Lead-Silver Anode Degradation during Zinc Electrorecovery Process: Chloride Effect and Localized Damage
Figure 3
The rate of anode degradation at different time intervals during the electrowinning process, obtained at current density 500 A/m2 via mass-loss measurements (°C).