Development of Epoxy Based Surface Tolerant Coating Improvised with Zn Dust and MIO on Steel Surfaces
Table 5
Comparative mechanical test results of different kinds of surface tolerant coatings.
| | Benchmark 1 | Benchmark 2 | Benchmark 3 | STC1 | STC2 |
| Pull off adhesion (Mpa) | 5 Mpa | 5.4 Mpa | 4.9 Mpa | 5.4 Mpa | 5.2 Mpa | Adhesion failure | Cohesive failure | Adhesion failure | Cohesive failure | Cohesive failure | Impact energy, load: 4.730 kg, max height: 23′′ | 23.18 J | 26.88 J | 18.54 J | 26.88 J | 26.88 J | Scratch resistance | 10 Kg: passed | 10 Kg: passed | 10 Kg: passed | 10 Kg: passed | 10 Kg: passed | Flexibility | 140°: passed | 140°: passed | 140°: passed | 140
°
: passed | 140
°
: passed | Tensile strength | 8.46 Mpa | 5.76 MPA | 5.07 MPa | 10.37 MPa | 10.58 MPa | Taber abrasion results by weight loss (gm) | 0.1277 | 0.0945 | 0.2080 | 0.0981 | 0.1073 | Contact angle | 55.34 | 52.34 | 62.24 | 74.74 | 67.20 |
|
|