Thermomechanical Impact of Polyurethane Potting on Gun Launched Electronics
Table 8
Results, fully potted model at hot, sticky potting, maximum stresses.
| Part
| Svm | Time | S1 | Time | Delta disp | Time | MPa | Sec |
MPa | Sec | mm | Sec |
| Top-Chip-1 | 16.4 | 0.0142 | 8.4 | 0.0124 | 0.024 | 0.0116 | Top-Chip-2 | 24.3 | 0.0121 | 15.9 | 0.0122 | 0.021 | 0.0119 | Top-Chip-3 | 38.0 | 0.012 | 23.7 | 0.012 | 0.019 | 0.0117 | Top-Chip-4 | 22.1 | 0.0034 | 12.1 | 0.0112 | 0.015 | 0.0127 | Bottom-Chip-1 | 107.5 | 0.0119 | 41.5 | 0.0124 | 0.022 | 0.0119 | Bottom-Chip-2 | 82.6 | 0.0116 | 40.9 | 0.0127 | 0.020 | 0.0117 | Bottom-Chip-3 | 80.6 | 0.0119 | 55.4 | 0.0121 | 0.017 | 0.0127 | Bottom-Chip-4 | 77.7 | 0.0128 | 34.5 | 0.0128 | 0.021 | 0.0116 |
|
|