Journal of Composites / 2014 / Article / Tab 1 / Research Article
Multifunctional Thermally Remendable Nanocomposites Table 1 Measurements of the electrical, thermal, and mechanical properties of nanoadditive containing composite panels relative to the control. Thermal conductivity values are given for the two temperature extremes over the range for which they were measured.
Panel Nanoadditive Resistivity (
/square) Thermal conductivity (W/m·K) Storage modulus (GPa) Loss modulus (GPa) 30°C 110°C 30°C 30°C (1) Control-carbon fiber only*
0.476 0.482 42.1 6.95 (2) 1 ply s-MWCNT + 5 plies with spray-coated MWCNTs (lot 1)
0.544 0.566 61.5 10.5 (3) Spray-coated MWCNTs (lot 1) 15637 0.583 0.621 61.6 9.41 (4) Spray-coated MWCNTs (lot 1)**
0.609 0.579 64.9 9.94 (5) Spray-coated MWCNTs (lot 2) 13597 0.544 0.551 53.0 11.2 (6) Spray-coated purified laser SWCNTs*** 1673498 0.549 0.578 67.0 9.03 (7) Unidirectional (0° orientation) spun MWCNTs on front side only# 770 0.687 0.747 62.3 8.42 (8) Unidirectional (0° orientation) spun MWCNTs on front side only##
0.542 0.525 49.0 10.0 (9) Bidirectional spun MWCNTs with purified HiPco SWCNTs dispersed in resin### 7342 0.509 0.447 48.4 5.02 (10) Bidirectional spun MWCNTs with purified laser SWCNTs dispersed in resin 475902 0.540 0.482 21.7 2.41
Black, **Brown, ***Orange, # Blue, ## Purple, and ### Green.