Processing and Characterization of Yttria-Stabilized Zirconia Foams for High-Temperature Applications
Table 2
Values of Young modulus for single/double YSZ samples after thermal shock test.
| | (Hz) | E (GPa) |
| 8YSZ | A1 | | | W/out cycles | 597 | 0.10 | 4 cycles | 330 | 0.03 | 8 cycles | 259 | 0.02 |
| 3YSZ double coated | A1 | | | W/out cycles | 2373 | 5.07 | 4 cycles | 1673 | 2.52 | 8 cycles | 1430 | 1.84 | 12 cycles | 1296 | 1.51 | A2 | | | W/out cycles | 1721 | 2.25 | 4 cycles | 1390 | 1.47 | 8 cycles | 1202 | 1.1 | 12 cycles | 1139 | 0.98 |
| 3YSZ single coated | A1 | | | W/out cycles | 1257 | 0.42 | 4 cycles | 1108 | 0.33 | 8 cycles | 1084 | 0.32 | 12 cycles | 1060 | 0.30 | A2 | | | W/out cycles | 1021 | 0.23 | 4 cycles | 958 | 0.20 | 8 cycles | 919 | 0.18 | 12 cycles | 911 | 0.18 |
|
|