Preparation, Structural, Electrical, and Ferroelectric Properties of Lead Niobate–Lead Zirconate–Lead Titanate Ternary System

Table 4

Variation of remnant polarization () and coercivity () for PNZT ternary system.

Composition	Remnant polarization; () (µC/cm^2)	Coercivity (); (kV/cm)
0.5PN–0.15PZ–0.35PT	0.24	19.15
0.5PN–0.25PZ–0.25PT	0.10	6.33
0.5PN–0.35PZ–0.15PT	0.20	13.61