Thermomechanical Impact of Polyurethane Potting on Gun Launched Electronics
Table 6
Results, fully potted model at cold, sticky potting, maximum stresses.
| Chips | Svm | Time | S1 | Time | Delta disp | Time | MPa | Sec | MPa | Sec | mm | Sec |
| Top-Chip-1 | 26.3 | 0.0117 | 17.8 | 0.0113 | 0.002 | 0.0038 | Top-Chip-2 | 33.8 | 0.0117 | 21.0 | 0.0113 | 0.002 | 0.0118 | Top-Chip-3 | 25.0 | 0.0113 | 17.2 | 0.0118 | 0.003 | 0.0113 | Top-Chip-4 | 16.9 | 0.0113 | 9.6 | 0.0115 | 0.002 | 0.0115 | Bottom-Chip-1 | 61.8 | 0.0113 | 39.6 | 0.0115 | 0.002 | 0.0118 | Bottom-Chip-2 | 61.7 | 0.0113 | 33.9 | 0.0115 | 0.002 | 0.0113 | Bottom-Chip-3 | 77.6 | 0.0113 | 48.3 | 0.0118 | 0.002 | 0.0038 | Bottom-Chip-4 | 60.3 | 0.0113 | 39.4 | 0.0112 | 0.002 | 0.0136 |
|
|