Modyfication of the Rigid Polyurethane-Polyisocyanurate Foams
Table 5
Receipts of foams containing recyclates of standard foam (foams 1–4) and polyethylene glycol 1500 (foams 5–36).
| No. of foam as in Table 1 | No. of foam obtained from recyclates
| Rokpol RF-55 (g) | Products of foam decomposition (g)
| | 0 | 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 0.0 | 56.7 | 0.0 | | | | | | | | |
| 0 | 1 | 51.0 | 6.7 | | | | | | | | | 2 | 45.3 | 13.4 | | | | | | | | | 3 | 39.6 | 20.0 | | | | | | | | | 4 | 34.0 | 26.7 | | | | | | | | |
| 1 | 5 | 51.0 | | 6.5 | | | | | | | | 6 | 45.3 | | 13.0 | | | | | | | | 7 | 39.6 | | 19.4 | | | | | | | | 8 | 34.0 | | 25.9 | | | | | | | |
| 2 | 9 | 51.0 | | | 6.4 | | | | | | | 10 | 45.3 | | | 12.8 | | | | | | | 11 | 39.6 | | | 19.3 | | | | | | | 12 | 34.0 | | | 25.7 | | | | | | |
| 3 | 13 | 51.0 | | | | 6.3 | | | | | | 14 | 45.3 | | | | 12.6 | | | | | | 15 | 39.6 | | | | 19.0 | | | | | | 16 | 34.0 | | | | 25.3 | | | | | |
| 4 | 17 | 51.0 | | | | | 6.2 | | | | | 18 | 45.3 | | | | | 12.5 | | | | | 19 | 39.6 | | | | | 18.7 | | | | | 20 | 34.0 | | | | | 25.0 | | | | |
| 5 | 21 | 51.0 | | | | | | 6.1 | | | | 22 | 45.3 | | | | | | 12.3 | | | | 23 | 39.6 | | | | | | 18.4 | | | | 24 | 34.0 | | | | | | 25.5 | | | |
| 6 | 25 | 51.0 | | | | | | | 6.1 | | | 26 | 45.3 | | | | | | | 12.2 | | | 27 | 39.6 | | | | | | | 18.2 | | | 28 | 34.0 | | | | | | | 24.3 | | |
| 7 | 29 | 51.0 | | | | | | | | 5.9 | | 30 | 45.3 | | | | | | | | 11.8 | | 31 | 39.6 | | | | | | | | 17.6 | | 32 | 34.0 | | | | | | | | 23.5 | |
| 8 | 33 | 51.0 | | | | | | | | | 5.8 | 34 | 45.3 | | | | | | | | | 11.7 | 35 | 39.6 | | | | | | | | | 17.5 | 36 | 34.0 | | | | | | | | | 23.3 |
|
|