Potentiodynamic Polarization Behaviour of Electroless Ni-P-W Coatings
Table 4
Experimental results of potentiodynamic polarization test.
| Sl. no. | Ecorr (mV versus SCE) | Icorr (A/cm2) |
| 1 | −451.41 | 6.107 | 2 | −327.02 | 0.050 | 3 | −358.33 | 0.042 | 4 | −468.92 | 1.967 | 5 | −257.34 | 0.065 | 6 | −343.07 | 0.083 | 7 | −334.05 | 0.039 | 8 | −330.62 | 0.071 | 9 | −364.45 | 0.197 | 10 | −477.13 | 4.502 | 11 | −463.15 | 0.295 | 12 | −336.3 | 0.256 | 13 | −434.62 | 0.173 | 14 | −355.74 | 0.648 | 15 | −273.61 | 0.038 | 16 | −408.09 | 2.479 | 17 | −308.4 | 0.128 | 18 | −307.84 | 0.065 | 19 | −278.71 | 0.080 | 20 | −388.78 | 0.485 | 21 | −299.43 | 1.591 | 22 | −366.32 | 0.687 | 23 | −492.59 | 1.426 | 24 | −304.76 | 0.062 | 25 | −344.22 | 0.751 | 26 | −360.3 | 0.055 | 27 | −362.39 | 0.407 |
|
|