAM applications. Moreover, the reliability of the memory effects is evaluated by performing a switching cycling test. As shown in Figure 3(c), the bistable resistance switching behaviour is reversible and steady after 10 cycles. To evaluate the resistive switching characteristics of 5 at% Co-doped ZnO film, the evolution of HRS and LRS over 4000 cycles was measured, which is shown in Figure 3(b). From the distributions of HRS and LRS in Figure 3(d), the two well-resolved states provide a clear memory window of the device.
The mechanisms for resistance switching in metal oxides are interesting but still controversial. The filamentary mechanism has been reported to explain the resistance switching behaviour in the pure and doped ZnO films . According to filament theory, defects might condense in the metal oxide to form tiny conducting filament at HRS, and these tiny conducting filaments could gather and align to form a long conducting filament, thus leading to transition to LRS . In this work, the conducting filaments in ZnO may be created and enhanced by the alignment of the structural defects due to Co doping.
High oriented pure and Co-doped ZnO thin films were prepared by a facile electrochemical deposition method. EDS mapping indicates that ZnO films are homogenously doped with Co. Reliable and reproducible bipolar resistance memory switching performance is achieved in 5 at % Co-doped ZnO films. The present work demonstrates that Co-ZnO films have the potential for next generation non volatile memory applications.
This research was sponsored by Australian Research Council (ARC) Discovery Project (DP 110102391).
- S. Q. Liu, N. J. Wu, and A. Ignatiev, “Electric-pulse-induced reversible resistance change effect in magnetoresistive films,” Applied Physics Letters, vol. 76, no. 19, pp. 2749–2751, 2000.
- J. J. Yang, M. D. Pickett, X. Li, D. A. A. Ohlberg, D. R. Stewart, and R. S. Williams, “Memristive switching mechanism for metal/oxide/metal nanodevices,” Nature Nanotechnology, vol. 3, no. 7, pp. 429–433, 2008.
- S. X. Wu, X. Y. Li, X. J. Xing, P. Hu, Y. P. Yu, and S. W. Li, “Resistive dependence of magnetic properties in nonvolatile Ti/Mn: TiO2/SrTi0.993Nb0.007O3/Ti memory device,” Applied Physics Letters, vol. 94, no. 25, Article ID 253504, 3 pages, 2009.
- A. Beck, J. G. Bednorz, C. Gerber, C. Rossel, and D. Widmer, “Reproducible switching effect in thin oxide films for memory applications,” Applied Physics Letters, vol. 77, no. 1, pp. 139–141, 2000.
- L. Chua, “Memristor. The missing circuit element,” IEEE Transactions on Circuit Theory, vol. 18, no. 5, pp. 507–519, 1971.
- J. W. Seo, J.-W. Park, K. S. Lim, et al., “Transparent resistive random access memory and its characteristics for nonvolatile resistive switching,” Applied Physics Letters, vol. 93, no. 22, Article ID 223505, 3 pages, 2008.
- D. B. Strukov, G. S. Snider, D. R. Stewart, and R. S. Williams, “The missing memristor found,” Nature, vol. 453, no. 7191, pp. 80–83, 2008.
- S. Seo, M. J. Lee, D. H. Seo et al., “Reproducible resistance switching in polycrystalline NiO films,” Applied Physics Letters, vol. 85, no. 23, pp. 5655–5657, 2004.
- B. J. Choi, D. S. Jeong, S. K. Kim et al., “Resistive switching mechanism of TiO2 thin films grown by atomic-layer deposition,” Journal of Applied Physics, vol. 98, no. 3, Article ID 033715, 10 pages, 2005.
- A. Chen, S. Haddad, Y. C. Wu, T. N. Fang, S. Kaza, and Z. Lan, “Erasing characteristics of Cu2O metal-insulator-metal resistive switching memory,” Applied Physics Letters, vol. 92, no. 1, Article ID 013503, 2008.
- M. Villafuerte, S. P. Heluani, G. Juárez, G. Simonelli, G. Braunstein, and S. Duhalde, “Electric-pulse-induced reversible resistance in doped zinc oxide thin films,” Applied Physics Letters, vol. 90, no. 5, Article ID 052105, 2007.
- J. J. Yang, F. Miao, M. D. Pickett, et al., “The mechanism of electroforming of metal oxide memristive switches,” Nanotechnology, vol. 20, no. 21, Article ID 215201, 2009.
- L. Shi, D. Shang, J. Sun, and B. Shen, “Bipolar resistance switching in fully transparent ZnO:Mg-based devices,” Applied Physics Express, vol. 2, no. 10, Article ID 101602, 2009.
- P. Li, S. Wang, J. Li, and W. Yu, “Structural and optical properties of Co-doped ZnO nanocrystallites prepared by a one-step solution route,” Journal of Luminescence, vol. 132, no. 1, pp. 220–225, 2012.
- W. Chang, “Resistive switching behaviors of ZnO nanorod layers,” Applied Physics Letters, vol. 96, no. 24, Article ID 242109, 3 pages, 2010.