Development of Epoxy Based Surface Tolerant Coating Improvised with Zn Dust and MIO on Steel Surfaces
Table 2
In can properties of the various coatings.
| Systems | High constitute of ingredients | Polymer base | Cross-linker | Hard dry | Main FT-IR peaks | Surface tension (newton/meter) |
| Benchmark 1 | Ti, Mg, Si, and Al | Epoxy resin | Triethylenetetramine with catalyst | 14–16 hours |
Strong band included Ti–O(Stret), - 800–1110 cm−1 | 30.42 | Benchmark 2 | Si and little amount of Ti and Mg | Epoxy resin | Triethylenetetramine with catalyst | 14–16 hours | 31.75 | Benchmark 3 | Si and little amount of Ti | Epoxy resin | Triethylenetetramine with catalyst | 12–14 hours | 33.61 | STC1 | Zn, Ti, Si | Bisphenol A based epoxy resin with Zn dust | Fomulated polyamidoamine adduct | 8–10 hours | Zn–O at 454 cm −1 | 29.92 | STC2 | Fe, Ti, Si | Bisphenol A based epoxy resin with MIO flakes | Fomulated polyamidoamine adduct | 8–10 hours | Fe–O at 560 cm −1 | 29.20 |
|
|